The purpose of this project is analyze to the transparency and mechanical properties of lithium disilicate for dental application. Lithium disilicate glass-ceramic were synthesised by using melting technique in SiO2-Li2O-Al2O3-K2O -P2O5 glass system and heated treatment samples at the crystallization temperature of that glass. The Differential thermal analysis: DTA X-ray diffraction: XRD were used analysis on thermal properties phase formation. Moreoven density Hardness were determined to evaluate the properties at physical and Mechanical respective by the X-ray diffraction showed that the glass-ceramic sample demonstrated the phase of Li2SiO3 Li2Si2O5 and SiO2 . The optimum of glass-ceramic. Sample were on faired with the sample heated 650°c first step and heated at 800°c for second step. That show the highest hardness valve at 755 HV

This research aims to study the possibility of steel fibers plastic fiber (polypropylene) fly ash and metakaolin mixed into the concrete. The concrete used in the research of the w / c 0.42 By 0.5 percent in the volume of steel fiber and poly propylene fiber in the amount of 0.25 percent by weight of the concrete. Concrete example of this test consisted of plain concrete(OPC).Concrete mixing materials pozzolan fly ash mixed plastics synthetic fibers of the type poly propylene fiber(FA/PP)concrete mixing materials pozzolan fly ash mixed plastics synthetic fibers of the type steel fibers (FA/ST) concrete mixing materials pozzolan meta kaolin mixed plastics synthetic fibers of kind polypropylene fiber(MK/PP) and concrete mixing materials pozzolan meta kaolin mixed plastics synthetic fibers of the typesteel fibers (MK/ST) by casting a cylindrical sample size 10 x 20 cm. Sample size 10x10x10 cm. cube and sample size 10x10x35 cm. beam. After 28 days and cure water concrete examples to test the strength of the pull compressive strength and flexural strength. And to test the movement of chloride through the concrete with Chloride Migration Test. Then bring the strength of the pull compressive strength flexural strength and the chloride permeability of concrete. Bringing concrete materials pozzolan mixed with synthetic fibers to develop the quality of concrete with improved efficiency and also reduces the porosity of the concrete. And permeability of chloride formed in the concrete (Only in landscape with the sea). The test can tell. Concrete mixing materials pozzolan with synthetic fibers to make a significant impact on the properties of concrete is improved as well. Depending on the type of polyester and the amount of material to pozzolan blended.

The research aims to study the quality of Chaiya salted eggs coated with tea waste to partially replace soil from termite mound. The residue of tea waste dried to a moisture content of 14.9% was used to prepare salt coating paste. It was found that the mixture of coating paste by substitution of termite mound soil with 10% (w/w) tea waste was appropriate to coat the duck eggs. The salt content increased in both egg yolk and egg white with increasing salt coating time. Coating egg with 10% tea waste for 24 days egg yolk contained salt 0.83% moisture 17.04% and weighed 19.19 grams. The pH value and hardness were 6.43 and 93.67 gram respectively. The egg white contained salt 5.27% moisture 81.61% and pH value was 7.60. The salted boiled eggs coated by 10% tea waste treatment for 21 days were accepted by the panelists in terms of the overall liking with the level of much liking (8.67) not significantly different (p>0.05) from that of the control treatment (0% tea waste). Microorganisms in the salted boiled eggs did not excess Thai OTOP standard. A hundred general consumers accepted this product in terms of the overall liking with the level of much liking (8.00).

The Kaolinite development process to improve the characteristics. The Kaolinite mixed ratios are 10% 20% 30% and 40% and the result indicated that the experiment mortar-mix ratio at 0:8:2.75:0.2:0.05:0.04:0.5 of cement powder sand Kaolinite limestone superplasticised and clean water compared to No MK control sample covered ASTM standard in tensile strength more than 100 ksc compressive strength of MK20% with superplasticised at 434 ksc. The water absorption values under the standard passed

This research aims to study the using oil palm fiber to develop pseudo-plywood from polyethylene product. The mixture ratios of oil palm fiber : polyethylene are 50 : 50 55 : 45 60 : 40 65 : 35 and 70 : 30 by weight. The pseudo-plywood samples are cast in 30 x 30 x 1.5 centimeter in dimension. The pseudo-plywood sample testing follows the TIS 966-2547. The results show that the density bending strength modulus of elasticity thermal conductivity and tension perpendicular to surface of pseudo-plywood with high quantity of oil palm fiber are lower than pseudo-plywood with low quantity of oil palm fiber while that the water absorption and swelling by density of pseudo-plywood with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 65 of ratio can pass the standard.