WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%

The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.

The research aims to study and develop the Kaolinite mixed with cement powder for the mass wall. The Kaolinite development process to improve the characteristics. The Kaolinite mixed ratios are 10% 20% 30% and 40% and the result indicated that the experiment mortar-mix ratio at 0:8:2.75:0.2:0.05:0.04:0.5 of cement powder sand Kaolinite limestone superplasticised and clean water compared to No MK control sample covered ASTM standard in tensile strength more than 100 ksc compressive strength of MK20% with superplasticised at 434 ksc. The water absorption values under the standard passed

This study developed the cemented tungsten carbide by steadily sintering at 1430 °C for one hour. The tungsten carbide structure is a long shape. Its grain size has a difference between width and length and there are high distribution of sizes and shapes. In comparison with the work piece which has the similar size of grain structure the milling duration of tungsten carbide is less even though the condition of WC-Co is the same (95% WC – 5% Co). When the sintering of 1400 °C with the identical milling duration is performed. It turned out that both grain structures of the tungsten carbide and the work piece are similar and their grain sizes are slightly different. However when the grain structures are almost the same and sphericity is increased the hardness and wear resistance will also be improved. Therefore the size of grain structure between 1.00 – 3.00 μm with the milling duration of 100 hours will provide a work piece that has a wear resistance according to international standard

The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.