This research aims to develop the coconut coir and fiber indoor acoustic and thermal insulation boards mixed with natural latex. The 5 ratios of coconut coir: coconut fiber: natural rubber were equal to 0.1: 0.9: 0.1 0.1: 0.9: 0.15 0.1: 0.9: 0.2 0.1: 0.9: 0.25 and 0.1: 0.9: 0.3 by weight. The indoor acoustic and thermal insulation boards were produced by knitting the coconut coir and fiber spraying the natural latex and heat compressing. The properties testing of indoor acoustic and thermal insulation boards included the density test water absorption test tensile strength test thermal conductivity test sound protection efficiency test and real usage test. From the results 0.1: 0.9: 0.15 ratio is the most suitable ratio of coconut coir and fiber indoor acoustic and thermal insulation board mixed with natural latex. The natural latex which putted in these indoor acoustic and thermal insulation boards can reduce the water absorption and increase tensile strength and sound protection efficiency.

The objective of this research is to develop the high corrosion resistance and good thermal insulation precast adobe wall panels mixed with natural latex. The 6 ratios of Portland cement type1: clay: rice husk ash: straw: rice husk:waterproofed liquid: natural latex: tap water were designed including: 1: 3: 0.3:0.02: 0.02: 0.02: 0: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.05: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02:0.1: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.15: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.2: 0.4 and 1:3: 0.3: 0.02: 0.02: 0.02: 0.25: 0.4 by weight. The precast adobe wall panels castedas same as the common concrete and reinforced by the bamboo. From the resultsthe proper ratio of precast adobe wall panel mixed with natural latex was 1: 3: 0.3:0.02: 0.02: 0.02: 0.1: 0.4 ratio. The properties of the proper precast adobe wall panelincluded density 1810.83 kg/m3 water absorption 17.16 % compressive strength 15.13MPa bending strength 3.01 MPa thermal conductivity coefficient 0.234 watt/m.Kelvin. Moreover the proper precast adobe wall panel mixed with natural latex also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. The proper amount of natural latex effected the precast adobe wall panels to improve the mechanical properties including: increase the compressive and tensile strength decrease the density thermal conductivity coefficient and water absorption.

The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.

This research aims to develop the cement board from vesicular basalt fragment which reinforced with steel wire mesh. The ratio of Portland cement type1: fine sand: vesicular basalt fragment: sodium silicate: tap water was equal to 1: 2: 4: 0.03: 0.55 by weight. The 5 sizes of steel wire mesh (steel wire no.25) were installed including: 3/8” 1/2” 5/8” 3/4” and 1”. The cement boards were produced by compression machine. The property tests of cement-bonded fiberboard followed the TIS. 878-1994 standard (cement bonded particle board: high density). From the results the 3/4 of steel wire mesh size was the most suitable size for reinforcing the cement board from vesicular basalt fragment. This developed cement boards was the construction materials which had the high bending strength good thermal insulation and moisture protection properties.

The objectives of this research are to study the product development of light weight concrete wall board mixed with coconut leaf waste for small community enterprise to find the suitable coconut leaf waste mixed ratio with cement river sand coconut leaf waste water and catalyst accelerator at 1:0.4:0.13:0.33:0.03 ratio. CC13 (1:0.13) at 28 days has density 2266 kg/m3 bending resistance 3.05 MPa heat conduction efficiency 0.236 W/m-K. The coconut leaf waste can absorb water inside and the cement board can attach to the concrete wall easily. Suitability to make the big concrete wall.