The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.

Epoxy is one type of materials for adhesive. It was improved the strength by adding the filler such as iron alumina or silica. Generally the epoxy adhesive was mixed with iron for application in the metal adhesive. The mechanical properties were importance of adhesive. Because it was one factor for lifetime limit. The iron/epoxy was casted in the magnetic field which was alignment with surface of samples. The alignment of iron particles was induced with magnetic fields. The mechanical properties and wear behavior of samples were investigated hardness and wear test. It was found that the alignment of iron particles in the epoxy were improves hardness and wear.

This research is to study the recycling of residue clams shell from Mahachai Samutsakorn Thailand. This waste was collected from canned clams industry and it can be recycled as the composition of Mon brick instead of the rice husk. The study of clams shell composition found that Calcium was main composition as 98.50%VS. The moisture and ash content was 0.88% and 58.27%TS respectively. The works methodology is using ash from clams shell incinerated at temperature 900 1000 1100 and 1200oC in 5 hours respectively instead of rice husk in Mon brick processing. The fabrication of Mon brick was in size 5x5x5 cm adding ash from clams shell intead of rice husk. The result found that increasing the temperature to incinerate clams shell ash instead density and compressive strength increased while moisture and water absorption deceased. When Mon brick was fabricated in standard size at 6x15x3.5 cm the changed material characteristics was in the same trend as previous size. Mon brick in standard size adding 100% clams shell ash instead of rice husk had density 2.63 g/cm3 moisture content was 2.86% water absorption at 1 and 24h was 17.40 and 20.16% respectively and compressive strength was 0.52 MPa. These characteristics was according to standard of Engineering Institute of Thailand. It can reduce the cost of rice husk in Mon brick factory 28800 bath/year while the waste from canned clams factory could be reduced 20.94%.

This research presents the engineering properties of asphalt (AC 60/70) modified with different ratios of scrap natural rubber. Then select the best properties of the binder to mix asphaltic concrete. From laboratory testing results with adding 7% scrap natural rubber into mixtures for the best results. The properties of asphaltic concrete can be improved by adding 7% scrap natural rubber. For asphaltic concrete Marshall Stability increased with adding scrap natural rubber into asphalt. Moreover the stiffness modulus of asphaltic concrete can be improved 13.53 compared to AC 60/70.

In this work the objective is to develop the bilayer structure consisting of hydroxyapatite-alumina (HAp-Al2O3) layer and 3 mol% yttria tetragonal zirconia (TZ-3Y) layer using conventional technique consisting of the simple pressing together with pressureless sintering. In order to obtain the desired characteristics of bilayer structure layer thickness cosintering temperature and Al2O3 addition on successful fabrication of HAp-Al2O3/TZ-3Y bilayer structure are investigated. The results indicated that the HAp-10A/TZ-3Y bilayer structure was successfully fabricated by single-end die pressing the powders in hollow cylindrical graphite die under 60 MPa pressure and further wet-bag isostatically pressing in oil to 300 MPa pressure before sintering at 1200 ˚C for 1 h. It is found that an addition of 10 vol% Al2O3 into the HAp outerlayer is the essential condition to effectively suppress the differences in densification and coefficient of thermal expansion of the two layers during cosintering at 1200 oC for 1 h. The obtained HAp-10A/TZ-3Y bilayered disc has diameter of 21.0 mm HAp-10A outerlayer of 4.5 mm thick and TZ-3Y underlayer of 2.5 mm thick. The XRD pattern of the powders crushed from its HAp-10A outerlayer revealed no transformation into other new phases demonstrating that there is no reaction between HAp and Al2O3 during sintering at 1200˚C. The cross-section morphology of HAp-10A/TZ-3Y bilayered composite obtained from the SEM result revealed the porous structure with good interconnectivity. The high porous structure of the bilayered composite provided high surface area for cell attachment indicative of good cell growth and differentiation. The primary grain sizes of HAp-10A outerlayer and TZ-3Y underlayer were in the range of 1-3 um and 100-500 nm respectively. The hardness of HAp-10A layer and /TZ-3Y layer in bilayer structure varied with different layer thicknesses. Accordingly the results presented in this work demonstrated that the HAp-10A/TZ–3Y bilayered composite fabricated by simple technique has thick HAp-Al2O3 outerlayer and strong interfacial bonding between interface layers which can be tailored for specific applications