The purpose of this research is to study the effect of safety measure to construction productivity for ceiling activity by studying a construction of buildings in Bangkok. The safety system composed of (1) stable scaffolding system (2) providing clean and not slip walkways on the scaffold (3) installation of handrails not less than 0.90 meters in height (4) installing stairs (5) providing personal protective equipment for workers (6) are responsible for scaffolding and (7) scaffolding permit document. Cost of the safety system is 23908 baht or approximately 33 baht/m2. Productivity rates for prior and after the used of safety system are 1.57 and 1.41 m2. /person/hr. respectively. The productivity declines for approximately 10.19 % the working time for ceiling could take longer for 10.45 % and labor cost could increase for 10.19 %.

Nowadays one of the automotive engineering is conductivity of brake pads playing a role in friction coefficient which means safety of customer. Thus thermal properties have been improved using composited materials. This project aims to study the conductivity behavior of 3 different brake pads which are supported by the company Compact International (1994) Ltd. For experimental works temperature based on brake condition was simulated from 200 to 400°C and cooled down from 400 to 200°C at 1 5 and 8 MPa of pressure respectively. By standard JIS D4413 testing condition of pressure was referred. The non-linear of conductivity value are calculated from the temperature under steady state condition. As a result of testing there are several of parameters effecting on the non-linear conductivity value. The brake pad that is a mix of high-fiber affects the fluctuation of thermal conductivity. At the same time lubricant in the brake pad cause the stability of conductivity value in different temperature range at the same pressure. On the other hand the brake pad mixed hi-copper inspires the narrow range of conductivity value in different pressures at the same temperature. Moreover the conductivity value as a mention is inversely proportion with the coefficient of kinetic friction.

The objectives of this research are to propose a linear mixed model (LMM) with spatial correlation for an analysis of rice yields in Thailand to estimate the rice yield in each month of all provinces in Thailand to investigate factors influencing on the rice yields and to construct the maps of rice yields. A linear mixed model (LMM) in which the spatial effects follow the conditional autoregressive model (CAR) is used. The estimated rice yields are used to construct the rice yield maps. The dependent variables are the rice yield in each month of each province. The data are secondary data at a provincial level. The factors considered are rainfall averaged temperatures and regions. The results show that the factors influencing on the rice yields are rainfall averaged temperature and region. The amount of regional effects ordering from largest to smallest values are northestern region southern region western region central region eastern region and northern region respectively. The top ten provinces and months with high yields ranking from largest to smallest values are Ubon Ratchathani in November (1328000 ton) Surin in Novermber (1070000 ton) Si Sa Ket in Novermber (1023000 ton) Buri Ram in November (939400 ton) Nakhon Ratchasima in November (907500 ton) Roi Et in Novermber (852800 ton) Chiang Rai in Novermber (769800 ton) Khon Kaen in Novermber (692800 ton) Maha Sarakham in Novermber (676200 ton) Udon Thani in Novermber (620600 ton) respectively. The rice yeilds maps are easy for readers to identify which areas have high or low yields. They are a useful tool for planning decision making and implementing plans to help rice famers to increase their rice production.

In this work the objective is to develop the bilayer structure consisting of hydroxyapatite-alumina (HAp-Al2O3) layer and 3 mol% yttria tetragonal zirconia (TZ-3Y) layer using conventional technique consisting of the simple pressing together with pressureless sintering. In order to obtain the desired characteristics of bilayer structure layer thickness cosintering temperature and Al2O3 addition on successful fabrication of HAp-Al2O3/TZ-3Y bilayer structure are investigated. The results indicated that the HAp-10A/TZ-3Y bilayer structure was successfully fabricated by single-end die pressing the powders in hollow cylindrical graphite die under 60 MPa pressure and further wet-bag isostatically pressing in oil to 300 MPa pressure before sintering at 1200 ˚C for 1 h. It is found that an addition of 10 vol% Al2O3 into the HAp outerlayer is the essential condition to effectively suppress the differences in densification and coefficient of thermal expansion of the two layers during cosintering at 1200 oC for 1 h. The obtained HAp-10A/TZ-3Y bilayered disc has diameter of 21.0 mm HAp-10A outerlayer of 4.5 mm thick and TZ-3Y underlayer of 2.5 mm thick. The XRD pattern of the powders crushed from its HAp-10A outerlayer revealed no transformation into other new phases demonstrating that there is no reaction between HAp and Al2O3 during sintering at 1200˚C. The cross-section morphology of HAp-10A/TZ-3Y bilayered composite obtained from the SEM result revealed the porous structure with good interconnectivity. The high porous structure of the bilayered composite provided high surface area for cell attachment indicative of good cell growth and differentiation. The primary grain sizes of HAp-10A outerlayer and TZ-3Y underlayer were in the range of 1-3 um and 100-500 nm respectively. The hardness of HAp-10A layer and /TZ-3Y layer in bilayer structure varied with different layer thicknesses. Accordingly the results presented in this work demonstrated that the HAp-10A/TZ–3Y bilayered composite fabricated by simple technique has thick HAp-Al2O3 outerlayer and strong interfacial bonding between interface layers which can be tailored for specific applications

The objective of this research was to determine and estimate the quality of ground water for producing village-tap water without pre-treatment in 3 districts Samchuk Nongyasai and Dermbangnangbuat districts Suphanburi province. Villagetap water was collected from 88 boreholes covered 17 sub-districts in June 2014 and January 2015 using standard method and then correctly preserved before analysis process. The result showed that pH conducted in filed using pH meter found in the range 7.0 to 9.2. Total hardness was found in the range of 110 to 590 mg/L as CaCO3. The concentration of Mn Fe Pb was found in the range of 0.08 - 0.88 mg/L nd - 1.88 mg/L and nd - 0.07 mg/L respectively. The concentration of Cd was to be non-detectable for all samples. The result found that total hardness was found higher value than standard quality water according to publish by Ministry of Natural Resources and Environment Thailand. The contamination of Mn and Fe in some samples was higher value than maximum allowable concentration. The problem of Fecontamination can extremely affect to physical properties of quality water. The production of household-water filtration in this work was modified from Bureau of Community Technology Department of Science Service Ministry of Science and Technology. The technology communication of the production household-water filtration was conducted by workshop procedure. The production household-water filtration was conducted step-by-step. All participants can produce the household-water filtration by themselves.