The objective of this study is to improve the efficiency in manufacturing process of Arabian-style ventilation bricks with a new production method that uses a machine. The study focuses on all steps of productions in order to increase productivity. After the experiment the study shows that the improvement of ventilation brick manufacturing includes the increase in production volume from 20 pieces per day to 50 pieces per day representing an increase of 76.19 percent; and the decrease in production cycle time originally from 1401 minutes per piece to 97 minutes per piece representing a decrease of 93.07 percent respectively.

The purpose of this study were to conduct and to evaluate the effectiveness of Automotive service technician The research procedure starting by collect and study document : research paper international occupational standard (Oklahoma Department of Career and Technology Education) and competency needed in Motorcycle Mechanic suggested by 7 person who working in this field. All data will be referred for behavior objectives list and learning materials design such as information sheet practice operation sheet for experience skill training evaluation sheet with evaluation criteria which clearly listed topics. The sample group in this study was 19 PAJAMANGALA UNIVERSITY OF TECHNOLOGY PHRANAKHON Faculty of Industrial Education in academic year 2 0 1 7 . Pre-test will be given before training steps according to the manual. The students will do the test after each training topic. At the training end Post-test will be given and student final assignment will be evaluated by 5 experts. The Pre-test and Post-test scores will be statistical mean difference test. The research results found that the student final assignment competencies evaluation in percentage mean score was 87.55/94.66/85.13 that higher than 80/80/80 about the expectation. The test percentage mean score after training each topic was 92.11 that higher than 90 about the expectation. The percentage mean score difference test between before and after training was significant at statistical level .01 and the after training score was higher than before training score.

This research is to study the recycling of residue clams shell from Mahachai Samutsakorn Thailand. This waste was collected from canned clams industry and it can be recycled as the composition of Mon brick instead of the rice husk. The study of clams shell composition found that Calcium was main composition as 98.50%VS. The moisture and ash content was 0.88% and 58.27%TS respectively. The works methodology is using ash from clams shell incinerated at temperature 900 1000 1100 and 1200oC in 5 hours respectively instead of rice husk in Mon brick processing. The fabrication of Mon brick was in size 5x5x5 cm adding ash from clams shell intead of rice husk. The result found that increasing the temperature to incinerate clams shell ash instead density and compressive strength increased while moisture and water absorption deceased. When Mon brick was fabricated in standard size at 6x15x3.5 cm the changed material characteristics was in the same trend as previous size. Mon brick in standard size adding 100% clams shell ash instead of rice husk had density 2.63 g/cm3 moisture content was 2.86% water absorption at 1 and 24h was 17.40 and 20.16% respectively and compressive strength was 0.52 MPa. These characteristics was according to standard of Engineering Institute of Thailand. It can reduce the cost of rice husk in Mon brick factory 28800 bath/year while the waste from canned clams factory could be reduced 20.94%.

This research aims to produce scrap page kaolin of brick construction. The kaolin clay ratio of 100: 0 80:20 60:40 50:50 40:60 20:80 and 0: 100 by volume Add mixed with rice husk and rice 15 percent by weight A total of seven ratios. According to standard tests or TIS. 77-2545 ordinary story brick building. The moisture content and water absorption is increasing. While density Thermal conductivity resistance flexural and compressive strength tends to decrease. The best ratio of 80:20 by volume with compressive strength 43.16 kg / cm 2 and 24.93 percent water absorption. Criteria standard of TIS. 77-2545 requiring compressive strength not less than 35 kg / cm2 and water absorption must not be higher than 25 percent. Can be used in the manufacture of brick construction including building decorative wall can be developed into products. Because skin color and beautiful

จากการทดลองวิจัยพบว่าดินลูกรัง ที่ใช้ในการททำวิจัยเป็นดินชั้นคุณภาพ A4 ประเภทของดินทรายแป้ง (Silty Soils) โดยมีอัตราส่วนผ่านตะแกรงเบอร์ 4 เทากับ 99.20% อัตราส่วนผ่านตะแกรงเบอร์ 10 เทากับ 96.20% อัตราส่วนผ่านตะแกรงเบอร์ 40 เทากับ 92.34% และอัตราส่วนผ่านตะแกรงเบอร์ 200 เทากับ 72.08% ดินลูกรังมีค่าพิกัด Atterberg พิกัดเหลว (Liquid Limit) เทากับ 17.49% พิกัดพลาสติก (Plastic Limit) เทากับ 15.08 % และดัชนีมวลดิน (Plasticity Index) เทากับ 2.41% องค์ประกอบทางเคมีของดินลูกรังพบว่าดินลูกรังมีซิลิกอน ออกไซด์ (SiO2) อลูมิน่า ออกไซด์ (Al2O3) ไอรอน ออกไซด์ (Fe2O3) เป็น 58.60 % 25.50% 13.00% ตามลำดับและพบสารประกอบ Silicon Oxide (SiO2) : Quartz ดินลูกรังมีผลการทดสอบหาความหนาแน่นปรากฏมีค่า 2.69 g/cm3 ความถ่วงจำเพาะ 2.32 ค่า Loss on Ignition 3.43 % การกระจายตัวของขนาดอนุภาค 28.42 μmขนาดรูพรุน 42.62 μm และพรุน ตัว 47.74% การขึ้นรูปตามอัตราส่วนของ ดินลูกรัง – พลาสติก ที่ดินลูกรัง 100% 90% และ80% ไม่สามารถอัดขึ้นรูปได้เนื่องจากดินมีมวลที่ละเอียดเมื่อขึ้นรูปจะไม่เกิดการยึดเกาะระหว่างมวลกับพลาสติกดังรูปในตารางและอัตราส่วนดินลูกรังตังแต่ 70%-0%สามารถขึ้นรูปได้สมบูรณ์ ตัวอย่างทดสอบดินลูกรัง-พลาสติกที่มีกำลังอัดสูงขึ้นตามเวลาที่ทำการกำ เนื่องจากวัสดุ HDPE มีความเหนียวและยืดหยุ่นทำให้วัสดุทดสอบไม่มีการแตกหักแต่จะเปลี่ยนรูปตามแรงที่กระทำ ซึ้งพบว่าดินลูกรังผสมพลาสติกเมื่อเพิ่มปริมาณพลาสติกมากขึ้นกำลังรับแรงเพิ่มตามสำดับผู้ใช้ควรเลือกใช้ตามความเหมาะสมกับงาน ปริมาณดินลูกรัง 50% ขึ้นไปตัวอย่างจบน้ำและปริมาณดินลูกรังตำกว่า 50% ก้อนตัวอย่างทดสอบลอยน้ำ ตัวอย่างสามารถดูซึมน้ำได้น้อยกว่า 30% ทุก ตัวอย่างที่สามารถขึ้นรูปได้ ซึ้งสามารถนำไปใช้ในงานก่อสร้างได้ ดินลูกรังผสมปลาสติกไม่เกิดการเปลี่ยนแปลงปริมาตรหรือเกิดน้อยมาก ซึ้งเป็นคุณสมบัติที่ดีของวัสดุก่อสร้าง ผลการทดสอบด้วยกล้องขยายกำลัง 50x พบว่าดินลูกรังสามารถขึ้นรูปได้ด้วยการประสานของพลาสติกโดยยิงมีอัตราสวนของพลาสติกมากยิงทำให้มีความสามารยึดเกาะขึ้นรูปและกำลังได้ดีตามไปด้วย