This research is developed and designed wall clocks decorative home From sawdust waste in the factory Bang Pho district in Bangkok. The study was conducted by testing groups of wood manufacturer Bang Pho community the results are as follows. The study found that the criteria of design analysis from the experts were 3.97 at a high level and the satisfaction of the product production was 4.11 at a high level. When evaluating the overall picture the mean score of 4.04 was high level.

This research aims to study and develop fiber from Palmyra Palm to use In the design of furniture in the residence in Phetchaburi. The study was conducted by testing groups of user who use furniture made of fiber from Palmyra Palm in in the residence Puek Tian district in Phetchaburi the results are as follows. The study found that the criteria for design analysis from the experts were 4.13 at a high level and satisfaction in using the 4.30 on a high level. When evaluating the overall picture the average score of 4.22 was high level.

This research then has two main objectives. The first objective is to fabrication of bioactive glass ceramics containing BaFe12O19 (BF) crystals has been carried out for the application in hyperthermia treatment. The BaFe12O19 powder was firstly prepared and subsequently mixed with the non-silicate P2O5-CaO-Na2O bioactive glass with various BF concentrations. After that the glass ceramics were produced via a sintering method at 600◦C and their crystal phases were examined by XRD and in vitro test was carried out by soaking in simulated body fluid. Remanence and saturation magnetization and coercivity were deduced from magnetic measurement. It was found that the samples exhibited magnetic behavior which is similar to hard magnetic materials. Our second objective is the effects of sintering temperatures on the physical and bioactivity of SrFe12O19 (SF)-P2O5-CaO-Na2O bioglass ceramics were investigated. XRD results confirmed the existence of the strontium ferrite and calcium phosphate phases. SEM images showed that grain size and hardness were related to density and liquid phase present in the samples. A maximum coercivity value of 3138 Oe was obtained for the bioglass ceramic sintered at 600 ºC. The remanence (Mr) and saturation magnetization (Ms) of the bioglass ceramic sintered at 500 ºC possess the maximum value of 6.35 and 10.64 emu/g respectively. Moreover the apatite was formed on the surface layers of the bioglass ceramics confirming their biocompatibility

This research then has two main objectives. The first objective is to fabrication of bioactive glass ceramics containing BaFe12O19 (BF) crystals has been carried out for the application in hyperthermia treatment. The BaFe12O19 powder was firstly prepared and subsequently mixed with the non-silicate P2O5-CaO-Na2O bioactive glass with various BF concentrations. After that the glass ceramics were produced via a sintering method at 600◦C and their crystal phases were examined by XRD and in vitro test was carried out by soaking in simulated body fluid. Remanence and saturation magnetization and coercivity were deduced from magnetic measurement. It was found that the samples exhibited magnetic behavior which is similar to hard magnetic materials. Our second objective is the effects of sintering temperatures on the physical and bioactivity of SrFe12O19 (SF)-P2O5-CaO-Na2O bioglass ceramics were investigated. XRD results confirmed the existence of the strontium ferrite and calcium phosphate phases. SEM images showed that grain size and hardness were related to density and liquid phase present in the samples. A maximum coercivity value of 3138 Oe was obtained for the bioglass ceramic sintered at 600 ºC. The remanence (Mr) and saturation magnetization (Ms) of the bioglass ceramic sintered at 500 ºC possess the maximum value of 6.35 and 10.64 emu/g respectively. Moreover the apatite was formed on the surface layers of the bioglass ceramics confirming their biocompatibility

In this research scaffolds of β-tricalcium phosphate (β-TCP) and zinc nickel ferrite (ZnxNi1-xFe2O4) were simply fabricated via the uniaxial pressing together with pressureless sintering which can be tailored for specific applications. The morphology of ZnxNi1-xFe2O4/β-TCP scaffolds with all formulas obtained from the SEM result revealed the larger grains the higher porosity and higher interconnectivity with increasing of ZnxNi1-xFe2O4 amount in β-TCP matrix. The high porous structure of the composite scaffold provided high surface area for cell attachment indicative of good cell growth and differentiation. Biological in vitro test using direct contact method with human cells revealed that the composite scaffold of β-TCP and Zn0.8Ni0.2Fe2O4 with all ratios induced the higher growth of Human osteoblast cells and the better cell spreading on surface of specimens