This research aims to develop the cement board from vesicular basalt fragment. The 5 ratios of Portland cement type1: fine sand: vesicular basalt fragment: sodium silicate: tap water are equal to 1: 2: 0: 0.03: 0.5 1: 2: 2: 0.03: 0.5 1: 2: 4: 0.03: 0.55 1: 2: 6: 0.03: 0.6 and 1 : 2 : 8: 0.03: 0.65 by weight. The cement boards were produced by compression machine. The property tests of cement-bonded fiberboard followed the TIS. 878-1994 standard (cement bonded particle board: high density). From the results 1: 2: 4: 0.03: 0.55 is the most suitable ratio of cement board from coconut shell ash. This developed cement boards can apply the vesicular basalt fragment to use as the construction materials with light-weight high strength good thermal insulation and moisture protection properties

The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.

This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of light-weight precast concrete wall panel product with adding high density foam sheet. The light-weight precast concrete wall panel product was produced by covering the foam sheet with steel pouring the mortar (M3 ratio which was proper ratio) and curing the light-weight precast concrete wall panel product. From the testing results followed the TIS.2226-2548 and TIS.878- 2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 956.03 kg/m3 of density 9.18 MPa of bending strength and 0.170 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. Moreover the developing product can apply to register the petty patent.

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of l ight-weight precast concrete wall panel product with aerated foam injection technique as core wall. The light-weight precast concrete wall panel product was produced by casting the mortar panels with M3 ratio (proper ratio) set up the steels and injecting the aerated foams. From the testing results followed the TIS.2226-2548 and TIS.878-2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 1110.58 kg/m3 of density 9.18 MPa of bending strength and 0.186 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. the developing product can apply to register the petty patent.