This research is to test the fatigue endurance of the material by using end bending of specimen. The testing material is S45C steel and forming to the standard size for testing. The specimens with a diameter of 8 mm required a different bending moment. It was found that the large bending moment affects the fatigue of the specimen. The specimen quickly damaged due to the high bending stress and there were a small number of load cycles. If the bending moment acting on the specimen was reduced to the bending stress decreased and the number of load cycles increasing. It was shown that the bending stress and the magnitude of the bending moment affected the fatigue of the material. Also the appearance of damage marks of the specimen will have a flaw around the fracture surface. Then the flaw will be enlarged until the specimen will be damaged by fracture.

The objective of this research is to study the suitable factor level for the improvement of annealing furnace for rolled coils steel sheet. The experimenting has been performed to find suitable oxygen level by 5 annealing furnace experiment. The research has been started by collection the combustion. After that the burning adjustment by changing combustion technology with 5 levels of BGCV control valve open as 23% 40% 50% 75% and 100% has been implemented. The combustion adjustment data are recorded analyzed and compared with incomplete combustion value. The research result has been found that after improvement the combustion value. The percentage of oxygen level are improved to the better quality which standard at MV0-49% equal 2.5-4 O2% and MV50-100% equal 1.5-2.5 O2% conclusion 1 furnace as follows at the MV23.1% MV40% MV50% MV75% and MV100% level of oxygen as 2.5% 3% 3% 2% 1.5% and level of carbon monoxide as 0 ppm 2 ppm 2 ppm 2 ppm and 0 ppm respectively. Resulting of fuel energy consumption in the annealing process has been reduced around 225608 baht /year/furnace. Therefore it can depict that energy saving and annealing furnace efficiency improving are increased. The modified parameters will be applied to be the new standard reference values for the further engineer’s operational manual.

Deterioration of reinforced concrete deep beam structure caused by chloride is severe andtakes up wide area even though the structure is not exposed to sea water or brackish water. Even the structure which is far from sea water or brackish water is affected by this problem.When the reinforced concreate deep beam structure is affected by chloride steel reinforced inside the structure is corroded resulting in reducing the cross-sectional area of the reinforced steel affecting load capacity deflection and beam failure. If there is no repair or strengthening such capabilities are continuously reduced until it is no longer safe to use the beam. Therefore it is necessary to repair or strengthening the deteriorated structure to be safely used. This research investigated strengthening of deteriorated reinforced concrete deep beam caused by chloride with 4 formats of carbon Fiber sheets to seek guidelines for the most efficient strengthening. The resultshowed that the strengthening by the 4 format of carbon fiber sheet could increase ultimate loadcapability yet could not improve ductility of the deteriorated beam to become close to the beamthat is not deteriorated. The strengthening that could increase the maximum ultimate load capability was the table format strengthening. In addition the strengthening that the carbon fiber making 45 degrees with the length of the beam could best prevent diagonal cracks.

The fatigue testing machine that uses the force of torsion is invented to be a compact machine that uses the torsion as the force in the test. From the tests it achieved the highest of 200 newton meters using pneumatics to test the metal materials i.e. the steel S45C molded in accordance with the JIS Z 2274 standard. To find out the capacity of the fatigue testing machine that uses the force of torsion with 8 mm 10 mm and 12 mm diameter test pieces the machine was tested with different levels of the force of torsion and the percentage of the deviation of the tests did not exceed the limit of + 10 percent. This research could reduce the cost of the procurement of the fatigue testing machine that uses the force of torsion and could be used in the instruction in the department of mechanical engineering faculty of engineering Rajamangala University of Technology Phra Nakhon in the future.

The purpose of this fashion thesis is to study the characteristics of the light color and the shape of the light of Aurora and designed the work to be novel interesting by showing the design of the ladys style costume by using the light color characteristics of Aurora a color scheme that can be combined with the technique of clothing editing binding. Dyeing batik making in costume design That makes the consumer look new unique more beautiful. The tools used in this study Is an aurora light analysis model. The sample used in this study is a photograph of Norwegian photographer Ole Christian Salomonsen. The criteria in the analysis are 2 aspects which are 1) Body 2) Color and overall analysis to be used Creative costume The results show that the aurora outline and color light is caused by charged particles in the space passing through the Earths atmosphere releasing energy in the form of light in which different colored light characteristics occur. The light curtain that you see has various shapes such as helical scrolls. Flutter wave tear streak or all three forms Applied to the costume design by paying attention to the style of the dress and the selection of various techniques including Fabric overlapping tie dyeing Batik making suitable for clothing styles for creating new and unique costume designs that meet the needs of consumers.