This research had two objectives that were to study parameters for forming bulletproof ceramic armor plates and to create a model of a bulletproof ceramic armor plate for small armored regular trucks. The parameters used to form a ceramic armor plate contain the thickness of the armor plate and the compressive strength which affects the density distribution of the green compact. A ballistic ceramic armor plate with a hexagonal shaped material was created as a concave bulletproof plate. Extrusion results displayed that the hexagonal material was formed at a very high density on the side surface of the armor plate but with uneven capacity distributed across the overall plate due to the friction occurring on the wall of the mold. The finite element method particularly at the Ansys/Explicit Dynamic tools were applied to analyse the damage of bulletproof plates. The model of a concave-shaped bulletproof plate was set for the SKD11material influencing the changes in the direction of the bullet firing when the bullet hit the bulletproof plate at a velocity of 880 m/s in accordance with the NIJ 4 standard. The bullet was made of tungsten carbide and the ceramic armor plate was built with a size of 300×300 mm and thicknesses of 14 16 18 and 20 mm. The bullet was fired into the center part and onto the curved surface of the ceramic plate. The result shows that the armor plate could not resistant to penetration. In this situation the direction of the bullets movement against the armor plate especially at a curved surface as a slope could result the deflection of the bullet direction as well as reduction of penetration capability.

Most of the current containers that we put food are made of plastic or foam boxes. After the use is finished the container becomes rubbish and will greatly affect the environment. Due to slow degradation Plus informal disposal And higher consumption The use of natural products is in great demand. Because it is beautiful and natural-looking pleasing to consumers Therefore the basic processes forming patterns were studied by rubber product molding techniques. Determine the material to be molded into the sample container. Design and build a small molding set. Provide binders used for the stabilization of natural materials. Experiment for forming and the Conclusion of the experiment From the results of operations and experiments it was found that the study of the prototype extrusion set Using a rubber molding technique Can be applied by various elements The process of rubber molding can be used in the development of natural container molding and the process can produce prototype containers from natural materials. Under the suitable size of the mold the area of the mold is smaller than the mold plate area of the machine or the size of the mold area the area of no more than 60-70% of the mold holder plate.

Currently the automotive industry plays an important role on the economic growth in Thailand. As the same time the waste of automotive parts has increased as well. As a results the automotive parts made from three different natural fiber parts was studied consisting of hyacinths sugarcane and pineapple leaf fiber. By of 50 x 250 x 20 mm of mold dimension the specimens were produced under 700 W of heating stick and measured temperature by a K type of thermometer. There were 3 same proportion specimens made from: 1) sugar cane fiber: husk: latex adhesive 2) water hyacinth fiber: husk: latex adhesive 3) pineapple fiber: husk: latex adhesive in the ratio of 25:25:50 by weight which were formed under temperature between 100GC and 105°C at 5 MPa of pressure and leading to find out the bending moment ability. The test results show that the specimen made from sugar cane fiber has the highest value 5482.5 Nand 4061.11 N/mm2 of bending moment and bending stress respectively. It was more than specimen made of water hyacinth 29.84 % and pineapple fiber 65.01 %.

Molds manufacturing to produce chloroprene rubber product with carbon steel over time the mold surface will wear. From the original. The practice in the industry often uses surface coatings (Hard chrome method) or change materials to create molds. Therefore this research is to study the effect of corrosion or wear. To see the size of surface mold changed in the experiment. Based on a tolerance of 0.1 millimeters at the molding point and after molding in the actual work conditions of a 2-3 weeks sample and mold size measurement. At less than 10 times the permissible coordinate value is 0.01 millimeters. The experiment found that. The wear of carbon steel molds was formed with chloroprene rubber. It has a very small value when referenced to the tolerance coordinates which is not significantly reduced when the rubber specimen size is determined. The allowance range is 10 μm to 100 μm. Therefore the design of chloroprene rubber to make molds with carbon steel. It can help reduce production costs. Without replacing with corrosion-resistant materials or adding coatings.

The aims of this research work were to enhance the impact resistance and processibilty of wheat gluten (WG) by the addition of epoxidized natural rubber (ENR) compared to glycerol. This work was divided into two parts: to study the optimum ENR content for improvement of WG and the effect of together functions between ENR and glycerol on the properties of WG. Tested specimens were mixed and prepared by internal mixer and compression molding machine respectively. ENR and glycerol were varied from 10 to 40 phr. The effects of modifier types and contents on WG were evaluated by tensile impact and water absorption testing and thermal analysis. Fracture behavior and rubber dispersion were investigate with scanning electron microscope (SEM). The result revealed that the increase of ENR or Glycerol contents led to the decreases in tensile modulus and strength except for modifier content of 10 phr whereas elongation at break and impact strength increased. Glass transition temperature (Tg) of modified WG tended to decreased with the increase of ENR or glycerol contents especially for glycerol. The presence of glycerol affected on the decomposition temperature (Td) values but those were unchanged for case of ENR. Water resistant of WG specimen was improved by the presence of ENR whereas the increase of glycerol led to weight loss at immersion time of 2880 min. For the effect of ENR : glycerol ratios it indicated that glycerol enhanced tensile resistances but suppressed impact and water resistances of modified WG by ENR. Sizes and dispersion of ENR particles were improved by the addition of glycerol. Tg and Td values of modified WG by ENR and glycerol increased when ENR fractions were increased.