The objective of this research is to develop the high corrosion resistance and good thermal insulation precast adobe wall panels mixed with natural latex. The 6 ratios of Portland cement type1: clay: rice husk ash: straw: rice husk:waterproofed liquid: natural latex: tap water were designed including: 1: 3: 0.3:0.02: 0.02: 0.02: 0: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.05: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02:0.1: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.15: 0.4 1: 3: 0.3: 0.02: 0.02: 0.02: 0.2: 0.4 and 1:3: 0.3: 0.02: 0.02: 0.02: 0.25: 0.4 by weight. The precast adobe wall panels castedas same as the common concrete and reinforced by the bamboo. From the resultsthe proper ratio of precast adobe wall panel mixed with natural latex was 1: 3: 0.3:0.02: 0.02: 0.02: 0.1: 0.4 ratio. The properties of the proper precast adobe wall panelincluded density 1810.83 kg/m3 water absorption 17.16 % compressive strength 15.13MPa bending strength 3.01 MPa thermal conductivity coefficient 0.234 watt/m.Kelvin. Moreover the proper precast adobe wall panel mixed with natural latex also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. The proper amount of natural latex effected the precast adobe wall panels to improve the mechanical properties including: increase the compressive and tensile strength decrease the density thermal conductivity coefficient and water absorption.

The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.

This article presents how the analysis an insulation of high voltage transformer bushing. The purpose is to analysis the moisture in the bushing to evaluate the approach for maintenance. The analysis rely on the principle of the Polarization and Depolarization Current (PDC) technique which is a technique for analyzing the insulation of high voltage equipment to test high voltage transformer bushing for a case study. This method is performed by energize 1000 Vdc into a bushing in period of time and then switch off the circuit for discharge current. Finally we calculate the moisture of main insulation of high volt bushing as well compare with standard moisture of criteria. The method is useful of preventive maintenance plane of high volt bushing and reduce the failure in the power system.

This research aims to develop the ceiling board mixed with coconut coir. The 5 ratios of gypsum plaster: coconut coir: sodium silicate: tap water are equal to 1 : 0 : 1: 0.03 1: 100: 1: 0.03 1: 150: 1: 0.03 1: 200: 1: 0.03 1: 250: 1: 0.03 และ 1: 300: 1: 0.03 by weight. The ceiling boards were produced by casting in normal temperature (30 – 35 degree of Celsius). The properties testing of ceiling board mixed with coconut coir followed the TIS 219-2009 standard (gypsum plasterboard) including: breaking load nail pull resistance deflection water absorption density and thermal conductivity coefficient. From the results 1 : 1 5 0 : 1: 0.03 is the most suitable ratio of ceiling board mixed with coconut coir. This developed ceiling boards can reduce the quantity of coconut coir waste and get the good thermal insulation ceiling board products

The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.