This research aims to develop the coconut coir and fiber indoor acoustic and thermal insulation boards mixed with natural latex. The 5 ratios of coconut coir: coconut fiber: natural rubber were equal to 0.1: 0.9: 0.1 0.1: 0.9: 0.15 0.1: 0.9: 0.2 0.1: 0.9: 0.25 and 0.1: 0.9: 0.3 by weight. The indoor acoustic and thermal insulation boards were produced by knitting the coconut coir and fiber spraying the natural latex and heat compressing. The properties testing of indoor acoustic and thermal insulation boards included the density test water absorption test tensile strength test thermal conductivity test sound protection efficiency test and real usage test. From the results 0.1: 0.9: 0.15 ratio is the most suitable ratio of coconut coir and fiber indoor acoustic and thermal insulation board mixed with natural latex. The natural latex which putted in these indoor acoustic and thermal insulation boards can reduce the water absorption and increase tensile strength and sound protection efficiency.

This research aims to develop the coconut coir ceiling board mixed with natural latex. The 6 ratios of gypsum plaster: coconut coir: sodium silicate: natural rubber: tap water are equal to 1: 0.15: 0.03: 0.00: 1 1: 0.15: 0.03: 0.01: 1 1: 0.15: 0.03: 0.02: 1 1: 0.15: 0.03: 0.03: 1 1: 0.15: 0.03: 0.04: 1 and 1: 0.15: 0.03: 0.05: 1 by weight. The ceiling boards were produced by casting in normal temperature (30 – 35 degree of Celsius). The properties testing of coconut coir ceiling board mixed with natural latex followed the TIS 219-2009 standard (gypsum plasterboard) including: breaking load nail pull resistance deflection water absorption density thermal conductivity coefficient and real usage. From the results 1: 0.15: 0.03: 0.03: 1 ratio is the most suitable ratio of coconut coir ceiling board mixed with natural latex. This developed ceiling boards can reduce the quantity of coconut coir waste and get the good thermal insulation ceiling board products.

The objective of this research is to develop the high corrosion resistance and good thermal insulation precast adobe wall panels mixed with natural latex. The 6 ratios of Portland cement type1: clay: rice husk ash: straw: rice husk:waterproofed liquid: natural latex: tap water were designed including: 1: 3: 0.3:0.02: 0.02: 0.02: 0: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.05: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02:0.1: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.15: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.2: 0.4 and 1:3: 0.3: 0.02: 0.02: 0.02: 0.25: 0.4 by weight. The precast adobe wall panels castedas same as the common concrete and reinforced by the bamboo. From the resultsthe proper ratio of precast adobe wall panel mixed with natural latex was 1: 3: 0.3:0.02: 0.02: 0.02: 0.1: 0.4 ratio. The properties of the proper precast adobe wall panelincluded density 1810.83 kg/m3 water absorption 17.16 % compressive strength 15.13MPa bending strength 3.01 MPa thermal conductivity coefficient 0.234 watt/m.Kelvin. Moreover the proper precast adobe wall panel mixed with natural latex also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. The proper amount of natural latex effected the precast adobe wall panels to improve the mechanical properties including: increase the compressive and tensile strength decrease the density thermal conductivity coefficient and water absorption.

The objective of this research is to develop the concrete flooring tile product from old asphalt road waste. The 6 ratios of Portland cement type1: coarse sand: old asphalt road waste: water reducer type A: tap water were designed including: 1: 5: 0: 0.02: 0.4 1: 4.5: 0.5: 0.02: 0.4 1: 4: 1: 0.02: 0.4 1: 3.5: 1.5: 0.02: 0.4 1: 3: 2: 0.02: 0.4 and 1: 2.5: 2.5: 0.02: 0.4 by weight. The concrete flooring tile casted with the compressive machine. The property tests followed the TIS.378 - 1988 (concrete flooring tiles). According to the result it was found that the 1: 2.5: 2.5: 0.02: 0.4 was the proper ratio of the concrete flooring tile. The increasing of old asphalt road waste in concrete flooring tile effected to decrease the water absorption and thermal conductivity properties. In term of the density and bending strength properties there were not many differences. The developed concrete flooring tile product from old asphalt road waste can use as same as the common concrete flooring tile product in market.

This research aims to develop the natural rubber and ethylene vinyl acetate (EVA) plastic floor tile with flame resistance property. The 6 ratios of natural-rubber STR 20: zinc oxide: stearic acid: sulfur: mercaptobenzothiazole: diphenyl guanidine: EVA plastic: antimony trioxide were equal to 100: 5: 2: 3: 0.5: 0.2: 20: 0 100: 5: 2: 3: 0.5: 0.2: 20: 20 100: 5: 2: 3: 0.5: 0.2: 20: 40 100: 5: 2: 3: 0.5: 0.2: 20: 60 100: 5: 2: 3: 0.5: 0.2: 20: 80 and 100: 5: 2: 3: 0.5: 0.2: 20: 100 by weight or phr. The samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius with 30x30x0.2 cm of dimension for 4: 29 to 5: 19 minutes. The properties of the natural-rubber floor tiles were tested under ASTM standard. From the results it was found that the natural rubber and ethylene vinyl acetate plastic floor tile with flame resistance property was the suitable ratio for using as the rubber floor tiles in building and extinguished a fire by themselves. The antimony trioxide effected to increase the density hardness and thermal conductivity and decrease the tensile strength tear strength and wear resistance properties of the natural rubber and EVA plastic floor tiles