This research aims to study the water hyacinth fiber inside high density cement fiber board. By using ratio components among cement : fine sand : water hyacinth fiber : water : catalyst accelerated the formations of cement (aluminum sulfate (AI2 (SO4) 3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) on the ratio 1: 0.2: 0.075: 0.3: 0.03 by weight of total water hyacinth fiber. The 5 ratios consist of 0.0 (A1 D1 formulae) 0.025 (A2 B2 C2 D2 formulae) 0.050 0.03 (A4 B4 C4 D4 formulae) and 0.1 (A5 B5 C5 D5 formulae) by weighted all fibers were treated with sodium hydroxide solution (NaOH) at a concentration of 12%. The fiber to solution ratio was 1: 10 boiled in open system at 100 °C for 1 - 3 hours. By compressing the mixture cast machine at normal temperature (30 - 35 °C). Use a density of 0.75 g / cm3. From the test results the ratio B4 is the appropriate ratio. Can pass TIS 878- 2537 Cement Board: high density and physical properties mechanical properties and thermal insulation are good. Accelerate the formation of the most suitable cement is calcium chloride (CaCl2)

This research aims to develop the cement board from vesicular basalt fragment. The 5 ratios of Portland cement type1: fine sand: vesicular basalt fragment: sodium silicate: tap water are equal to 1: 2: 0: 0.03: 0.5 1: 2: 2: 0.03: 0.5 1: 2: 4: 0.03: 0.55 1: 2: 6: 0.03: 0.6 and 1 : 2 : 8: 0.03: 0.65 by weight. The cement boards were produced by compression machine. The property tests of cement-bonded fiberboard followed the TIS. 878-1994 standard (cement bonded particle board: high density). From the results 1: 2: 4: 0.03: 0.55 is the most suitable ratio of cement board from coconut shell ash. This developed cement boards can apply the vesicular basalt fragment to use as the construction materials with light-weight high strength good thermal insulation and moisture protection properties

The Kaolinite development process to improve the characteristics. The Kaolinite mixed ratios are 10% 20% 30% and 40% and the result indicated that the experiment mortar-mix ratio at 0:8:2.75:0.2:0.05:0.04:0.5 of cement powder sand Kaolinite limestone superplasticised and clean water compared to No MK control sample covered ASTM standard in tensile strength more than 100 ksc compressive strength of MK20% with superplasticised at 434 ksc. The water absorption values under the standard passed

The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.

This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties