The results of the study on the optimum temperature for baking soda extinguishers were investigated. B9R-3-EMERALD Using brass material in experiments. It was found that the temperature of 750˚C was good for 48% of the workpiece 52% was found that the workpiece was damaged at the surface of the work very porous at the surface. Caused by the heat of metal water pouring into contact with the moisture of the mold resulting in gas. High temperature of metal water Or eliminate gas in metal water is not exhausted. The workpiece is not suitable at a temperature of 800 ° C with a good workpiece of 76%. The workpiece loses 24%. The workpiece loses less punch at the lower porosity as well at 750˚C in temperature. 850˚C workpiece 96% workpiece 4% workpiece the workpiece is almost out. It is less than 750˚C and 800˚C at porosity. And at 900˚C the workpiece is 100% of the workpiece 0%. The workpiece is the best. Workpiece waste from the minimum. The test results make the temperature at 900 ° C is the cleanest casing temperature

This Research is to Study the Development of 6k White Gold Low Alloys Metal for Jewelry Production The Optimum Conditions for Casting Jewelry and Jewelry were Investigated. The Results of the Experiments Show that the Chemical Composition of the 8k White Gold Low Alloys is Slightly Different when Compared with XRF (X-ray Fluorescence Spectrometers) Pre-and Post-Melting Quantities The Heat of the Test Specimen was found to be 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn33.33%Au+50.67% Ag+8% Cu+7%Zn+1%Sn and 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn It is Found that the Heat from the Beginning to the Level of Change before the Liquid is used the Average Temperature of 458.9 – 326.3 Degrees Celsius Respectively 33.33%Au+50.67%Ag+8%Cu+7%Zn+1%Sn It is the Formula that Gives the Lowest Value of Liquid State Change from 326.3 Degrees Celsius to the Best Value of this Experiment. Suitable for use in the Manufacture of Jewelry due to its Melting Ability for Molding. Melting for Molding and Formed by Hand. The Amount of Zinc(Zn) may be an Important Factor in the Variation which is Directly Proportional to the Maximum Increase in the Final order of 7 Percent

This research is a study of the optimum heat temperature for baking sintered castings for burnout removal of EC 500 type ash wax from cast mortar. Improving jewelry casting process to reduce waste from silver jewelry production process. By studying the temperature of the mortar. To burn remove wax from the mortar and clean the gaps. Then try to bring silver water instead of metal casting. The results of a baked casing study using the EC500 housing prototype from the study showed that the EC500 wax material is melted from all solids to ash wax by heating at 850 ° C to burn. Remove ash wax which makes the cavity clean. When the casting was casted with 925 sterling silver the most complete workpiece after the improvement of the waste jewelry casting process was found to be 1 piece 1 percent 99 pieces or 99 percent.

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

The objects of this research were (1) to study the enterprenurial success in Clean Food Delivery Store in Bangkok (2) to study of individual factor and operation factor toward the success of Clean Food Delivery Store (3) for suggestion develop Clean Food Delivery Store. This research is servey research Tools of research is from population 158 data was collected by questionaires Statical Analize with percentage Mean Standard Deviation Mutiple Regression Analysis at the 0.05 level The result found mostly female age 30 – 40 years old their education was bachelor single income 30001 – 50000 bath Experience 1 – 2 year and knowledge from internet. The result operation factors is management marketing operation and technology and financial effect to success of Clean Food Delivery Store .