The plastic outlet problem is a rigid inflexible material. When assembling with a metal outlet set then it is usually not completely homogeneous. When used The outlet burns out quite often. And the plastic itself is less heat resistant. This allows the plastic to melt burn easily and conform to the upgrade of technology capabilities in precision mold manufacturing. And high complexity The researcher has foreseen the factors in making Developing the design and manufacturing of rubber plug molds economic opportunities for Natural Rubber Applications Therefore came up with the idea to develop the design and material selection. And the factors that affect the production is the mold and the process of forming. To help entrepreneurs to exchange knowledge and study the knowledge from this research to continue in the application of natural rubber to increase future value. From the results and experiments it was found that the study of the method of creating a prototype compression molding kit by using rubber forming techniques can be applied and used by various components of forming rubber can be used to develop forming Rubber plug sockets are possible and this process can produce prototypes from natural rubber.

The purpose of this research was to study hot-melt adhesives from natural rubber (Standard Thai Rubber 20 STR 20). In order to improve the adhesion and melting properties of hot-melt adhesive to get the best glue formula from STR 20 the ethylene vinyl acetate content (EVA) paraffin wax (Wax) and petroleum resin (Resin) were varied from 25 50 100 125 and 150 phr (Part Per Hundred Rubber). It was found that the best adhesive formulas consisted of 100 phr of STR 20 25 phr of wax 150 phr of EVA and 150 phr of resin. For preparing hot-melt adhesive first the wax was heated and maintained at 160-170 ºC then cut the STR 20 into small pieces and slowly added the rubber into the melted wax until the rubber was completely melted. And then added resin and EVA and cooled to room temperature finally the results show that hot-melt adhesive was dark brown hard and odorless smooth texture and easy to melt with 514±14 centipoises of Viscosity at 150 ºC 82.49±1.4 lbf/in2 of shear strength and 2.06±0.02 kN/m of cleavage peel strength.

This research aims to develop the coconut coir and fiber indoor acoustic and thermal insulation boards mixed with natural latex. The 5 ratios of coconut coir: coconut fiber: natural rubber were equal to 0.1: 0.9: 0.1 0.1: 0.9: 0.15 0.1: 0.9: 0.2 0.1: 0.9: 0.25 and 0.1: 0.9: 0.3 by weight. The indoor acoustic and thermal insulation boards were produced by knitting the coconut coir and fiber spraying the natural latex and heat compressing. The properties testing of indoor acoustic and thermal insulation boards included the density test water absorption test tensile strength test thermal conductivity test sound protection efficiency test and real usage test. From the results 0.1: 0.9: 0.15 ratio is the most suitable ratio of coconut coir and fiber indoor acoustic and thermal insulation board mixed with natural latex. The natural latex which putted in these indoor acoustic and thermal insulation boards can reduce the water absorption and increase tensile strength and sound protection efficiency.

This research aims to develop the natural rubber and ethylene vinyl acetate (EVA) plastic floor tile with flame resistance property. The 6 ratios of natural-rubber STR 20: zinc oxide: stearic acid: sulfur: mercaptobenzothiazole: diphenyl guanidine: EVA plastic: antimony trioxide were equal to 100: 5: 2: 3: 0.5: 0.2: 20: 0 100: 5: 2: 3: 0.5: 0.2: 20: 20 100: 5: 2: 3: 0.5: 0.2: 20: 40 100: 5: 2: 3: 0.5: 0.2: 20: 60 100: 5: 2: 3: 0.5: 0.2: 20: 80 and 100: 5: 2: 3: 0.5: 0.2: 20: 100 by weight or phr. The samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius with 30x30x0.2 cm of dimension for 4: 29 to 5: 19 minutes. The properties of the natural-rubber floor tiles were tested under ASTM standard. From the results it was found that the natural rubber and ethylene vinyl acetate plastic floor tile with flame resistance property was the suitable ratio for using as the rubber floor tiles in building and extinguished a fire by themselves. The antimony trioxide effected to increase the density hardness and thermal conductivity and decrease the tensile strength tear strength and wear resistance properties of the natural rubber and EVA plastic floor tiles

This research presents the engineering properties of asphalt (AC 60/70) modified with different ratios of scrap natural rubber. Then select the best properties of the binder to mix asphaltic concrete. From laboratory testing results with adding 7% scrap natural rubber into mixtures for the best results. The properties of asphaltic concrete can be improved by adding 7% scrap natural rubber. For asphaltic concrete Marshall Stability increased with adding scrap natural rubber into asphalt. Moreover the stiffness modulus of asphaltic concrete can be improved 13.53 compared to AC 60/70.