This Research is to Study the Development of 6k White Gold Low Alloys Metal for Jewelry Production The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 8k White Gold Low Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn33.33%Au+50.67% Ag+8% Cu+7%Zn+1%Sn and 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 458.9 – 326.3 Degrees Celsius Respectively 33.33%Au+50.67%Ag+8%Cu+7%Zn+1%Sn It is the Formula that Gives the Lowest Value of Liquid State Change from 326.3 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 7 Percent

This research is a study of the optimum heat temperature for baking sintered castings for burnout removal of EC 500 type ash wax from cast mortar. Improving jewelry casting process to reduce waste from silver jewelry production process. By studying the temperature of the mortar. To burn remove wax from the mortar and clean the gaps. Then try to bring silver water instead of metal casting. The results of a baked casing study using the EC500 housing prototype from the study showed that the EC500 wax material is melted from all solids to ash wax by heating at 850 ° C to burn. Remove ash wax which makes the cavity clean. When the casting was casted with 925 sterling silver the most complete workpiece after the improvement of the waste jewelry casting process was found to be 1 piece 1 percent 99 pieces or 99 percent.

The purpose of this research was to investigate the optimum heat temperature for the EC500 wax cured basecoat extrusion from all castings without waxing in the mortar. To reduce waste when the casting mortar through the casting process Silver Sterling 925 silver jewelry company Muang District Chiang Mai where the waste is caused by waxing outflow. The imperfections and leave waxing inside. Experiment with high temperature heat in mortar. And analyze the quality of work surface after casting with microscope. To find defects such as droplets and porosities caused by a range of temperatures. Temperature of baking mortar There is a difference from the conventional waxing mortar temperature. That is outflow of EC500 type wax. In the mortar to live. High heat The results of the 100 sample EC500 wax samples were tested at a temperature of 25 ° C. The mortar temperature was 700 ° C. 60 percent of waste was found the mortar was laid at 750 ° C 54 percent of waste was found. The mortar temperature was 800 ° C 32 percent waste was found the mortar temperature was 850° C Detecting 1 percent waste. The results of the study show that heat temperatures of up to 850 ° C can solve the problem of casting sterling silver alloys from the EC500 wax model. Finds the least waste.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production.The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 6k White Gold Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 5%Au+42%Ag+12%Cu+3%Zn+18%Pd 25%Au+46%Ag+8%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4% Cu+3% Zn+18% Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 702.3 - 636.7 Degrees Celsius Respectively 25%Au+54%Ag+0%Cu+3%Zn+18%Pd It is the Formula that Gives the Lowest Value of Liquid State Change from 636.7 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 3.58 Percent.