The research was aimed at studying 1) work efficiency of the accountants working for the companies registered in the Stock Exchange of Thailand 2) the influence of work motivation and self-development towards work efficiency of the accountants working for the companies registered in the Stock Exchange of Thailand and 3) guidelines for improving work efficiency of the accountants working for the companies registered in the Stock Exchange of Thailand. The questionnaires were constructed as a research tool with content validity and reliability for collecting information from 997 accountants working for the companies registered in the Stock Exchange of Thailand. The data was statistically analyzed by SPSS version 16.0 and AMOS version 6.0 with frequency distribution percentage arithmetic mean standard deviation and structural equation model analysis: SEM. The research findings indicated that the accountants in the sample group had maintenance and motivator factors in their work motivation at high level (  =3.56) and they also had professional emotional and physical development in their self-development at high level while their social development was at moderate level. Totally it said the self-development was at high level (  =3.60) and the work efficiency was 60.31%. The urgent guidelines for improving work efficiency of the accountants working for the companies registered in the Stock Exchange of Thailand were setting more appropriate working environment such as temperature brightness smell noise cleanliness safety furniture and office supplies. Furthermore the influence of maintenance and motivator factors in the work motivation and self-development had casual relationship with work efficiency of the accountants working for the companies registered in the Stock Exchange of Thailand at a statistical significance of the 0.05 and had ability to predict at good level and acceptably because the square multiple orrelation was 87.6% which its acceptance was 40% up presented by structural equation model analysis: SEM as follow: SeD = 0.070 MaF + 0.723* MoF; R2 = 0.528 WE = 0.340* MaF + 0.746* MoF+ 0.450* SeD; R2 = 0.876

The objective of this study aims to develop a concrete boat by using lightweight concrete. The use of granular foam replaced the aggregate in various quantities to reduce the weight of boat. The replacement ratios of aggregate by the granular foam were 0 25 50 75 and 100% by volume of aggregate. The test results of compressive strength tensile strength modulus of rupture and unit weight of concrete were used to find out the appropriate mixture for producing the concrete boat. The results indicated that the appropriate mixture for producing concrete boat was the replacement of aggregate by granular foam at 100% which had the compressive strength at 28 days of 50.59 kg/cm2 and the unit weight was 949.71 kg/m3. The weight of lightweight concrete was lighter than the normal concrete about 57%. The prototype of lightweight concrete boat which had 1.04 m wide 2.20 m long and 0.38 m height had about 50 kg of weight. The maximum weight capacity of the boat was 240 kg. The cost of a lightweight concrete boat was about 650 baht

Recovering of tungsten carbide (WC) with the electrolysis solution in the electrolyte to a reaction with cemented carbide scraps 0.2-1.0 V between temperature from 30-80 C concentration 1-7 N hydrochloric acid solution within 48 hours the results showed the cemented carbide dissolution proper to the influence of voltage temperature and solution concentration. Can recovering tungsten carbide purity over 95.62% of which contain other ingredients include titanium 1.74% tantalum 1.68% and niobium 0.42% concluded that the electrolysis recovering tungsten carbide is appropriate under voltage is 0.4 V temperature 80C 7 N solution of hydrochloric acid recovery rate of tungsten carbide powder about 91.37% with an average particle size of 1.0 m

This research was on the production of hardmetal from recovery of tungsten carbide tool scraps recycling through ball milling for 40 hours. The metal powder obtained which was of the size between 0.11-0.22 µm was composed of 96.69% of tungsten carbide (WC) 1.68% of tantalum (Ta) 1.21% of titanium (Ti) and 0.42% of niobium (Nb). When mixed with 5-15% cobalt binder metal cold isostatic press (CIP) sintered at 1450 ° C it became hardmetal work piece dimension 12.39 x 13.82 x 5.60 mm with 1410 HV hardness and 14.34 g/cm3 density. The result of S45C steel turning was tools life good. The research concluded that the hardmetal work piece produced by the developed material had suitable basic specification and would lead to the development in working in the future.

This research is to study the recycle process of hard materials high hardness type and cemented carbide produced by press forming and sintering process included cemented carbide mixed with tungsten carbide cobalt silicon titanium and others. The research aims to recovery tungsten to use it again. It starts in cleaning and ball milling materials for resizing from length 12-25 mm. width 10-15 mm and thickness 2.5-8.0 mm. then disintegrated with the electric-chemical process filtering metal powder cleaning and drying. The result of dissolved materials with electricchemical process in 85% condensed HCl 6-24 volts and 3-10 amperes. The solution heats up 180 degree Celsius is found that material will be 550 11m of W03 the same as usage of Phosphoric Solution. The result of the study in dissolved materials by using the conductor of electricity is found that usage of cobalt is the best to disintegrate tungsten carbide better than tungsten carbide and stainless steel 10-15%. The result of this research is found that the best practice of tungsten carbide recovery is dissolved materials with electric-chemical process in not over 7N condensed HCl 6.00 volts and 3.00 amperes. The metal powder will be almost 100% pure tungsten carbide and particle sized distribution is 34-360 11m. After ball milling for 24 hours particle sized distribution is less than 60 11m compared with the imported metal powder. It is concluded that the recycle of cemented carbide into tungsten carbide powder qualified for sintering work and produced to the durable hard materials. It ensures that this research is useful for the related industry and the approach for production of tungsten carbide which was instead of the imported metal powder.