The research involved the characterization of the properties of silver alloys -bearing copper and zinc. The alloys composed of 58.4% silver 20.85-41.76% copper and 0-20.83% zinc respectively. When comparing the characteristics of this alloy and sterling silver 925 the alloy specimen had mechanical properties better than the sterling silver 925. The alloy tests presenting the mechanical values of the hardness shear bond strength elasticity of the specimen were in a range of 54.6-95.3 HV1 209.5-379.3 MPa. 100.6-193.8 MPa. and 32.1-51.7% respectively. While the mechanical values of sterling silver 925 were 52.8 HV1 193.5MPa. 96.0 MPa. and 29.8% respectively. Besides these the microstructure of the alloy specimen showed the dendrite structure. We found that this structure decreased when the concentration copper in the specimen increased. After adding zinc into the alloys the high amount of zinc caused the zinc-rich (alpha) phase changed to Eutectic phase together with the significantly increased area of alpha phase. These effects therefore brought up the better various mechanical properties of the alloys. At the same time the another test specimen composed 58.67% Ag 39.20% Cu and 2.14% zinc. The color level of this specimen was close typically to the sterling silver 925 with the difference of Da at 0.236 and Db only at 5.268. Additionally the higher copper concentration in the alloy provided a value tentatively increased but b value decreased. However more remarkable results were that the zinc showed opposite effects from the copper.

The objective of this research is to study how rotation speeds affect mechanical properties with friction welding between semi-solid metal 7075 aluminum alloys and semi-solid metal 356 aluminum alloys. The factor of interest is rotation speeds with different conditions at 800 1000 1200 1400 and 1600 rpm respectively. 1.8 millimeter for burn of length 30 seconds for welding time and clockwise rotation are set as a control constant condition for the entire experiment. After friction welding we found that different rotation speeds significantly affected mechanical properties of these alloys. At rotation speed 1400 rpm the maximum tensile strength is 122.24 MPa and the maximum hardness in welded zone is 140.5 HV. The microstructure size is 2.250 µm long and 2.144 µm wide. Its size in welded zone is practically small because of friction force. Moreover this friction force causes the mixture of MgZn2 and Mg2Si in welded zone.

This paper discusses the mixed alloy silver pink by spending innocent Alloy capital ratio of 58.00% and check the analysis of color against Silver 925 under the metal content of about 58.40% alloy 41.60% result. According to the study the researchers used to hold above ingredients prototype to develop a mixture of silver to feature pink by analyzing the color (Color Analysis) tested the color of silver mixed pink capital ratio of 116.80 alloy. 83.20 wt.% has a shiny bright color space the L 67.17 a = 9.60 b = 2.04 a compound that can be used to produce silver mixed pink. In the manufacturing industry has for the user.

WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%