The purpose of this project is to study the mechanical and physical properties of recycled roofing materials. The pulp extracted from the UHT beverage boxes to get aluminum foil mixed with low density polyethylene. This can be used engineering and is an option to reduce the amount of UHT boxes left over to roofing sheets. In experiment 3 aluminum foil medium size and fine then hot and extruded with 68 and 10 bar compression then cut into test pieces. To test mechanical and physical properties in accordance with the test standards: Torsion Testing Tensile strength Impact resistance Heat resistance water absorption and density testing. Compare the mechanical and physical properties of the material; different sizes of aluminum foil and compressive strength. To bring the best materials to the product. From the tests it was found that the properties of recycled composite materials From the box UHT beetroot This is made of coarse aluminum foil. 18.23 MPa bending strength 10.66 MPa tensile strength 110.987 J / m2 impact resistance 52.40 Shore-D Hardness 0.62 % Water Absorption 0.70 % Thickness Swelling 1.086 g/m3 Density 0.031 m2.K/W Thermal Resistance and 0.291 W/mK Thermal Conductivity is the best mechanical properties. Due to the large aluminum foil it can be used for high strength. Which is higher than the aluminum foil of a smaller size.

This research aims to develop the cement board from vesicular basalt fragment. The 5 ratios of Portland cement type1: fine sand: vesicular basalt fragment: sodium silicate: tap water are equal to 1: 2: 0: 0.03: 0.5 1: 2: 2: 0.03: 0.5 1: 2: 4: 0.03: 0.55 1: 2: 6: 0.03: 0.6 and 1 : 2 : 8: 0.03: 0.65 by weight. The cement boards were produced by compression machine. The property tests of cement-bonded fiberboard followed the TIS. 878-1994 standard (cement bonded particle board: high density). From the results 1: 2: 4: 0.03: 0.55 is the most suitable ratio of cement board from coconut shell ash. This developed cement boards can apply the vesicular basalt fragment to use as the construction materials with light-weight high strength good thermal insulation and moisture protection properties

The objectives of this research are to propose a proper model for risk assessment for drought in Thailand. A hidden Markov model is adopted. The results indicate that the amount of rainfall depends on the hidden states drought or non-drought state. If the state changes from drought to non-drought the amount of rain will increase. The probability of changing from drought state to non-drought state is higher than from drought state to drought state. The probability of drought occurrence in February is highest followed by in November March December January July April June October September August and May respectively. When the temperature increases the probability of drought occurrence will increase.

This Research is to Study the Development of 6k White Gold Alloys for Jewelry Production. By Studying the Influence of 6k White Gold Alloys on Physical Properties for Jewelry Molding Process. Of 6k Gold Alloys at Various Compound Rates. The Results of the Experiments Show that the Chemical Composition of 6k White Gold Alloys is Slightly Different when Compared with the XRF (X-ray Fluorescence Spectrometers). Compare the pre and Post-Melting Quantities. The Result of the Compounding Test with the Color Level of 6k White Gold at the Compound Rate 25%Au+54%Ag+0%Cu+3%Zn+18%Pd The Lowest Color Level was L * = 82.14 a * = -0.16 b * = 7.71 and the Lowest Color Difference was 21.07. With other Ingredients It Shows that the Test Specimen of 6k White Gold has a Rather Greenish Color and is Slightly Yellowish Compared to the Blue Line that Approaches the Standard line. These Properties are the Physical Properties Required to Produce a 6k White Gold Jewelry Body.