This research aimed to study the use of coarse aggregate obtained from removing old recycled asphalt pavement (RAP) in the production of the porous concrete paving block. Crushing and size separation of the coarse aggregate by using standard sieve size by selected the gradation size of the coarse aggregate that passed to sieve size 1/2” and retained on sieve size 3/8” and other that passed to sieve size 3/8” and retained on sieve size No.4 by mixing ratio 50 : 50 of the mass as replaced natural coarse aggregate. Portland cement quantity about 18% and 20% by weight of the aggregate. The water to cement ratio was 0.30 and 0.35 respectively. Compressive strength flexural strength and water permeability were investigated. The results showed that the cement content and water to cement ratio was influenced the strength properties and water permeability rate of the porous concrete paving block. The porous concrete paving block mixed with higher cement content (20%) had the compressive strength at the age of 28 days increased by 16-24% when compared with lower cement content (18%). On the other hand the water permeability rate decreased by 5.1-8.1%.

During the epidemic of the coronavirus covid-19 single-use plastic containing products were in high demand across the community and may not be cost effective to recycle. However repurposing such materials can reduce their environmental impact for instance plastic foam waste can be made into pots for planting different types of plants and trees. By mixing the foam with a suitable cement in a ratio of 1:1 a large range of pot diameters from 4.5-10 inches can be produced suitable for both indoor and outdoor planting requirements. These pot products suitable for growing plants of all sizes are durable unbreakable water tight. Therefore it is a product that repurposes the leftovers from the community and may even add value. This strategy helps reduce the problem of waste and in particular encourages replenishment of green space to nature and the environment which also helps to combat global warming.

WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%

This research was on the production of hardmetal from recovery of tungsten carbide tool scraps recycling through ball milling for 40 hours. The metal powder obtained which was of the size between 0.11-0.22 µm was composed of 96.69% of tungsten carbide (WC) 1.68% of tantalum (Ta) 1.21% of titanium (Ti) and 0.42% of niobium (Nb). When mixed with 5-15% cobalt binder metal cold isostatic press (CIP) sintered at 1450 ° C it became hardmetal work piece dimension 12.39 x 13.82 x 5.60 mm with 1410 HV hardness and 14.34 g/cm3 density. The result of S45C steel turning was tools life good. The research concluded that the hardmetal work piece produced by the developed material had suitable basic specification and would lead to the development in working in the future.

การวัดค่าความแข็งเป็นวิธีการตรวจสอบคุณภาพวัสดุและชิ้นส่วนโลหะที่เป็นที่นิยมกันอย่างกว้างขวาง โดยเฉพาะชิ้นส่วนเหล็กกล้าที่ผ่านกรรมวิธีทางความร้อนจำเป็นต้องตรวจวัดค่าความแข็ง เพื่อตรวจสอบความถูกต้องของกระบวนการผลิตการวัดค่าความแข็งมีหลายวิธีแต่ที่นิยมกันมากคือ การวัดความแข็งแบบร็อคเวลล์ เครื่องวัดความแข็งเป็นอุปกรณ์ที่สำคัญ ดังนั้นจำเป็นต้องทำงานได้อย่างถูกต้องแม่นยำ การตรวจสอบถึงความแม่นยำของเครื่องวัดค่าความแข็งอาจจำเป็นต้องตรวจสอบเป็นประจำทุกครั้ง โดยเฉพาะถ้าเป็นการผลิตชิ้นงานแบบจำนวนมาก วิธีการตรวจสอบเครื่องวัดความแข็ง คือการสอบเทียบกับวัสดุอ้างอิงมาตรฐานทางความแข็ง วัสดุอ้างอิงทางความแข็งจึงนับว่าเป็นอุปกรณ์ที่สำคัญ ซึ่งปัจจุบันยังไม่มีการผลิตใช้ในประเทศ ต้องนำเข้าจากต่างประเทศจึงมีราคาค่อนข้างสูง ดังนั้นงานวิจัยนี้จึงมีแนวความคิดที่จะทำการศึกษาความเป็นไปได้การนำผลิตแท่งอ้างอิงทางความแข็งกลับมาใช้ใหม่ โดยจะต้องให้ได้มาตรฐานและคุณภาพที่ทัดเทียมกับแท่งสอบเทียบที่ผลิตจากต่างประเทศ และเป็นที่ยอมรับตามมาตรฐานสากลโดยใช้มาตรฐาน ISO 6508-3:2005 ในการอ้างอิง โดยเบื้องต้นจะเน้นเฉพาะแท่งอ้างอิงทางความแข็งมาตรฐาน ร็อคเวลล์ สเกลซี และช่วงความแข็งที่จะเริ่มทดลอง 20 30 40 50 และ 60 HRC ผลการวิจัยสามารถควบคุมรูปร่างและส่วนขนาดความแข็งเฉลี่ยในแต่ละระดับความแข็งใกล้เคียงความแข็งเดิม และ มีค่าพิสัย (Range) อยู่ในมาตรฐานของแท่งอ้างอิงทางความแข็งหน่วย ร็อคเวลล์ลเกลซี ตามมาตรฐาน ISO 6508-3:2005 สรุปผลการวิจัยแท่งอ้างอิงทางความแข็งที่เลือกมาใช้ในการทดลองสามารถนำกลับมาใช้ใหม่ได้ตามกระบวนการที่ได้ทำการวิจัย