This research aims to study the using oil palm fiber to develop cement-bonded fiberboard product. The mixture ratios of Portland cement type1: fine sand: oil palm fiber:tap water: catalyst are 1 : 1.95 : 0.05 : 0.40 : 0.03 1 : 1.94 : 0.06 : 0.40 : 0.03 1 : 1.93 : 0.07 : 0.40 : 0.03 1 : 1.92 : 0.08 : 0.40 : 0.03 and 1 : 1.91 : 0.09 : 0.40 : 0.03 by weight. The cement-bonded fiberboard samples are cast in 30 x 30 x 1.5 centimeter in dimension. The cement-bonded fiberboard sample testing follows the TIS 878-2537. The results show that the density thermal conductivity bending strength modulus of elasticity and tension perpendicular to surface of cement-bonded fiberboard with high quantity of oil palm fiber are lower than cement-bonded fiberboard with low quantity of oil palm fiber while that the water absorption and swelling in water of cement-bonded fiberboard with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.06 of ratio can pass the standard.

This research aims to study the using basalt rock fragments to develop as interlocking block product. The mixture ratios of Portland cement type1: basalt rock fragments are 11 : 6 1 : 6.5 1 : 7 1 : 7.5 and 1 : 8 by weight and water per cement ratio was 0.6 by weight. The interlocking block samples are cast in 10 x 20 x 10 cubic centimeter of dimension with manual compression molding machine. The interlocking block samples were tested in accordance with TCPS 602-2547 standard which subjected for the interlocking block. The results show that the weight compressive strength and thermal conductivity of interlocking blocks with high quantity of basalt rock fragments are lower than interlocking blocks with low quantity of basalt rock fragments while that the water absorption of interlocking blocks with high quantity of basalt rock fragments are higher. From this research the medium and small enterprises could choose the proper ration for the interlocking block production mixing basalt rock fragments as per requirement.

This research aims to study the usage pumice rock fragments to develop paving block product for community. The mixture ratios of Portland cement type1: sand: quarry dust: pumice rock fragments: water that there are 6 ratios. The paving block samples are casted in 30 x 30 x 5 centimeter in dimension. The paving block sample testing follows the TIS 378-2531 on concrete flooring tiles. From the experiment bending strength and thermal conductivity of paving blocks with high quantity of pumice rock fragments are lower than paving blocks with low quantity of pumice rock fragments but the water absorption of paving blocks with high quantity of pumice rock fragments are higher. However all of pumice rock fragments paving block samples with lower than 1: 2: 2.4: 0.6: 0.6 of ratio can pass the standard and the surface temperature is lower than other covering materials about 2 degree Celsius.

This research aims to produce scrap page kaolin of brick construction. The kaolin clay ratio of 100: 0 80:20 60:40 50:50 40:60 20:80 and 0: 100 by volume Add mixed with rice husk and rice 15 percent by weight A total of seven ratios. According to standard tests or TIS. 77-2545 ordinary story brick building. The moisture content and water absorption is increasing. While density Thermal conductivity resistance flexural and compressive strength tends to decrease. The best ratio of 80:20 by volume with compressive strength 43.16 kg / cm 2 and 24.93 percent water absorption. Criteria standard of TIS. 77-2545 requiring compressive strength not less than 35 kg / cm2 and water absorption must not be higher than 25 percent. Can be used in the manufacture of brick construction including building decorative wall can be developed into products. Because skin color and beautiful

This research aims to study how to use stones Pumice Products is interlocking block for community development. The mixture ratios of Portland cement type1: sand: quarry dust: pumice rock fragments: water that there are 5 ratios. The products were tested by the community TCPS 602-2547 (2004) (Thai): interlocking block. The results showed that interlocking block of stone pumice much a compressive strength and thermal conductivity under a block of stone pumice less. The water absorption is increased When a block of stone pumice much. The optimum ratio and the use of waste rock Pumice highest ratio of cement to stone dust on the stone Pumice water in a 10: 6.4: 0.6: 0.45 to 10: 6.1: 0.9. 0.45 by weight.