The results of the experiments were found that the temperature of the castings was higher than that of the silver alloys. The workpiece temperature is 500C the workpiece is good 26%. The workpiece is 74%. The temperature is 550C. The workpiece is 26%. The workpiece is 74%. The temperature is 600C. The workpiece is 40%. The workpiece is 60%. The workpiece is a fin. There are many factors that cause fins on the workpiece. Use of low-strength mortar In addition the use of excessive compression or heat transfer resulting in the expansion and shrinkage is not equal. This causes the cracking of the metal water to expand at a temperature of 650 ° C. The fine specimen 56% of the workpiece loses 44%. This temperature results in the smallest workpiece caused by the uneven surface. Cause of the cooling rate in each part of the casting is not equal. And at 700 degrees Celsius it is best to cast silver ornaments with pink color because the results show that the work is minimal. There are 70% good work piece 30%

This Research is to Study the Development of 6k White Gold Low Alloys Metal for Jewelry Production The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 8k White Gold Low Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn33.33%Au+50.67% Ag+8% Cu+7%Zn+1%Sn and 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 458.9 – 326.3 Degrees Celsius Respectively 33.33%Au+50.67%Ag+8%Cu+7%Zn+1%Sn It is the Formula that Gives the Lowest Value of Liquid State Change from 326.3 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 7 Percent

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

The tungsten carbide powder which recycled from the scarps of cemented tungsten carbide produces the purity of 99%. Using this tungsten carbide powder to manufacture a cutting tool and test its properties are the main objective of this work. Based on the standard SNMG 120408 the cutting tool with the dimension of 12.7x12.7x4.76 is fabricated. With the 100 hours of Ball milling grinding Cobalt mixing and sintering at 1430 °C the experimental result is impressive. At 15% of mixedcobalt the cutting tool with the hardness of 2031.6 HV be able to cut S45C steel in the feed rate of 0.2 meters per revolution and 45 m/min in the cutting speed. Besides that it provides the depth of cut of 0.25 mm and when it reaches the cutting distance of 4200 mm the surface roughness is 3.65 μm. In comparison with the cutting tool made of imported tungsten carbide powder which has a hardness of 1254 HV it turned out that our cutting tool has the equivalent quality in terms of hardness and wear resistance. Hence this work is considered to be a material development and a tungsten carbide cutting tool manufacture those would be the vital base to lead us to a commercial production.

Springback behavior is a major problem of sheet metal forming process. Especially aluminum alloy which often encounter such problems often. At present aluminum alloy is increasingly of used in the automotive industry for replace of the steels due to its lightweight and good finished surface. This work aims study to springback behavior of cold rolled aluminum alloy (AA6016) during air-bending process by ISO7438/2010 test standard. To analyze the influence of bending process parameter are included: sheet thickness punch radius bending angle die open and the ratio of bending radius and material thickness (r/t) effecting to springback behavior. The results are clearly that the springback angle is likely to increase with increase of the punch radius size of die open and the ratio of punch radius and sheet thickness and the springback tenor to decrease when the sheets thickness and bending angle increased. The increased bending angle will resulted to bending surface region is roughness increase and crack occurred to follow. As a result the bending force and the springback angle decreased.