This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production.The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 6k White Gold Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 5%Au+42%Ag+12%Cu+3%Zn+18%Pd 25%Au+46%Ag+8%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4% Cu+3% Zn+18% Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 702.3 - 636.7 Degrees Celsius Respectively 25%Au+54%Ag+0%Cu+3%Zn+18%Pd It is the Formula that Gives the Lowest Value of Liquid State Change from 636.7 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 3.58 Percent.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. The Influence of Admixtures on Mechanical Properties was Investigated (Tensile Strength and Hardness) of 6k White Gold Alloys at Various Composite Ratios. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. Test results of Mechanical Properties of Test Pieces. The Tensile Strength of the 6k Gold Alloy is 25% Au+46%Ag+8%Cu+3%Zn+18%Pd The Highest Value was 1.14 kN / mm2 the Lowest Percentage was 64% and the Hardness was 259.87HV. The Result of this Test is that the Mechanical Properties of the Material are Brittle Material. When the Mold is Formed the Fracture and Forming will be Difficult. 25%Au+42%Ag+12%Cu+3%Zn+ 18%Pd 25%Au+50%Ag+4%Cu+3%Zn+18%Pd and 25%Au+54%Ag+0%Cu+3%Zn+ 18%Pd Tensile Strength in the Range of 0.66-0.70 kN / mm2 Percentage of Elongation in the Range of 84-90% and Hardness of 277.60 244.60 and 186.73HV Respectively. The Mechanics will Show that the Alloys of White Gold 6k 25%Au+54%Ag+0%Cu+3% Zn+18%Pd Have Similar Tensile Strength. The Maximum Percentage of Elongation is 90% and the Minimum Hardness is 186.73HV. It is Suitable for Forming because it has Ductile Material. This is a Good Mechanical Property in the Metal Forming Machine.

This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.

การวิจัยนี้เป็นการศึกษาวิเคราะห์หาสภาวะที่เหมาะสมสาหรับการหล่อขึ้นรูปตัวเรือนเครื่องประดับโลหะเงินเจือต่า 58.33 wt% AgCuSn โดยทาการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่า 58.33% เพื่อศึกษาสภาวะที่ดีที่สุดจากการปรับปรุงคุณสมบัติทางเคมีที่ส่งผลต่ออิทธิพลของคุณภาพระดับของโลหะเงินเจือต่าที่เป็นไปตามมาตราานผลิตเครื่องประดับ ผลจากการศึกษาโลหะเงินเจือต่า 58.33 % ที่อัตราส่วนผสม 58.33Ag + 41.16Cu + 0.51Sn จากการวิเคราะห์ค่าระดับสีและค่าความแตกต่างของสีและมีพฤติกรรมความต้านทานการหมองของโลหะเงินเจือต่ามากที่สุด จึงทาให้อัตราส่วนผสมนี้มีความเหมาะสมสาหรับการหล่อขึ้นรูปตัวเรือนเครื่องประดับโลหะเงินเจือต่า และพบปัญหารูพรุนจากงานหล่อของเครื่องประดับโลหะเงินเจือต่า 58.33Ag + 41.16Cu + 0.51Sn ไม่พบรูพรุนในการหล่อที่อุณหภูมิ 1000 ºC เป็นอุณหภูมิที่เหมาะสมในการหล่อได้งานที่มีคุณภาพดี โลหะมีสุดหลอมเดือดที่เหมาะสม ส่วนอุณหภูมิที่ 1040 ºC จะทาให้อุณหภูมิมีจุดหลอมละลายมาก ทาให้งานมีรอยแตกร้าวบางจุด ส่วนอุณหภูมิที่ 1080 ºC เป็นอุณหภูมิที่สูงมากเกินไป จึงทาให้ชิ้นงานมีรอยแตกมาก ส่วนปัญหาต่างๆ ที่เกิดขึ้นในกระบวนการหล่อสามารถทาการวิเคราะห์หาสาเหตุและกาหนดแนวทางการแก้ไขได้อย่างเหมาะสมเพื่อลดความสูญเสียที่อาจจะเกิดขึ้นในผลิตภัณฑ์เครื่องประดับโลหะเงินเจือต่า 58.33 wt% AgCuSn ผลจากการทดลองและวิเคราะห์หาค่าคุณสมบัติเชิงกายภาพและวิเคราะห์ปัญหาของชิ้นงานทดสอบที่ได้จากการทดลองในสภาวะที่ดีที่สุดมีค่าที่เป็นไปตามมาตราานของเครื่องประดับเงินตามมาตราานอุตสาหกรรมการผลิตเครื่องประดับทั้งของในประเทศและต่างประเทศ