This research presents the engineering properties of asphalt (AC 60/70) modified with different ratios of scrap natural rubber. Then select the best properties of the binder to mix asphaltic concrete. From laboratory testing results with adding 7% scrap natural rubber into mixtures for the best results. The properties of asphaltic concrete can be improved by adding 7% scrap natural rubber. For asphaltic concrete Marshall Stability increased with adding scrap natural rubber into asphalt. Moreover the stiffness modulus of asphaltic concrete can be improved 13.53 compared to AC 60/70.

The aims of this research work were to enhance the impact resistance and processibilty of wheat gluten (WG) by the addition of epoxidized natural rubber (ENR) compared to glycerol. This work was divided into two parts: to study the optimum ENR content for improvement of WG and the effect of together functions between ENR and glycerol on the properties of WG. Tested specimens were mixed and prepared by internal mixer and compression molding machine respectively. ENR and glycerol were varied from 10 to 40 phr. The effects of modifier types and contents on WG were evaluated by tensile impact and water absorption testing and thermal analysis. Fracture behavior and rubber dispersion were investigate with scanning electron microscope (SEM). The result revealed that the increase of ENR or Glycerol contents led to the decreases in tensile modulus and strength except for modifier content of 10 phr whereas elongation at break and impact strength increased. Glass transition temperature (Tg) of modified WG tended to decreased with the increase of ENR or glycerol contents especially for glycerol. The presence of glycerol affected on the decomposition temperature (Td) values but those were unchanged for case of ENR. Water resistant of WG specimen was improved by the presence of ENR whereas the increase of glycerol led to weight loss at immersion time of 2880 min. For the effect of ENR : glycerol ratios it indicated that glycerol enhanced tensile resistances but suppressed impact and water resistances of modified WG by ENR. Sizes and dispersion of ENR particles were improved by the addition of glycerol. Tg and Td values of modified WG by ENR and glycerol increased when ENR fractions were increased.

การวิจัยฉบับนี้ได้กล่าวถึงการลดระยะเวลาการทำแม่พิมพ์ยางซิลิโคนโดยเร่งความแข็งด้วยอุณหภูมิต่ำ เนื่องจากแม่พิมพ์ยางซิลิโคนใส สามารถเก็บรายละเอียดของชิ้นงานได้ดีและสามารถมองเห็นชิ้นงานด้านในได้แต่แม่พิมพ์ยางซิลิโคนใสใช้เวลาในการแข็งตัวนาน จึงได้ศึกษาและทำการทดลองนำเอาอุณหภูมิความเย็นเข้ามาช่วยในการเร่งการแข็งตัวของซิลิโคนใสโดกำหนดอุณหภูมิเป็น 3 อุณหภูมิ ประกอบด้วย 10 5 0 องศาเซลเซียล แต่อุณหภูมิแบ่งเป็น 3 ช่วงเวลา ประกอบด้วย 2 3 4 ชั่วโมง จึงทำการการทดลองขั้นต่อไป จากการทดลองโครงการลดระยะเวลาการทำแม่พิมพ์ยางซิลิโคนใสโดยเร่งความแข็งด้วยอุณหภูมิต่ำเพื่อหาอุณหภูมิและช่วงระยะเวลาที่เหมาะสมในการเร่งความแข็งของซิลิโคนใส พบว่าที่อุณหภูมิ 5 องศาเซลเซียล ช่วงระยะเวลา 3 ชั่วโมงมีค่าความแข็งใกล้เคียงกับมาตรฐานและมีความเหมาะสมที่สุด เนื่องจากผลการทดลองพบว่าอุณหภูมิและระยะเวลาที่เหมาะสมที่สุดนั้นสามารถลดระยะเวลาการแข็งตัวของซิลิโคนใสได้ 6 ชั่งโมงและมีประสิทธิภาพใกล้เคียงกับชิ้นงานมาตรฐาน

The enhancement of mechanical properties of natural rubber vulcanisates was expected by surface modification of perlite particles. Thus the objective of the present study was to investigate the cure properties and the heat aging resistance properties in terms of stress at 100% elongation tensile strength and percentage elongation at break after surface modification. Furthermore the rebound resilience and abrasion resistance of perlite treated with silane filled in NR vulcanisates were investigated. In a comparison the properties of clay-filled NR vulcanisates were determined. The results reveal that surface modification by using silane caused a reduction of scorch time and cure time but an increase in torque difference and swelling resistance. Also surface modification gives better perlite-NR interactions before and after aging. The better heat resistance properties of perlite-filled NR vulcanisates than those of clay-filled vulcanisates is detected from relative property data. Nevertheless a lower percentage of rebound resilience and abrasion resistance of perlite-filled vulcanisates before and after surface modification than those of clay-filled vulcanisates are observed. This is owing to the large particle size low specific surface area poor dispersion and agglomeration of perlite in NR vulcanisates.

In the rubber situation The problem has accumulated. All sectors are mobilized. The idea is to solve the problem of falling rubber prices. Or the output overflow. Overpriced The rubber growers. Have been affected by the same. This is a problem that many sectors. Trying to find a way out Research or development Products that can be used to produce rubber. It is another way to alleviate the suffering of farmers. The characteristics of rubber processing. There are many types of rubber raw rubber rubber and rubber. And have specific properties in themselves. The obvious is flexibility. Rubber quality in each production source is not equal. It is a problem of creating products with many components of rubber. But many of the products do not require the quality of the rubber. The problem is less. Such as shockproof materials in various packaging. Especially the material inside the packaging. For glass and ceramic products Only flexible features are needed. The rubber coating on the material has been invented many experiments. Be it on wood on fabric etc. as well as paper. But rubber coating on paper. To use for such purposes. It is made to be shockproof material by means of the pump in the packaging. There is no such trial. Researchers have the idea to study and develop the process. Cushioning material from rubber coated paper. To be suitable for packaging applications for glass and ceramic products. With regard to the ability to actually use. Value for money. Industrial production The satisfaction of the consumer. And the standard of packaging. The researcher found that. Applying the varnish on three variables and mixing the three compounds results that if the coating is applied on a material with a resilient property it will increase the elastic properties of the material. Corrugated paper is particularly suitable because the rubber can be inserted into the corrugated paper inside the corrugated paper. The test results are very good. Satisfaction I found that the content provider is very satisfied with the format and usage. But in weight it is also a problem because of the water that makes the weight of the packaging. The researcher should consider that the weight of rubber latex should be improved.