This research then has two main objectives. The first objective is to fabrication of bioactive glass ceramics containing BaFe12O19 (BF) crystals has been carried out for the application in hyperthermia treatment. The BaFe12O19 powder was firstly prepared and subsequently mixed with the non-silicate P2O5-CaO-Na2O bioactive glass with various BF concentrations. After that the glass ceramics were produced via a sintering method at 600◦C and their crystal phases were examined by XRD and in vitro test was carried out by soaking in simulated body fluid. Remanence and saturation magnetization and coercivity were deduced from magnetic measurement. It was found that the samples exhibited magnetic behavior which is similar to hard magnetic materials. Our second objective is the effects of sintering temperatures on the physical and bioactivity of SrFe12O19 (SF)-P2O5-CaO-Na2O bioglass ceramics were investigated. XRD results confirmed the existence of the strontium ferrite and calcium phosphate phases. SEM images showed that grain size and hardness were related to density and liquid phase present in the samples. A maximum coercivity value of 3138 Oe was obtained for the bioglass ceramic sintered at 600 ºC. The remanence (Mr) and saturation magnetization (Ms) of the bioglass ceramic sintered at 500 ºC possess the maximum value of 6.35 and 10.64 emu/g respectively. Moreover the apatite was formed on the surface layers of the bioglass ceramics confirming their biocompatibility

The purpose of this study were to conduct and to evaluate the effectiveness of Automotive service technician The research procedure starting by collect and study document : research paper international occupational standard (Oklahoma Department of Career and Technology Education) and competency needed in Motorcycle Mechanic suggested by 7 person who working in this field. All data will be referred for behavior objectives list and learning materials design such as information sheet practice operation sheet for experience skill training evaluation sheet with evaluation criteria which clearly listed topics. The sample group in this study was 19 PAJAMANGALA UNIVERSITY OF TECHNOLOGY PHRANAKHON Faculty of Industrial Education in academic year 2 0 1 7 . Pre-test will be given before training steps according to the manual. The students will do the test after each training topic. At the training end Post-test will be given and student final assignment will be evaluated by 5 experts. The Pre-test and Post-test scores will be statistical mean difference test. The research results found that the student final assignment competencies evaluation in percentage mean score was 87.55/94.66/85.13 that higher than 80/80/80 about the expectation. The test percentage mean score after training each topic was 92.11 that higher than 90 about the expectation. The percentage mean score difference test between before and after training was significant at statistical level .01 and the after training score was higher than before training score.

The objectives of this research are to study the production step proper ratio physical properties mechanical properties and thermal insulation of concrete blocks mixed with waste ceramic powder. The ratios of concrete block mixed with waste ceramic powder include Portland cement type1: quarry dust: waste ceramic powder equal to1: 6.8: 0.2 1: 6.7: 0.3 1: 6.6: 0.4 1: 6.5: 0.5 and1: 6.4: 0.6 by weight. Water per cement ratio are 0.6 by weight. The concrete block samples were castedby the general production as same as the ordinary concrete blocks and were tested follow TIS.58. From the results the best amount of waste ceramic powder which put into concrete block is 1: 6.7: 0.3 of ratio. The proper ratios of waste ceramic powder can decrease the density or weight and increase the thermal insulation efficiency of concrete blocks. However the high amounts of waste ceramic powder effect to decrease the mechanical properties concrete blocks that are lower than TIS.58 standard.

The research project investigated the effects of CoO additive on dielectric ferroelectric physical and mechanical properties of modified Bi0.5(Na0.81K0.19)0.5TiO3 ceramics were investigated. The samples were synthesized by solid state reaction technique where powders were calcined at 850 °C for 4 h and ceramics were sintered at 1050 °C for 4 h which difference heating rate controlled i.e. 100 300 and 600 °C/h for. The ceramics of BNKT/x wt.% CoO was added CoO by various x=0.00 0.10 0.20 0.30 0.60 and 0.90. Phase formation was determined by X-ray diffraction technique (XRD). The X-ray diffraction analysis of the ceramics suggests that all samples exhibited a perovskite structure. The dielectric properties under room temperature and various temperatures were also determined. Dielectric measurement data showed that the additive and heating rate controlled influenced dielectric constant and dielectric loss. Furthermore the hysteresis loop behaviors slightly changed with increasing the CoO contents.

The purpose of this project is analyze to the transparency and mechanical properties of lithium disilicate for dental application. Lithium disilicate glass-ceramic were synthesised by using melting technique in SiO2-Li2O-Al2O3-K2O -P2O5 glass system and heated treatment samples at the crystallization temperature of that glass. The Differential thermal analysis: DTA X-ray diffraction: XRD were used analysis on thermal properties phase formation. Moreoven density Hardness were determined to evaluate the properties at physical and Mechanical respective by the X-ray diffraction showed that the glass-ceramic sample demonstrated the phase of Li2SiO3 Li2Si2O5 and SiO2 . The optimum of glass-ceramic. Sample were on faired with the sample heated 650°c first step and heated at 800°c for second step. That show the highest hardness valve at 755 HV