The objective of this study were 1) to develop the gas detector unit for installation on Drone and 2) to test the operational sensitivity of the developed device. The development steps included designing complying the electrical circuit testing the electrical system and online connecting system. Besides the operational sensitivity of the developed device was tested comparing the Gas Alert Micro 5 IR the reference gas detector device both in the laboratory and the field site. The results showed that the developed gas detector could detect carbon dioxide carbon monoxide and methane and displayed the results via Line notification every minute. Additionally carbon dioxide detection by MG-811 sensor gave the results similar to the reference device by 95 percent of significant level with the average amount of detected carbon dioxide in the laboratory and the field site were 700-915 ppm and 138-399 ppm respectively. However the measured results of carbon monoxide and methane from the develop device were relatively different to the reference device. Further study on carbon monoxide sensor and methane sensor calibration are recommended.

Silica is an amorphous and nanometer scale voids and porous form of silicon dioxide. As long known for its high specific surface area synthetic silica has been used to adsorb water readily and applied for keeping many biological products dry protecting equipment from moisture damage. In the study the researchers have interested in making the tentative eco-friendly dehumidifying products based on the silica extract from bamboo leaves. The extraction procedures were performed by boiling dry bamboo leaves with various concentrated hydrochloric acid (HCl) at 1 2 3 and 4 M then burning them at 650oC for 4 hr before analyzing the purity of the biosilica with the X-ray Fluorescence Method. The results showed that the highest purity of the biosilica sample at 96% could be obtained after treated with 4 M HCl comparing with the control commercial silica. By hygroscopic test the extracted biosilica with 2 M HCl showed the highest moisture absorption properties close to the commercial silica. While the highest adsorption capacity was found in the biosilica sample treated with 3 M HCl. The dehumidifying efficiencies of all HCl treated biosilica power were not much different comparing to the commercial silica gel. Instead of using synthetic silica therefore this high environmentally friendly and cheaper biosilica from bamboo leaves can preferably be decent and further applied in green industry.

The research was to develop environmental packaging from composite materials hyacinth fiber rice husk and coconut fiber for temperature preservation to replace the use of foam packaging that cannot be degraded naturally. In the composite materials water hyacinth fiber rice husk and coconut fiber at the ratios 7: 1: 2 1 : 1 : 2 and 1: 1: 1 were extruded by heat using isocyanate glue as a solder and testing the physical and biological properties of composite materials as fiberboard. For testing of temperature preservation of the bio packaging heat transfer test to obtain the bio-packaging for the environment the composite materials of fiber water hyacinth rice husk and coconut fiber at the ratio of 7 : 1 : 2 was the most appropriate type. Since it had a density of 0.7 grams per cubic centimeter strength of 26.76 MPa moisture content of 3.8 percent ages and swelling of 26.63 percent ages. In dry condition at room temperature it could store heat for 2 hours and could retain the cold temperature as shown for the temperatures rising from 4 to 30.7 degree Celsius within 2 hours. This research therefore presents a new alternative method of natural fiber composite materials application for temperature preservation in order to reduce the use of foam containers and increase cost value to natural bio waste materials.

Aluminum is a lightweight material which are popularly used in various parts of the industry. However there are some limitations on the tribological properties such as abrasive wear and friction when it was compared to other metals. Tribological properties of aluminium was improved with anodizing process and silicon dioxide supplement. the effect of time on surface structure and friction coefficient were studied with with scanning electron microscope and sliding wear tester. It was found that friction coefficient of aluminium was decreased after improvement process was applied.

Non-destructive test with Acoustic Emission technique was used for monitoring of the corrosion in the above ground oil storage tank. In the analytical characteristics of acoustic emission wave however Acoustic Emission test has to be prior used for the location detection of corrosion especially indication of the severity of corrosion. In this research the relationship between the corrosion rate and the sound wave energy was studied. The corrosion and damage detected on the surface of the aboveground storage tank was determined by the Acoustic Emission Test. Nine pieces of low carbon steel grade SS400 was soaked in sodium chloride solution in simulated tanks at concentrations of 1.5 3.5 and 5.5 wt%. Next the corrosion activity was checked by performing with the Acoustic Emission Testing for 1 hour and thus calculating the corrosion rate of the test specimens. From the experiment it was found that the rate of corrosion affects the Acoustic Emission Energy. The corrosion rate was increased with the concentrations of the solution increasing from the corrosion process. The corrosion rate was also increased with the sound wave power increases. Therefore in order to achieve the corrosion rate and the position of the defects on the inner surface of the tank non-destructive testing with acoustic emission technique can be factually chosen for this specific application.