The purpose of this research is to improve the physical and mechanicalqualities of natural rubber latex tiles. Water: surfactant: surfactant: 1: 2.75: 0.03: 0.30:0.03: 0.04 by weight and added with natural latex. In the ratio of Portland Cement Type 1: Natural Latex is 1: 0 1: 0.025 1: 0.05 1: 0.075 and 1: 0.10. Formed with compression presses at normal temperatures it was found that the optimum amount of natural latex For concrete reinforced concrete tiles the ratio is 1: 0.025. The tests in accordance with Thai Industrial Standard TIS 535-2556 are tested in 4 aspects. Dimensional stress test Water absorption test And waterproofness testing The value has passed the benchmark. And low thermal conductivity. Increasing the insulation of the roof as well. Can be used as a prototype product tile concrete roof natural latex. To produce commercially And there can be many local latex or rubber latex. To be more useful and valuable.

This research aims to test the properties of concrete block mixed with basalt fragment as aggregates in products. The mix ratios of Portland cement type1 : basalt fragment : water are 1 : 10 : 0.7 1 : 10.5 : 0.7 1 : 11 : 0.7 1 : 11.5 : 0.7 and 1 : 12 : 0.7 by weight. The concrete block samples were mixed and casted in 7 x 19 x 39 centimeter by the concrete block molding machine. The concrete block sample testing follows the TIS 58-2533 standard on non-load bearing concrete blocks. From the results the density compressive strength and thermal conductivity of concrete block mixed with basalt fragment are lower than the common concrete block. In addition the water absorption and volumetric change are higher than the common concrete block. The optimal ratio in this work is 1: 11: 0.7

This research presents the engineering properties of asphalt (AC 60/70) modified with different ratios of rib smoked sheet. Then select the best properties of the binder to mix asphaltic concrete. From laboratory testing results with adding 9% rib smoked sheet into mixtures for the best results. The properties of asphaltic concrete can be improved by adding 9% rib smoked sheet. For asphaltic concrete Marshall Stability increased with adding rib smoked sheet into asphalt. Moreover the stiffness modulus of asphaltic concrete can be improved 9.03 compared to AC 60/70.

The objectives of this research are to study the production to find the proper ratio to test the physical mechanical properties and thermal conductivity to suggest the implementation and to transfer the technology of light-weight precast concrete wall panel product with adding high density foam sheet. The light-weight precast concrete wall panel product was produced by covering the foam sheet with steel pouring the mortar (M3 ratio which was proper ratio) and curing the light-weight precast concrete wall panel product. From the testing results followed the TIS.2226-2548 and TIS.878- 2537 the general characteristic of light-weight precast concrete wall panel product was perfect. The properties of light-weight precast concrete wall panel product include 17.81 MPa of compressive strength no bending when installed in common behavior 11.38% of water absorption passed in type1 of hardness and impact test 956.03 kg/m3 of density 9.18 MPa of bending strength and 0.170 watt/m.K of thermal insulation. This light-weight precast concrete wall panel product can use as the thermal insulation wall in building. Moreover the developing product can apply to register the petty patent.

This research has objectives to study the production to find the proper size of steel wire mesh to test the properties and to study the implementation of high strength and thermal insulation cement-bonded fiberboard from coconut meal corncob fibers and steel wire mesh. The mixture ratio of cement-bonded fiberboard included Portland cement type1: sand: coconut meal fiber: corncob fiber: water: calcium chloride equal to 1: 0.2: 0.0125: 0.0375: 0.3: 0.03 by weight and 5 different sizes of steel wire mesh were reinforced. Casted by compression and sharking machine. Tested the properties follow the TIS.878-2537. From the results 1 mm of diameter and 1” of gab of steel wire mesh (? 1 mm # 1”) was the proper size to reinforce the cement-bonded fiberboard to get highest bending strength. Moreover this cement-bonded fiberboard can pass the required standard. The high strength and thermal insulation cement-bonded fiberboard from coconut meal corncob fibers and steel wire mesh has the possibility to construction as exterior building wall.