Nowadays one of the automotive engineering is conductivity of brake pads playing a role in friction coefficient which means safety of customer. Thus thermal properties have been improved using composited materials. This project aims to study the heat capacity behavior of 3 different brake pads which are supported by the company Compact International (1994) Ltd. For experimental works temperature based on brake condition was simulated from 05 to 003°C at 5 MPa of pressure. By standard JIS D4413 testing condition of pressure was referred. The heat capacity values of brake pads are calculated under the temperature conditions. As a result of testing brake pad made of copper or high metal powders result in relatively low heat capacity. On the other hand brake pads containing fiber and a large amount of fillers result in an increased heat capacity and stability in various temperature conditions. The heat capacity varied according to the operating temperature. In addition the lubricant contained in the brake pads affects the higher heat capacity and stability at various temperatures.

Nowadays one of the automotive engineering is conductivity of brake pads playing a role in friction coefficient which means safety of customer. Thus thermal properties have been improved using composited materials. This project aims to study the conductivity behavior of 3 different brake pads which are supported by the company Compact International (1994) Ltd. For experimental works temperature based on brake condition was simulated from 200 to 400°C and cooled down from 400 to 200°C at 1 5 and 8 MPa of pressure respectively. By standard JIS D4413 testing condition of pressure was referred. The non-linear of conductivity value are calculated from the temperature under steady state condition. As a result of testing there are several of parameters effecting on the non-linear conductivity value. The brake pad that is a mix of high-fiber affects the fluctuation of thermal conductivity. At the same time lubricant in the brake pad cause the stability of conductivity value in different temperature range at the same pressure. On the other hand the brake pad mixed hi-copper inspires the narrow range of conductivity value in different pressures at the same temperature. Moreover the conductivity value as a mention is inversely proportion with the coefficient of kinetic friction.

Brake system is used the friction between disk and pads. In the driving conditions the brake behavior from the driver is difference. Based on this reason the damage on disk and pads are occurring. Nowadays the ratio of compound materials in pads is several and involved automotive industry has not available enough to experiment. Thus it is difficult to brake pads damaged analyzing in several driving conditions. In this problem the mechanical property tester is main tool for experimental works and test procedure base on the Brake lining and disc brake pads compressibility JIS D 4413. The experiment emphasizes on the flexibility behavior and internal energy by volume with 3 types of brake lining and pads. For the experiment focused on conditions by normal apply brake repeat apply brake and suddenly apply brake. The results revealed the normal apply brake condition the maximum and minimum of flexibility behavior was appeared on brake lining and pads type A and type C with testing temperature at 200C. By the repeat and suddenly apply brake conditions the brake lining and pads type C and type A with 300C is given to the maximum and minimum flexibility behavior. In case of internal energy by volume the maximum and minimum energy was appeared on pads type C and type B at the 30C of testing temperature. For the testing temperature at 200 and 400C the pads type A and type B were got the maximum and minimum energy respectively. On the other hand at the high flexibility behavior is given to high internal energy at the high temperature of the apply brake condition.