his research work aimed to study the effects of the addition of sisal fiber and surface treatment by epoxy silane on the physical and thermal properties of polylactic acid (PLA). Specimens of PLA and unidirectional fiber-reinforced composite were processed by a compression molding machine and evaluated the physical and thermal properties by water absorption measurement and differential scanning calorimetry (DSC) analysis respectively. The result showed that water absorption tended to increase by adding sisal fiber whereas surface treatment of sisal fiber by epoxy silane improved water resistance of composites. The water absorption values at immersion time of 5 days were 0.89 1.13 and 1.26 % for PLA PLA/treated sisal fiber composite and PLA/untreated sisal fiber composite respectively. For thermal properties the addition of sisal fiber led to decreases in glass transition temperature and crystallinity. These were because the presence of continuous fiber might interfere with the crystallization of PLA. The surface treatment of continuous fiber with epoxy silane led to difficult crystallization. The good interfacial adhesion interrupted PLA alignment.

This research 1) to study and analyze the relationship between the context of industrial handicraftsproperties of agricultural waste in community areas and 2) to agricultural waste to find physical properties and the industrial handicrafts for Bantumsua community Phetchaburi province. From primary data it was found the relationship of the community with the context of industrial crafts is a culture of agricultural wisdom from the collection of participatory research data. Found method and test the properties of paper pulp from agricultural waste where banana leaves = A bamboo leaves = B and pineapple leaves = C.Use the formula for quantifying the triangular grid the Trixie Blend Diagram to uses caustic sodium hydroxide 10-15% of dry weight. There are 7 test items 1 formula thin and thickness (a) according to the experimental standard referring to the community product standards plant fiber paper. For testing as follows: 1) standard average weight from the test of paper size 45x85 cm operation number list of the experimental formula test section 1.1) standard weight the overall average is equal to 220 grams/sqm. 1.2) part 2 tear strength which is strong = 3(10a) at 1962 mN the second strength = 1(8a) at 1907 mN and third = 6(13a) at 1467 mN. 1.3) Part 3 the overall moisture content of the paper the experiment found the humidity level is within the normal level at ± 10% which is complete and can be developed into a products or package. 2) Summary of physical properties the color characteristics of the paper according to provide color tones gray-brown and different beautiful suitable for the screen-printing and using large size rubber stamp. Process forming can produce use by semi-automatic heat setting at 140°C at time of 70 seconds per piece is suitable for further expansion to create industrial handicrafts for the community.

In this study natural rubber latex/chitosan (NRL/CT) composites were prepared by latex mixing. The effects of chitosan on latex properties and physical Properties of NRL/CT composite films were focused. It was found that there was no significant change in the latex properties with increasing CT content. Increasing CT contents of 0.5 to 8.0 phr caused the rising of 300 % modulus of the NRL/CT composite whereas the opposite trend was found for tensile strength and elongation at break. The antimicrobial efficacy of the chitosan-incorporated rubber was slightly enhanced from that of the non-chitosan rubber. By comprehensive consideration CT content suitable for antibacterial gloves according to Thai industrial standards (TIS 1056-1: 2013) was 1 phr. For other latex products that require high modulus and antibacterial activity such as tubing pillow foam rubber nipple and catheter CT could be used at higher contents from 2 to 4 phr.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.

การวิจัยนี้เป็นการศึกษาสมบัติของโลหะเงินเจือต่ำ 58.33% ที่มีธาตุทองแดง (Cu) และดีบุก (Sn) เป็นธาตุผสม ซึ่งมีปริมาณการผสมอยู่ในช่วงระหว่าง 36.66-41.57%Cu และ 0.10-5.01%Sn ตามล่าดับ โดยท่าการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่ำ 58.33%เพื่อ ศึกษาวิเคราะห์อิทธิพลของธาตุเจือทองแดงและดีบุกที่มีผลต่อสมบัติเคมีและสมบัติทางกายภาพที่ เหมาะสมในการผลิตเครื่องประดับเงินเจือต่ำ 58.33% ผลจากการศึกษาโลหะเงินเจือต่ำ 58.33 % ที่ประกอบด้วยเงิน (Ag) และทองแดง (Cu) เมื่อน่ามา เปรียบเทียบกับโลหะเงินสเตอร์ลิง 925 จากการศึกษาเปรียบเทียบพบว่าโลหะเงินผสมเจือต่ำ ต่ำ 58.33Ag + 41.16Cu +0.51Sn มีค่า มีค่า L* = 92.18 a* = 4.64 b* = 10.71 และ ΔE = 28.32 เป็น ส่วนผสมที่เหมาะที่สุดจากการวิเคราะห์ค่าระดับสีและค่าความแตกต่างของสี และมีพฤติกรรมความ ต้านทานการหมองของโลหะเงินเจือต่ำมากที่สุด เนื่องจากอิทธิพลของธาตุดีบุก (Sn) ที่ผสมเข้าไปใน อัตราส่วนที่เหมาะสม ผลจากการวิเคราะห์ส่วนผสมทางเคมีของโลหะเงินเจือต่ำ 58.33% พบว่าส่วนผสมทางเคมีของ โลหะเงินเจือต่ำในแต่ละอัตราส่วนผสมมีสัดส่วนของธาตุใกล้เคียงกับอัตราส่วนผสมจริง จึงท่าให้โลหะเงิน เจือต่ำที่ได้ท่าการทดลองมีค่าระดับสีและพฤติกรรมความต้านทานการหมองที่สูงไม่แตกต่างกันมากนัก เป็นไปตามมาตรฐานของเครื่องประดับเงินตามมาตรฐานอุตสาหกรรมการผลิตเครื่องประดับทั้งของใน ประเทศและต่างประเทศ