The objectives of this research were 1) to study the design and experiment of materials for producing water hyacinth basketry templates from para rubber 2) to test the water hyacinth basketry templates from para rubber 3) to create a body of knowledge in the development of water hyacinth basketry templates. from rubber latex to the community The process of operation is to design the shape of a water hyacinth basketry to suit the use of the product first after that create a water hyacinth basketry template from para rubber by experimenting with a formula mixed with natural rubber latex and experiment with weaving vegetables. water hyacinths to find the best techniques and styles Results from research on the design of water hyacinth wicker templates from rubber latex and testing of water hyacinth wicker template designs from rubber latex. The aim is to invent materials to solve the problem of replacing the old wicker template. From the research it was found that the water hyacinth basketry model was made from rubber latex. There are two techniques for creating new templates: removable templates and removable templates. and non-removable templates Removable latex coated wicker template can produce many pieces easy to weave The wicker template part is coated with rubber latex. Non-removable or weave cover It can be used to weave as a furniture product with the properties that were discovered that it has a long service life. It is durable strong and durable. Flexibility to reduce shock during weaving. and can be a tool in the profession Can reduce the cost of producing water hyacinth handicrafts Model development part There is a design template for water hyacinth basketry which is a water hyacinth wicker product that has a shape that is exotic modern beautiful and useful according to the products unique characteristics and is a valuable work that can decorate the house beautifully.

The plastic outlet problem is a rigid inflexible material. When assembling with a metal outlet set then it is usually not completely homogeneous. When used The outlet burns out quite often. And the plastic itself is less heat resistant. This allows the plastic to melt burn easily and conform to the upgrade of technology capabilities in precision mold manufacturing. And high complexity The researcher has foreseen the factors in making Developing the design and manufacturing of rubber plug molds economic opportunities for Natural Rubber Applications Therefore came up with the idea to develop the design and material selection. And the factors that affect the production is the mold and the process of forming. To help entrepreneurs to exchange knowledge and study the knowledge from this research to continue in the application of natural rubber to increase future value. From the results and experiments it was found that the study of the method of creating a prototype compression molding kit by using rubber forming techniques can be applied and used by various components of forming rubber can be used to develop forming Rubber plug sockets are possible and this process can produce prototypes from natural rubber.

Most of the current containers that we put food are made of plastic or foam boxes. After the use is finished the container becomes rubbish and will greatly affect the environment. Due to slow degradation Plus informal disposal And higher consumption The use of natural products is in great demand. Because it is beautiful and natural-looking pleasing to consumers Therefore the basic processes forming patterns were studied by rubber product molding techniques. Determine the material to be molded into the sample container. Design and build a small molding set. Provide binders used for the stabilization of natural materials. Experiment for forming and the Conclusion of the experiment From the results of operations and experiments it was found that the study of the prototype extrusion set Using a rubber molding technique Can be applied by various elements The process of rubber molding can be used in the development of natural container molding and the process can produce prototype containers from natural materials. Under the suitable size of the mold the area of the mold is smaller than the mold plate area of the machine or the size of the mold area the area of no more than 60-70% of the mold holder plate.

The objectives of this research were to study the personal and environment and investment experiences factors influencing decision making to invest in the provident funds of The Office of the Rubber Replanting Aid Fund’s Staffs. The sample consisted of 341 persons from Rubber Replanting Aid Fund’s staffs at Bangkok office (central region). The research instrument was a questionnaire and using the descriptive statistic such as mean percentage standard deviation to analyze the data and Exploratory Factor Analysis : EFA and Binary Logistic Regression Analysis to test the hypothesis. The results of the study found that sex age the knowledge and investment experiences the risks of investment the economy the politics differences influencing the decision making to invest in the provident funds of The Office of the Rubber Replanting Aid Fund’s Staffs at statistically 0.05 significant level.

The purpose of this research was to study hot-melt adhesives from natural rubber (Standard Thai Rubber 20 STR 20). In order to improve the adhesion and melting properties of hot-melt adhesive to get the best glue formula from STR 20 the ethylene vinyl acetate content (EVA) paraffin wax (Wax) and petroleum resin (Resin) were varied from 25 50 100 125 and 150 phr (Part Per Hundred Rubber). It was found that the best adhesive formulas consisted of 100 phr of STR 20 25 phr of wax 150 phr of EVA and 150 phr of resin. For preparing hot-melt adhesive first the wax was heated and maintained at 160-170 ºC then cut the STR 20 into small pieces and slowly added the rubber into the melted wax until the rubber was completely melted. And then added resin and EVA and cooled to room temperature finally the results show that hot-melt adhesive was dark brown hard and odorless smooth texture and easy to melt with 514±14 centipoises of Viscosity at 150 ºC 82.49±1.4 lbf/in2 of shear strength and 2.06±0.02 kN/m of cleavage peel strength.