This research conducted an investigation on vocational pre-service teachers’ performance based on Technological Pedagogical Content Knowledge Framework (TPCK) to support learning in 21st century. TPCK Framework integrated three kinds of knowledge needed by a teacher in providing learning process for students effectively. The results of this study found that vocational pre-service teachers had the knowledge of using technology understanding teaching pedagogies and mastering on content individually. However they were limited in blending such essential three domains together to form more effective learning process for their students.

The purpose of this study were to conduct and to evaluate the effectiveness of Automotive service technician The research procedure starting by collect and study document : research paper international occupational standard (Oklahoma Department of Career and Technology Education) and competency needed in Motorcycle Mechanic suggested by 7 person who working in this field. All data will be referred for behavior objectives list and learning materials design such as information sheet practice operation sheet for experience skill training evaluation sheet with evaluation criteria which clearly listed topics. The sample group in this study was 19 PAJAMANGALA UNIVERSITY OF TECHNOLOGY PHRANAKHON Faculty of Industrial Education in academic year 2 0 1 7 . Pre-test will be given before training steps according to the manual. The students will do the test after each training topic. At the training end Post-test will be given and student final assignment will be evaluated by 5 experts. The Pre-test and Post-test scores will be statistical mean difference test. The research results found that the student final assignment competencies evaluation in percentage mean score was 87.55/94.66/85.13 that higher than 80/80/80 about the expectation. The test percentage mean score after training each topic was 92.11 that higher than 90 about the expectation. The percentage mean score difference test between before and after training was significant at statistical level .01 and the after training score was higher than before training score.

The purpose of this project is to study the mechanical and physical properties of recycled roofing materials. The pulp extracted from the UHT beverage boxes to get aluminum foil mixed with low density polyethylene. This can be used engineering and is an option to reduce the amount of UHT boxes left over to roofing sheets. In experiment 3 aluminum foil medium size and fine then hot and extruded with 68 and 10 bar compression then cut into test pieces. To test mechanical and physical properties in accordance with the test standards: Torsion Testing Tensile strength Impact resistance Heat resistance water absorption and density testing. Compare the mechanical and physical properties of the material; different sizes of aluminum foil and compressive strength. To bring the best materials to the product. From the tests it was found that the properties of recycled composite materials From the box UHT beetroot This is made of coarse aluminum foil. 18.23 MPa bending strength 10.66 MPa tensile strength 110.987 J / m2 impact resistance 52.40 Shore-D Hardness 0.62 % Water Absorption 0.70 % Thickness Swelling 1.086 g/m3 Density 0.031 m2.K/W Thermal Resistance and 0.291 W/mK Thermal Conductivity is the best mechanical properties. Due to the large aluminum foil it can be used for high strength. Which is higher than the aluminum foil of a smaller size.

This research aims to develop the ceiling board mixed with coconut coir. The 5 ratios of gypsum plaster: coconut coir: sodium silicate: tap water are equal to 1 : 0 : 1: 0.03 1: 100: 1: 0.03 1: 150: 1: 0.03 1: 200: 1: 0.03 1: 250: 1: 0.03 และ 1: 300: 1: 0.03 by weight. The ceiling boards were produced by casting in normal temperature (30 – 35 degree of Celsius). The properties testing of ceiling board mixed with coconut coir followed the TIS 219-2009 standard (gypsum plasterboard) including: breaking load nail pull resistance deflection water absorption density and thermal conductivity coefficient. From the results 1 : 1 5 0 : 1: 0.03 is the most suitable ratio of ceiling board mixed with coconut coir. This developed ceiling boards can reduce the quantity of coconut coir waste and get the good thermal insulation ceiling board products

This research aims to study the water hyacinth fiber inside high density cement fiber board. By using ratio components among cement : fine sand : water hyacinth fiber : water : catalyst accelerated the formations of cement (aluminum sulfate (AI2 (SO4) 3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) on the ratio 1: 0.2: 0.075: 0.3: 0.03 by weight of total water hyacinth fiber. The 5 ratios consist of 0.0 (A1 D1 formulae) 0.025 (A2 B2 C2 D2 formulae) 0.050 0.03 (A4 B4 C4 D4 formulae) and 0.1 (A5 B5 C5 D5 formulae) by weighted all fibers were treated with sodium hydroxide solution (NaOH) at a concentration of 12%. The fiber to solution ratio was 1: 10 boiled in open system at 100 °C for 1 - 3 hours. By compressing the mixture cast machine at normal temperature (30 - 35 °C). Use a density of 0.75 g / cm3. From the test results the ratio B4 is the appropriate ratio. Can pass TIS 878- 2537 Cement Board: high density and physical properties mechanical properties and thermal insulation are good. Accelerate the formation of the most suitable cement is calcium chloride (CaCl2)