This research to examine the structure and mechanical properties of aluminum dross. A research project knowledge the aim is to study the microstructure and the mechanical properties of materials. The research is divided into two parts: 1 . preparation aluminum dross material and 2. to determine the structure and mechanical properties. The material must be washed in preparation contamination and dry then crushed and sifted to 200 mesh. Analyzed the microstructure with SEM which indicated the microstructure. The amount of alumina in aluminum dross grade No.0 has 8 0 percent with a powder aluminum dross grade No.1 is a hunk with crystalline alumina component 85 percent. Aluminum dross grade No. 2 which is a big hunk has crystalline alumina components 9 0 percent. Analysis results indicates that aluminum dross can be applied to other aspects such as to produce bulletproof vests and so on.

Aluminium was used in many industrial applications due to good properties such as ductile high corrosion resistant and high electrical conductivity. Since wear resistance of aluminium was very poor so that it was a limitation of using this material in several conditions. In this research aluminium was improved the wear resistance properties by using anodizing process and adding some titanium dioxide particles on the surface. The effect of anodizing process duration on the wear resistence property was studied. It was found that the process duration and amount of titanium dioxide play the important role on improvement of tribological properties of aluminium.

Aluminum is a lightweight material which are popularly used in various parts of the industry. However there are some limitations on the tribological properties such as abrasive wear and friction when it was compared to other metals. Tribological properties of aluminium was improved with anodizing process and silicon dioxide supplement. the effect of time on surface structure and friction coefficient were studied with with scanning electron microscope and sliding wear tester. It was found that friction coefficient of aluminium was decreased after improvement process was applied.

This paper aim to be improvement the installation methods for Sliding Aluminium Door and Glass in order to be the good quality product by applying the motion and time study design the new model of the receiver lock set for the sliding door. The step of study process started from studied the sliding door installation processes gathering the works process and reducing unnecessary and duplicate of work process on site elimination establishing standardized time for modifying the installation process. From the result before applied new method we founded that the installation process before installation process improvement we were spent the time of installation process at 45.38 minute per set and after we used the new method we founded that the installation process time was 35.36 minute per set it can be decreased the installation time was 10.02 minute and the efficiency of work process operation was increased 22.08 percent and the line balancing performance before improvement was 56.73 percent and after improvement was 88.40 percent and the line balancing performance was increased 31.67 percent. Unless there are the improvement installation methods it makes the company in case study will be do the work to be delay and cannot be hand over the works just in time by the schedule planning.

Springback behavior is a major problem of sheet metal forming process. Especially aluminum alloy which often encounter such problems often. At present aluminum alloy is increasingly of used in the automotive industry for replace of the steels due to its lightweight and good finished surface. This work aims study to springback behavior of cold rolled aluminum alloy (AA6016) during air-bending process by ISO7438/2010 test standard. To analyze the influence of bending process parameter are included: sheet thickness punch radius bending angle die open and the ratio of bending radius and material thickness (r/t) effecting to springback behavior. The results are clearly that the springback angle is likely to increase with increase of the punch radius size of die open and the ratio of punch radius and sheet thickness and the springback tenor to decrease when the sheets thickness and bending angle increased. The increased bending angle will resulted to bending surface region is roughness increase and crack occurred to follow. As a result the bending force and the springback angle decreased.