This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.

This paper describes an aluminum casting jewelry manufacturing because of the current manufacturing costs are higher. Material or metal that is commonly used to cast jewelry is silver which aluminum Alternatives to metal. Melting is There is a close color and surface finish can be beautiful. But aluminum is a material that is cheap has studied and tested. Replacement aluminum casting body jewelry. The temperature in the baking mold before casting to test all five temperatures are 550 500 450 400 350 degrees Celsius then casting body jewelry in the next stage of the research process casting jewelry with the. aluminum to Experimental temperatures used in baking mold casting plaster for the mold temperature of 400 is appropriate. Best of casting jewelry with aluminum. The results showed that there is minimal waste and a 102 pieces of 48 pieces and has a smooth surface. A similar performance to the other materials available. Similar properties

The objective of this research is a study to determine optimum forming condition of semi-finished bulk UHMWPE by using ram extruder that obtain maximum yield strength and minimum wear rate for apply to use in area of medical and mechanical application. Experimental extrusion specified forming condition consists of the temperature of 140 150 and 160 ºC and pressure of 3 5 8 and 10 MPa with the temperature exposure time of 30 minutes. After known optimum forming condition of UHMWPE powder thus forming UHMWPE filled with different kind of filler to study and determine optimum weight fraction of various types of filler that affect onto wear resistance property of UHMWPE composites. Result extruded condition at the temperature of 1 5 0 ºC under pressure of 5 MPa with exposure time of 30 minutes is an optimum extruded condition due to specimen shown a maximum yield strength ultimate tensile strength and elongation of 20.43 ± 1.21 MPa 28.33 ± 1.53 MPa and 285.60 ± 6.41 % respectively and obtain minimum wear rate of 3.02  10-9 ± 5.27  10-10 mm3/Nm. Its mechanical properties and wear resistance property higher than imported bulk UHMWPE by 23.3 % and 4.75 times respectively due to the formation of cross-linking are occurred in polymer chain and also its degree of crystallinity is high equal to 61.52%. For bulk UHMWPE IR-spectrum shown a variation peak of carbonyl group (C=O) are occurred that that it indicated the oxidation reaction at the end of polymer chain and tis degree of crystallinity is equal to 53.31% which result to decrease strength of polymer. In the case of UHMWPE filled with filler optimum weight fractions of various types of filler are as follows. 1. The filling of 0.3 wt. % Al2O3 particle size 0.05 μm shown yield strength ultimate tensile strength and elongation of 23.17 ± 3.35 MPa 34.78 ± 2.80 MPa and 229.00 ± 6.09% respectively that its mechanical properties was increased by 18.55% (increasing of ultimate tensile strength). For the wear rate is equal to 2.09  10-9 ± 3.39  10-10 mm3/Nm or its wear resistance was increased by 1.44 times in compared with initial bulk UHMWPE. 2. The filling of 0.4 wt. % Al2O3 particle size 0.3 μm shown yield strength ultimate tensile strength and elongation of 21.93 ± 0.51 MPa 25.40 ± 0.69 MPa and 267.67 ± 22.03% respectively that its mechanical properties was increased by 11.54% (increasing of ultimate tensile strength). For the wear rate is equal to 2.32  10-9 ± 4.78  10-10 mm3/Nm or its wear resistance was increased by 1.30 times in compared with initial bulk UHMWPE. ฉ 3 . The filling of 0.4 wt. % Al2O3 particle size 1 μm shown yield strength ultimate tensile strength and elongation of 23.93 ± 1.89 MPa 26.77 ± 1.20 MPa and 296.54 ± 7.51% respectively that its mechanical properties was increased by 5.83% (increasing of ultimate tensile strength). For the wear rate is equal to 2.14  10-9 ± 3.16  10-10 mm3/Nm or its wear resistance was increased by 1.41 times in compared with initial bulk UHMWPE 4 . The filling of 4 wt. % Al2O3 particle size 5 μm shown yield strength ultimate tensile strength and elongation of 22.57 ± 2.01 MPa 26.31 ± 3.11 MPa and 136.66 ± 11.67% respectively that its mechanical properties was increased by 7.68% (increasing of ultimate tensile strength). For the wear rate is equal to 2.37  10-9 ± 5.71  10-10 mm3/Nm or its wear resistance was increased by 1.27 times in compared with initial bulk UHMWPE

งานวิจัยนี้เป็นการศึกษาปัญหาในงานหล่อและพัฒนาแนวทางแก้ไขปัญหาในงานหล่อ เครื่องประดับสมัยใหม่ ที่มีการสร้างต้นแบบตัวเรือนเครื่องประดับจากกระบวนการผลิตด้วยเทคโนโลยีการ ขึ้นรูปด้วยเครื่องสร้างต้นแบบอย่างรวดเร็ว (Rapid Prototype Machine) ด้วยวัสดุแว็กซ์ wic100a โดย ทาการศึกษาอุณหภูมิการอบเบ้าปูน เพื่อกาจัดแว็กซ์ออกจากเบ้าปูนให้สมบูรณ์ แล้วทดลองนาไปหล่อเป็น ตัวเรือนโลหะ ผลจากการศึกษาการอบเบ้าปูนที่ใช้ต้นแบบตัวเรือนวัสดุ wic100a เมื่อนามาเปรียบเทียบกับ กราฟการอบเบ้าปูนที่มีต้นแบบตัวเรือนเป็นแว็กซ์เขียวทั่วไป จากการศึกษาพบว่าวัสดุแว็กซ์เขียวเมื่อได้รับ ความร้อนจะเริ่มหลอมละลายที่อุณหภูมิ 90 องศาเซลเซียส จนหลอมละลายจากก้อนเป็นของเหลว ทั้งหมดที่อุณหภูมิ 120 องศาเซลเซียส ซึ่งสามารถใช้อุณหภูมิและเวลาที่กาหนดไว้จากมาตรฐานทั่วไป นามาใช้ในการอบเบ้าปูนเพื่อกาจัดแว็กซ์ได้ โดยใช้อุณหภูมิสูงสุดเพื่อเผาไล่เศษขี้เถ้าแว็กซ์ที่ 750 องศา เซลเซียส แต่แว็กซ์ wic100a ไม่หลอมละลายในช่วงอุณหภูมิต่าว่า 270 องศาเซลเซียส แต่จะเกิดการเผา ไหม้แทนโดยใช้อุณหภูมิเผาให้ตั่งแต่ 270-450 องศาเซลเซียส ในสภาวะปกติ 350-500 องศาเซลเซียสใน เมื่ออยู่ในเบ้าปูน และต้องใช้อุณหภูมิในการเผาไล่ขี้เถ้าแว็กซ์ถึง 850 องศาเซลเซียส เพื่อเผาไล่เศษขี้เถ้า แว็กซ์ จึงจะสามารถทาให้โพรงแบบสะอาด เมื่อนาเบ้าปูนไปหล่อด้วยโลหะเงินสเตอร์ลิง 925 แล้วได้ ชิ้นงานที่มีความสมบูรณ์ดี

Thailand’s gem and jewelry industry is widely considered one of the greatest potential markets in the world. One of the important processes is producing the body jewellery or casting. The lost-wax castingtechnique is a popular technique used widely. However it can also be a source of many defects such as porosity tarnishing incomplete form filling and water stain. There is not finding causes of problems affecting the cost of production labor energy and time increased. This research aims to study the production problems and deficiencies of work piece in the actual work from10 casting industriesto identifying and preventing all these problems. This study will be helpful to entrepreneurs gems and jewelry industry to use as guidelines to prevent defects reduce waste reduce production costs and improve the casting process for the piece even more quality. The study found that most of the production process is the main the machinery / equipment and material problems the problem of secondary respectively by this process the main problem is the casting and foundry molds the injection and the candles prototype and mold making rubber the order is a minor respectively work piece for defects in castings are very common a flaw was found in the specimens I have a 6 specimen defects found in wax and defects found in rubber molds and prototypes the defect occurs in each style be caused by a wide variety of cases. Problems encountered in this study the most hole of the shrinkage problem problem of casting porosity the hole of the bubble the cracking problem the cast is not full the problem is the ceiling.