This research study to the effect of pozzolanic materials by replacement cement by fly ash and Meta kaolin which affect the mechanical and physical properties of concrete. According to Standard test such as Compressive strength flexural strength and impact strength. The replacement cement by fly ash was 15% 30% and 45% respectively and replacement cement by meta-kaolin was 10% 15% and 20% respectively. The results showed that the compressive strength of concrete at 28 days. When considered ratio w/b = 0.40 was higher than w/b = 0.45 all ingredient. The replacement cement by fly ash was the most effective. 10% (375 ksc) 15% (362 ksc) and 20% (354 ksc) respectively. The replacement cement by meta-kaolin gave the highest flexural strength of 41 ksc higher than control mixed concrete and all other ingredient. At the age of 28 days The replacement cement by meta-kaolin was 10 percent result to the highest impact strength was 11 joule which was close to that of fly ash by 30 percent give value was 110 joules and more than replacement cement by meta-kaolin was 15% (100 joule) and 20% (95 joule). It can be concluded that the increase in meta-kaolin content result to compressive strength will reduce flexural strength and impact strength. As the amount of fly ash increased the compressive strength increased. flexural strength and impact strength Increased value.

Currently the automotive industry plays an important role on the economic growth in Thailand. As the same time the waste of automotive parts has increased as well. As a results the automotive parts made from three different natural fiber parts was studied consisting of hyacinths sugarcane and pineapple leaf fiber. By of 50 x 250 x 20 mm of mold dimension the specimens were produced under 700 W of heating stick and measured temperature by a K type of thermometer. There were 3 same proportion specimens made from: 1) sugar cane fiber: husk: latex adhesive 2) water hyacinth fiber: husk: latex adhesive 3) pineapple fiber: husk: latex adhesive in the ratio of 25:25:50 by weight which were formed under temperature between 100GC and 105°C at 5 MPa of pressure and leading to find out the bending moment ability. The test results show that the specimen made from sugar cane fiber has the highest value 5482.5 Nand 4061.11 N/mm2 of bending moment and bending stress respectively. It was more than specimen made of water hyacinth 29.84 % and pineapple fiber 65.01 %.

Nowadays one of the automotive engineering is conductivity of brake pads playing a role in friction coefficient which means safety of customer. Thus thermal properties have been improved using composited materials. This project aims to study the heat capacity behavior of 3 different brake pads which are supported by the company Compact International (1994) Ltd. For experimental works temperature based on brake condition was simulated from 05 to 003°C at 5 MPa of pressure. By standard JIS D4413 testing condition of pressure was referred. The heat capacity values of brake pads are calculated under the temperature conditions. As a result of testing brake pad made of copper or high metal powders result in relatively low heat capacity. On the other hand brake pads containing fiber and a large amount of fillers result in an increased heat capacity and stability in various temperature conditions. The heat capacity varied according to the operating temperature. In addition the lubricant contained in the brake pads affects the higher heat capacity and stability at various temperatures.

Based on the research on creation of bas-relief molds for production of bas-reliefs made from boiled pineapple leafs conducted by Rachadasak Pengcum of which purpose was to help generate income for members of Pineapple Leaf Paper Community Enterprise Ban Pasang Wiwat Mueang District Chiang Rai Province it was found that the bas-reliefs need further improvements in terms of appearance and durability as well as the use of other natural raw materials to produce them. The researcher therefore has considered developing the previous research by applying other 3 valueless natural materials which include rice straw water hyacinth and banana stem skin to make bas-reliefs for different beautiful surfaces of the products. Also the quality of bas-reliefs has been comparatively investigated by surveying satisfactions of members of the Community Enterprise and visitors to the project towards the bas-reliefs made from rice straw water hyacinth and banana stem skin. The total period of questionnaire distribution was 3 months. There are 59 respondents administering the questionnaires most of whom (43 persons) are female which accounts for 72.88 per cent. The majority of the respondents (25 persons) obtained junior/senior secondary school diplomas or equivalent accounting for 42.37 per cent. 16 respondents or 27.12 percent are 60 years of age. As for satisfactions towards the bas-reliefs made from rice straw 89 times of “strongly agree” was selected whereas 126 times of “pretty much agree” 75 times of “fairly agree” and 5 times of “disagree” were marked by the respondents. Concerning the bas-reliefs made from water hyacinth 87 times of “strongly agree” was selected while 97 times of “pretty much agree” 110 times of “fairly agree” and 1 time of “disagree” were chosen. When asked about the bas-reliefs made from banana stem skin the respondents selected 77 times of “strongly agree” 99 times of “pretty much agree” 110 times of “fairly agree” and 8 times of “disagree”.

This research is to study the recycling of residue clams shell from Mahachai Samutsakorn Thailand. This waste was collected from canned clams industry and it can be recycled as the composition of Mon brick instead of the rice husk. The study of clams shell composition found that Calcium was main composition as 98.50%VS. The moisture and ash content was 0.88% and 58.27%TS respectively. The works methodology is using ash from clams shell incinerated at temperature 900 1000 1100 and 1200oC in 5 hours respectively instead of rice husk in Mon brick processing. The fabrication of Mon brick was in size 5x5x5 cm adding ash from clams shell intead of rice husk. The result found that increasing the temperature to incinerate clams shell ash instead density and compressive strength increased while moisture and water absorption deceased. When Mon brick was fabricated in standard size at 6x15x3.5 cm the changed material characteristics was in the same trend as previous size. Mon brick in standard size adding 100% clams shell ash instead of rice husk had density 2.63 g/cm3 moisture content was 2.86% water absorption at 1 and 24h was 17.40 and 20.16% respectively and compressive strength was 0.52 MPa. These characteristics was according to standard of Engineering Institute of Thailand. It can reduce the cost of rice husk in Mon brick factory 28800 bath/year while the waste from canned clams factory could be reduced 20.94%.