This research aims to produce the T-BAR particleboard from Physic nuts for interior building which are brought agricultural wastes to used for beneficial materials. Under the Thailand industrial standard (TIS-876-2547) specified the evaluated values such as desnsity water content water absorption thickness swelling bending strength elastic modulus and internal bonded. The experiment and evaluation processes between Physic nuts per Urea Formaldehyde ratio and Physic nuts per Phenol-cyanate based on 90:10 92:8 95:5 and 97:3 in consequence that we found the thickness of particleboard not more than 2 cm. The suitable ratio for Phenol-cyanate 92:8 percentage (Physic nuts 92% with Phenol-cyanate 8%) and suitable ratio for Urea Formaldehyde 90:10 percentage (Physic nuts 90% with Urea Formaldehyde 10%) at 120 Celsius temperature on pressing process. The Phenol-cyanate glue ratio of 0.80 gram per cubic centimeter suited to produce the particleboards averaged water content before pressing 8.89% suitable pressure in process 150 pound per square inch water content 7.65% density 0.818 gram per cubic centimeter water absorption 14.23% during 2 hours thickness swelling 8.02% during 2 hours internal bond 0.56 MPa bending strength 21.45 MPa modulus 2116 MPa. The Urea Formaldehyde glue ratio of 0.82 gram per cubic centimeter suited to produce the particleboards averaged water content before pressing 9.84% suitable pressure in process 152 pound per square inch water content 8.63% density 0.833 gram per cubic centimeter water absorption 14.36% during 2 hours thickness swelling 8.95% during 2 hours internal bond 1.39 MPa bending strength 22.37 MPa modulus 2117 MPa. As the results shown that both of Urea Formaldehyde and Phenol-cyanate with Physic nuts passed the TIS 876-2547 standard. The Physic nuts can produce the particleboards for using inside building.

This research aims to study the development of the Para rubber press machine with wrought pattern for continued 2-year project. Used natural Para rubber mixed in ta-Kuong by normally practical Para rubber farmers to evaluate the rubber press machine. It has developed the 11 roller the 3 plain duo sets of normal press rollers and the 2 duo sets of wrought rubber press rollers with the induction motor at 1430 rpm. The rotating transmission based on belts and chains. The evaluated results produced the dried Para rubber sheets thickness at 3.75 mm. on average as standard market need. From a robber sheet with enough patted on with a worker to carry the ta-Kuong to a top tray and a rubber press man to put the Para rubber piece to a machine on average the completed 185 wrought rubber sheets per hour in shorter time.

The Kaolinite development process to improve the characteristics. The Kaolinite mixed ratios are 10% 20% 30% and 40% and the result indicated that the experiment mortar-mix ratio at 0:8:2.75:0.2:0.05:0.04:0.5 of cement powder sand Kaolinite limestone superplasticised and clean water compared to No MK control sample covered ASTM standard in tensile strength more than 100 ksc compressive strength of MK20% with superplasticised at 434 ksc. The water absorption values under the standard passed

This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of light-weight precast concrete wall panel product with adding high density foam sheet. The light-weight precast concrete wall panel product was produced by covering the foam sheet with steel pouring the mortar (M3 ratio which was proper ratio) and curing the light-weight precast concrete wall panel product. From the testing results followed the TIS.2226-2548 and TIS.878- 2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 956.03 kg/m3 of density 9.18 MPa of bending strength and 0.170 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. Moreover the developing product can apply to register the petty patent.