Special project for product development model from clay corncob artificid cactus. The purpose is to study and develop a recipe of clay from corncob and educationto the satisfaction of the targrt group for the the product development model from clay corncob cactus. A special project has analyzed the study data were fed with a mixture of clay corncob. Then query the properties of clay corncob from five experts. Clay corncob has the best feature of artificial cactus model. Then ask the satisfaction of the target group of 50 people and analyzed by using frequency percentage and mean were as follows. The Results were what: 1. The study data for use in product development model from clay corncob cactus. The process of formulation of clay use the standard formula is essentially. The researcher have adapted the ingredients and scale is appropriate to the develop recipes clay corncob. Experts have commented that the consistent of the soil is suitable to be molded into products better. In conclusion clay corncob recipes can be used cost-effectively. To increase consumer choice and disseminate knowledge of the profession. 2. Satisfaction targeted towards product development. When you consider that The product forms The goal is satisfied overall were at the highest level with an average of 4.32 the price of satisfaction overall was high with an average of 4.04 in benefits have satisfied the most valuable. materials averaged 4.66 goals in overall satisfaction in the highest level with an average of 4.47 available from target overall satisfaction is at the highest level with an average of 4.46. Keywords: Clay Corncob Artificial Cactus Model

This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties

This research aims to study the application of coconut meal and corncob fiber as high density cement-bonded fiberboard. The cement: fine sand: coconut meal and corncob fiber: water: cement setting accelerator (aluminium sulphate (Al2(SO4)3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) ratio is equal to 1: 0.2: 0.05: 0.3: 0.03 by weight. The fibers are taken from coconut meal: corncob that 5 ratios are used following: 0.0500: 0 (CN0) 0.0375: 0.0125 (CN25) 0.0250: 0.0250 (CN50) 0.0125: 0.0375 (CN75) and 0: 0.0500 (CN100) by weight. 12% of Sodium Hydroxide (NaOH) was used to modify the fibers by using 1: 10 of fiber: solution and boiling 100 degree of Celsius (1-3 hours). The fiberboard production use pressure casting in normal temperature (30 – 35 degree of Celsius) and 0.75 g/cm3 of density. Resulting the CN75 ratio is suitable ratio which pass TIS 878-2537 standard (cement bonded particle board: high density) and has good physical properties mechanical properties and thermal insulation. The most suitable cement setting accelerator is calcium chloride (CaCl2).

This research studied about mixing material to make the cement block with corncob to get a lighter weight but still have industry standard strength for non-bearing concrete block (TIS. 58-2530). Normally general cement block use 1:2 ratio by weight of cement and flour rock respectively The corncob were ground through a standard 3/8 inches sieve and were used to replace the flour rock using a ratio of 0% 3% 5% 7% and 9% by weight and setting the ratio of water per cement as 36% 40% 44% and 48% by weight. The compressive strength of 7x19x39 centimeters cement block mixed with corncob was tested at the age of 28 days. The test results to make cement block mixed with corncob showed the suitable ratio 3% corncob using instead of flour rock. The average compressive strength of the blocks was 20.09 kg/cm2 and the percent of water absorption was 12.23 % which past the Thai Industry Standard (TIS 58-2530)

This research aims to study the application of coconut meal corncob and durian peel as wood-substituted biocomposites in medium density fiberboard. The fiber: urea formaldehyde glue: isocyanate glue with polymeric diphenymethane diisocyanate type (pMDI) ratio is equal to 1: 0.13: 0.003. The fibers are taken from coconut meal corncob and durian peel that 7 ratios are used to all of fiber mixing. The fiberboard production use 130?C of temperature with 20 – 50 kg/sq.cm of compressive pressure with 8 minutes per piece of rate. Their fiberboards have 603 – 856 kg/m of density that was tested follow the TIS 876-2547 standard. Resulting the MM33 ratio (coconut meal fibers: corncob fibers: durian peel fibers is equal to 0.33: 0.33: 0.33) and the CC50 ratio (coconut meal fibers: corncob fibers: durian peel fibers is equal to 0.50: 0.25: 0.25) can pass the standard in physical properties and mechanical properties. Moreover their fiberboards have good thermal insulation