The objective of this research is to develop the concrete flooring tile product from old asphalt road waste. The 6 ratios of Portland cement type1: coarse sand: old asphalt road waste: water reducer type A: tap water were designed including: 1: 5: 0: 0.02: 0.4 1: 4.5: 0.5: 0.02: 0.4 1: 4: 1: 0.02: 0.4 1: 3.5: 1.5: 0.02: 0.4 1: 3: 2: 0.02: 0.4 and 1: 2.5: 2.5: 0.02: 0.4 by weight. The concrete flooring tile casted with the compressive machine. The property tests followed the TIS.378 - 1988 (concrete flooring tiles). According to the result it was found that the 1: 2.5: 2.5: 0.02: 0.4 was the proper ratio of the concrete flooring tile. The increasing of old asphalt road waste in concrete flooring tile effected to decrease the water absorption and thermal conductivity properties. In term of the density and bending strength properties there were not many differences. The developed concrete flooring tile product from old asphalt road waste can use as same as the common concrete flooring tile product in market.

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

The objective of this research is to develop the precast adobe wall panel with high corrosion resistance and good thermal insulation. The ratio of Portland cement type1 clay rice husk ash straw rice husk waterproofed liquid and tap water was mixed and casted as same as the common concrete and reinforced by bamboo. From the results the proper prototype ratio of precast adobe wall panel was Portland cement type1: clay: rice husk ash: straw: rice husk: waterproofed liquid: tap water which equal to 1: 3: 0.3: 0.02: 0.02: 0.02: 0.4 by weight. The properties of the precast adobe wall panel prototype included density 1797 kg/m3 water absorption 16.70% bending strength 2.61 MPa compressive strength 21.40 MPa thermal conductivity coefficient 0.314 watt/m.Kelvin. Moreover the precast adobe wall panel prototype also was verified by TIS.2226-2548 with properties of impact resistance deflection and hardness in medium duty (MD) level. These straw and rice husk effected the precast adobe wall panel to decrease the density bending strength thermal conductivity coefficient and increase the compressive strength and water absorption.

The research is study motives the affect participation in quality assurance personal of Faculty of Engineering Rajamangala University of Technology Phra Nakhon from example group of 182 people which classified by sex ages position educational degree field of work and working life. This research is used themethod is collecting data by question tool themethod is questionare tool fo collected data that could be two categorized include knowledge skills and attitudes. The questionnaire is five rating scales that analyze the result by frequency percent average the average of standard deviation and T-test independent by using one way ANOVA. The results were as follows : From one hundred percent of the personnel of Faculty of Engineering Rajamangala University of Technology Phra Nakhon whom 63.70 persent classified by the educational field and 36.30% support line are ready to enter into Asean community which could be seen average in whole picture. After considering in three aspects the result appeared that knowledge and skills of personnel are also average. However the attitude of personnel was considered in a high level. Hypothetic test result was found that there was no difference among the personnel with difference sex ages educational degree field of work and working life in their readiness in entering Asean Community. position

This research is to study the recycling of residue clams shell from Mahachai Samutsakorn Thailand. This waste was collected from canned clams industry and it can be recycled as the composition of Mon brick instead of the rice husk. The study of clams shell composition found that Calcium was main composition as 98.50%VS. The moisture and ash content was 0.88% and 58.27%TS respectively. The works methodology is using ash from clams shell incinerated at temperature 900 1000 1100 and 1200oC in 5 hours respectively instead of rice husk in Mon brick processing. The fabrication of Mon brick was in size 5x5x5 cm adding ash from clams shell intead of rice husk. The result found that increasing the temperature to incinerate clams shell ash instead density and compressive strength increased while moisture and water absorption deceased. When Mon brick was fabricated in standard size at 6x15x3.5 cm the changed material characteristics was in the same trend as previous size. Mon brick in standard size adding 100% clams shell ash instead of rice husk had density 2.63 g/cm3 moisture content was 2.86% water absorption at 1 and 24h was 17.40 and 20.16% respectively and compressive strength was 0.52 MPa. These characteristics was according to standard of Engineering Institute of Thailand. It can reduce the cost of rice husk in Mon brick factory 28800 bath/year while the waste from canned clams factory could be reduced 20.94%.