The objectives of this research are to study the production step proper ratio physical properties mechanical properties thermal insulation and sound insulation efficiency of concrete blocks mixed with coconut shell ash. The ratios of concrete block mixed with coconut shell ash include Portland cement type1: quarry dust: coconut shellash which equal to 1: 6.8: 0.2 1: 6.7: 0.3 1: 6.6: 0.4 1: 6.5: 0.5 and 1: 6.4: 0.6 by weight. Water per cement ratio are 0.6 by weight. The concrete block samples were casted by the general production as same as the ordinary concrete blocks and were tested follow TIS.58. From the results the best amount of coconut shell ash which put into concrete block is 1: 6.7: 0.3 of ratio. The proper ratios of coconut shell ash can decrease the density or weight and increase the thermal insulation and sound insulation efficiency of concrete blocks. However the high amounts of coconut shell ash effect to decrease the mechanical properties concrete blocks that are lower than TIS.58 standard.

This research aims to develop the Para-rubber floor tiles mixed with ethylene vinyl acetate plastic wastes (EVA plastics) from the factories. The study use Para-rubber STR 20 at 100 phr with various contents of EVA plastics (e.g. 0 5 10 20 40 and 80 phr) and then mixed with chemical substance at constant ratio include zinc oxide at 5 phr stearic acid at 2 phr sulfur at 3 phr mercaptobenzothiazole at 0.5 phr and diphenyl guanidine at 0.2 phr. The samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius with 30x30x0.2 cm of dimension. The properties of the Para-rubber floor tiles are tested under ASTM standard. From the results it is found that the Para-rubber floor tiles mixed with 10 phr of EVA plastics is the suitable ratio for using as the rubber floor tiles and rubber wall tiles in building. This ratio can increase the hardness and wear resistant properties and decrease the density and thermal insulation properties when compare to the Para-rubber floor tiles without EVA plastic.

This research aims to study the properties of PMA asphalt shingle roof mixed withnatural latex by various contents of natural latex to PMA asphalt (e.g. 0.0 0.5 1.0 1.52.0 2.5 and 3.0 by weight). The heat pot was used to mix the mixture with lower than160 degree of Celsius. The PMA asphalt shingle roof mixed with natural latex sampleswere cast in 20 x 20 x 0.5 centimeter of dimension and added the fiber plate and stoneflake to reinforce and decorate the roof plate. The properties of the roof plates weretested under ASTM standard. From the results it is found that all samples can resist thetemperature higher than 200 degree of Celsius and the increasing of natural latex (lowerthan 1.5 of ratio) can improve the hardness property while the tensile strength andelongation properties are decreased. However when the amount of natural latexincreased to 2.0 of ratio the tensile strength are increased. After compare the PMA asphalt shingle roof mixed with natural latex (2.0 of ratio) and the general shingle roof found that the researched shingle roof can use as well as the general shingle roof and more tightly. The research results can develop to the PMA shingle roof products and replace the import shingle roofs.

การวิจัยนี้เป็นการศึกษาพฤติกรรมการอบชุบด้วยกระบวนการทางความร้อนของโลหะเงิน เจือต่ำ58.45wt%Ag +41.55wt%Cu โดยทำการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่ำ 58.33% เพื่อศึกษาสภาวะที่เหมาะในหาการปรับปรุงคุณสมบัติเชิงกลและโครงสร้าง จุลภาคของโลหะเงินเจือต่ำที่เป็นไปตามมาตรฐานผลิตเครื่องประดับ ผลจากการศึกษาโลหะเงิน 58.33 % ที่อัตราส่วนผสม 58.33Ag+36.66Cu+5.01Sn ซึ่งมี ค่าคุณสมบัติเชิงกลจากการทดสอบเบื้องต้นมีค่าเหมาะสมที่สุด จากนั้นท่าการศึกษาค่าความแข็งแรงดึง สูงสุดแบบเส้นลวดพบว่ามีค่าความต้านทานแรงดึงสูงสุดเท่ากับ 0.36 MPa ค่าเปอร์เซ็นต์การยืดตัว 0.11% เมื่อท่าการอบที่อุณหภูมิ 650 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่ อุณหภูมิห้องปกติ และค่าความแข็งจากการทดสอบมีค่าสูงสุดเท่ากับ 105.12 HV อบที่อุณหภูมิ 600 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่อุณหภูมิห้องปกติ ศึกษาโครงสร้างจุลภาค ของโลหะเงินเจือต่ำ 58.33Ag+41.57Cu+0.10Sn เมื่อท่าการอบปรับปรุงคุณสมบัติทางความร้อนและการ ชุบแข็งแบต่างๆ พบว่าโครงสร้างจุลภาคของชิ้นงานทดสอบหลังปล่อยให้เย็นตัวในอากาศ เกิดการ เปลี่ยนแปลงจาก β phase ที่มีขนาดเล็กลงเป็นโครงสร้าง Eutectic phase ที่มี α -phase และ β - phase ขนาดเล็กและละเอียด ซึ่งมีลักษณะสอดคล้องกับโครงสร้างจุลภาคของเฟสไดอะแกรมสมดุลโลหะ เงิน-ทองแดง ผลจากการทดลองและวิเคราะห์หาค่าคุณสมบัติเชิงกลของชิ้นงานทดสอบและโครงสร้างจุลภาค ที่ได้จากการทดลองในสภาวะต่างๆ มีค่าที่เป็นไปตามมาตรฐานของเครื่องประดับเงินตามมาตรฐาน อุตสาหกรรมการผลิตเครื่องประดับ ทั้งของในประเทศและต่างประเทศ