This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

This research is study on influences effect of decision to use PromptPay system of Thai commercial banks. The purpose of the research is as follows. Study the confidence that effect of the choice of financial transaction services through PromptPay system. Study the marketing mix factors that effect of the decision to use financial services through PromptPay system. This research is to collect data from customer of Thai commercial banks. Thai commercial banks are as follows. Bangkok Bank Public Company Limited. Krung Thai Bank Public Company Limited. The Siam Commercial Bank Public Company Limited. Kasikorn Bank Public Company Limited. and Bank of Ayudhya Public Company Limited. The results showed that most respondents had the following: They are female. They are between 31 and 40 years old. They are single. They graduated bachelor. They are studying at the undergraduate level. They are students. They earn less than 15000 baht per month. Frequency of financial transactions is 1 time per month. They used to transfer money through mobile applications. The reason for using the mobile banking is quick and easy. and Reduce the loss of money and the cost of banking transactions are the factors that affect the choice of use PromptPay system.

This research study about rainfall pattern in Thailand due to the influenced of the tropical cyclone. The annual rainfall analysis was derived from the Thai Meteorological Department (TMD) since 1 9 7 1 -2 0 0 0. The analysis of annual rainfall used composite analysis and classification of rainfall patterns with cluster analysis. To measuring the similarity between the rainfall patterns in each year by hierarchical clustering method. In addition use to Single Linkage rules for grouping the rainfall pattern and using the distance between the units close together as possible into consideration. The summarized of rainfall pattern due to the influenced of the tropical cyclone are usually found in the eastern and northeastern regions of Thailand. It is found that a heavy rainfall. The rainfall pattern in the western regions of Thailand has the least amount of rainfall as a result of drought.

The objective of this research were to study 1) General features of economic factor social factor environment factor and personal factor of people in muo-baan Suan-Son community and 2) The influence of economic factor social factor environment factor and personal factor involvement on quality of life of people in muo-baan Suan-Son community. This study was conducted by applying 2 research methodologies. For quantitative approach questionnaires were used to collect data 216 from people in muo-baan Suan-Son community. The data was analyzed by using descriptive statistics and hierarchical regression analysis. With the qualitative approach in-depth interview group discussion structured observation and field notes. The results indicated that 1) Most of people in muo-baan Suan-Son community had low bachelor degree enough income each month satisfied with family over work and community considered that the environmental protection in the community was moderate and the environment in the community was middle clean and enough. 2) The component of factor influence to quality of life of people in Muo-Baan Suan–Son community had health treat family community and welfair.

This objective research to study the possibility of used pozzolan material in the ternary blend by fly ash metakaolin and silica powder by replacement cement partially on the strength and resistance to chloride migration. Consideration of concrete with compressive strength in the range of 240-350 kg per sq. cm by varying the ratio of water/binder (w/b) there are three values are 0.4 0.45 and 0.50 and variable amounts of replacement cement some. The ternary blend of the fly ash metakaolin and silica powder of percentage of 0 2.5 5 10 15 20 and 25 by weight of cement. and the control specimens (w/b) without contain fly ash kaolin and silica powder the slump test in the range of 3-5 cm and the use superplasticizer to control the slump test of concrete. By casting specimens of cylindrical diameter 10x20 cm cube 10x10x10 cm and the beam size 10x10x35 cm after curing 28 days and test compressive tensile and flexural strength of concrete all specimens each ingredient by Chloride Migration Test method and the results showed that concrete is a mixture with pozzolan such as silica powder metakaolin and fly ash with amount increase replacement. The increase will help improve the quality of the concrete physical properties. The increased of compressive and Tension strength as the percentage increase especially to replacement cement increased by fly ash metakaolin and silica powder reduces the penetration of chloride in concrete respectively As a result of the porosity of the concrete with lower amounts of tightness concrete has increased