The objective of this research is to develop the concrete flooring tile product from old asphalt road waste. The 6 ratios of Portland cement type1: coarse sand: old asphalt road waste: water reducer type A: tap water were designed including: 1: 5: 0: 0.02: 0.4 1: 4.5: 0.5: 0.02: 0.4 1: 4: 1: 0.02: 0.4 1: 3.5: 1.5: 0.02: 0.4 1: 3: 2: 0.02: 0.4 and 1: 2.5: 2.5: 0.02: 0.4 by weight. The concrete flooring tile casted with the compressive machine. The property tests followed the TIS.378 - 1988 (concrete flooring tiles). According to the result it was found that the 1: 2.5: 2.5: 0.02: 0.4 was the proper ratio of the concrete flooring tile. The increasing of old asphalt road waste in concrete flooring tile effected to decrease the water absorption and thermal conductivity properties. In term of the density and bending strength properties there were not many differences. The developed concrete flooring tile product from old asphalt road waste can use as same as the common concrete flooring tile product in market.

This research aims to develop the natural rubber and ethylene vinyl acetate (EVA) plastic floor tile with flame resistance property. The 6 ratios of natural-rubber STR 20: zinc oxide: stearic acid: sulfur: mercaptobenzothiazole: diphenyl guanidine: EVA plastic: antimony trioxide were equal to 100: 5: 2: 3: 0.5: 0.2: 20: 0 100: 5: 2: 3: 0.5: 0.2: 20: 20 100: 5: 2: 3: 0.5: 0.2: 20: 40 100: 5: 2: 3: 0.5: 0.2: 20: 60 100: 5: 2: 3: 0.5: 0.2: 20: 80 and 100: 5: 2: 3: 0.5: 0.2: 20: 100 by weight or phr. The samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius with 30x30x0.2 cm of dimension for 4: 29 to 5: 19 minutes. The properties of the natural-rubber floor tiles were tested under ASTM standard. From the results it was found that the natural rubber and ethylene vinyl acetate plastic floor tile with flame resistance property was the suitable ratio for using as the rubber floor tiles in building and extinguished a fire by themselves. The antimony trioxide effected to increase the density hardness and thermal conductivity and decrease the tensile strength tear strength and wear resistance properties of the natural rubber and EVA plastic floor tiles

The purposes this research were: 1) to develop the activity packages on home textile pillow products forming process for textile product design students division the efficiency of 80/80 2) to compare academic achievement of textile product design students academic calendar 2018 before and after the experiment using the activity packages on home textile pillow products forming process 3) to study satisfaction of students toward the activity packages on home textile pillow products forming process. The sample consisted of 20 students who studied textile product design in the academic year 2018 at Rajamangala University of Technology Phra Nakhon. They were selected by purposive sampling. The research instruments were the activity packages on home textile pillow products forming process the achievement test and a satisfaction questionnaire. The data were analyzed by percentage mean standard deviation and t-test for dependent samples.The results of the study were as follows: 1) the efficiency of the activity packages on home textile pillow products forming process for textile product design students was obtained 84.65/82.50 higher than a predetermined threshold 80/80 2) academic achievement of home textile pillow products forming process for textile product design students was significantly higher than before the experiment using the activity packages on home textile pillow products forming process at the 0.5 level 3) the satisfaction of Textile Product Design students using the activity packages on home textile pillow products forming process was at the high level.

This research aims to study the water hyacinth fiber inside high-density fiber cement board. By using ratio components among cement : fine sand : water hyacinth fiber : water : catalyst accelerated the formations of cement (aluminum sulfate (AI2 (SO4) 3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) on the ratio 1: 0.2: 0.075: 0.3: 0.03 by weight of total water hyacinth fiber with the steel grating inside. By compressing the mixture cast machine at normal temperature (30 - 35 °C). From the test results the ratio of B4 is the appropriate ratio from the 1st year research result to produce the high-density fiber cement board with the steel grating inside 0.81mm #0.5”. It can pass the TIS 878-2537 standard of Cement Board and good based-on high density and physical properties mechanical properties and thermal insulation. Accelerate the formation of the most suitable cement is calcium chloride (CaCl2).

Molds manufacturing to produce chloroprene rubber product with carbon steel over time the mold surface will wear. From the original. The practice in the industry often uses surface coatings (Hard chrome method) or change materials to create molds. Therefore this research is to study the effect of corrosion or wear. To see the size of surface mold changed in the experiment. Based on a tolerance of 0.1 millimeters at the molding point and after molding in the actual work conditions of a 2-3 weeks sample and mold size measurement. At less than 10 times the permissible coordinate value is 0.01 millimeters. The experiment found that. The wear of carbon steel molds was formed with chloroprene rubber. It has a very small value when referenced to the tolerance coordinates which is not significantly reduced when the rubber specimen size is determined. The allowance range is 10 μm to 100 μm. Therefore the design of chloroprene rubber to make molds with carbon steel. It can help reduce production costs. Without replacing with corrosion-resistant materials or adding coatings.