This study was aimed to study business plan development of frozen Roti (Indian pancake) and formulate frozen Roti business strategies for the community enterprise producing traditional Muslim food in Ban Taladkaew Nonthaburi. Relevant theories documents articles as well as other useful information from in-depth interviews were collected and analyzed using the strategic management process theory. The samples used in this research were 10 community members of the traditional Muslim food stores from Ban Taladkaew. The results revealed that the strategies suitable for frozen Roti business of the community in Ban Taladkaew Nonthaburi as traditional Muslim food to increase capacity feasibility and appropriateness were Differentiation strategies. The recipe of frozen roti products a more than 150 year-old recipe with temple figurines and mosques as background showing that both Buddhist and Muslim Thais had lived together therefore Focused Differentiation was applied as consumer groups were for example students from schools nearby. Product and Operation Strategy was also used to focus on the development of standardized production processes and product quality in order to create alternative products for consumers. Marketing Strategy also help to create and increase different products from other markets which were aimed at online marketing. Finally Finance Strategy the most important one was applied to raise funds and prepare for the future business expansion.

The purposes of this research were to design and create dyed silk yarn and cotton yarn machine for community enterprises of Ban Na Pho woven group Na Pho district Buriram province. All materials were made of stainless steel and the principle of rotation of the yarn skein which was hung with spindle yarn inside the dye tank. Dyeing process began by mixing color tanks in the exterior size for diameter ๓๐๐ mm. Adjust the temperature inside the dye bag by the boiler was attached below. Using pump in dye tank for rotating the heat with stainless steel pipe in ๑๑/๒ inches and ๓ inches x ๑/๒ inches and the rectangular tank was ๖๐ cm. wide ๙๐ cm long and ๑๖๐ cm. high. It had ๕ mm. of plastic lid cover in front of and a channel that looked at the attachment of color yarn. The lid had ๒ levels adjustable lift spring lock and ๒-axis spindle yarn. It was triangular shaped drilled holes spray to ๑ mm. on the spindle with a diameter of ๑๕ cm. and ๖๐ cm. long rotating at ๑๐ rpm strength by using electric motor size ๐.๕ HP used ๒๒๐ volts. It could be rotated left and right with the gear ratios around ๒๐:๑ ๒ adjustable that were automatic with programming on the control box and simple pattern. the spray dyed paint had ๑ liter water pump to control pressure valve for opening and closing to dyed water flow regularly by the heat from the LPG gas with a head size of ๓๐ cm. and adjust the temperature up to ๑๒๐ Celsius degree. It was showed the temperature measurement of water dye with pressure gauge and temperature gauge. The efficiency of this dye can be dyed silk yarn and cotton yarn per ๕ kg. to ๑๐ kg. which was a medium-sized textile production to the local community enterprise and applied in the preparation of yarns before dying such as peeling glue and bleaching.

This research aims to develop the ceiling board mixed with coconut coir. The 5 ratios of gypsum plaster: coconut coir: sodium silicate: tap water are equal to 1 : 0 : 1: 0.03 1: 100: 1: 0.03 1: 150: 1: 0.03 1: 200: 1: 0.03 1: 250: 1: 0.03 และ 1: 300: 1: 0.03 by weight. The ceiling boards were produced by casting in normal temperature (30 – 35 degree of Celsius). The properties testing of ceiling board mixed with coconut coir followed the TIS 219-2009 standard (gypsum plasterboard) including: breaking load nail pull resistance deflection water absorption density and thermal conductivity coefficient. From the results 1 : 1 5 0 : 1: 0.03 is the most suitable ratio of ceiling board mixed with coconut coir. This developed ceiling boards can reduce the quantity of coconut coir waste and get the good thermal insulation ceiling board products

This research aims to study the water hyacinth fiber inside high density cement fiber board. By using ratio components among cement : fine sand : water hyacinth fiber : water : catalyst accelerated the formations of cement (aluminum sulfate (AI2 (SO4) 3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) on the ratio 1: 0.2: 0.075: 0.3: 0.03 by weight of total water hyacinth fiber. The 5 ratios consist of 0.0 (A1 D1 formulae) 0.025 (A2 B2 C2 D2 formulae) 0.050 0.03 (A4 B4 C4 D4 formulae) and 0.1 (A5 B5 C5 D5 formulae) by weighted all fibers were treated with sodium hydroxide solution (NaOH) at a concentration of 12%. The fiber to solution ratio was 1: 10 boiled in open system at 100 °C for 1 - 3 hours. By compressing the mixture cast machine at normal temperature (30 - 35 °C). Use a density of 0.75 g / cm3. From the test results the ratio B4 is the appropriate ratio. Can pass TIS 878- 2537 Cement Board: high density and physical properties mechanical properties and thermal insulation are good. Accelerate the formation of the most suitable cement is calcium chloride (CaCl2)

This research aims to test the properties of concrete block mixed with basalt fragment as aggregates in products. The mix ratios of Portland cement type1 : basalt fragment : water are 1 : 10 : 0.7 1 : 10.5 : 0.7 1 : 11 : 0.7 1 : 11.5 : 0.7 and 1 : 12 : 0.7 by weight. The concrete block samples were mixed and casted in 7 x 19 x 39 centimeter by the concrete block molding machine. The concrete block sample testing follows the TIS 58-2533 standard on non-load bearing concrete blocks. From the results the density compressive strength and thermal conductivity of concrete block mixed with basalt fragment are lower than the common concrete block. In addition the water absorption and volumetric change are higher than the common concrete block. The optimal ratio in this work is 1: 11: 0.7