The purpose of this study were to conduct and to evaluate the effectiveness of Automotive service technician The research procedure starting by collect and study document : research paper international occupational standard (Oklahoma Department of Career and Technology Education) and competency needed in Motorcycle Mechanic suggested by 7 person who working in this field. All data will be referred for behavior objectives list and learning materials design such as information sheet practice operation sheet for experience skill training evaluation sheet with evaluation criteria which clearly listed topics. The sample group in this study was 19 PAJAMANGALA UNIVERSITY OF TECHNOLOGY PHRANAKHON Faculty of Industrial Education in academic year 2 0 1 7 . Pre-test will be given before training steps according to the manual. The students will do the test after each training topic. At the training end Post-test will be given and student final assignment will be evaluated by 5 experts. The Pre-test and Post-test scores will be statistical mean difference test. The research results found that the student final assignment competencies evaluation in percentage mean score was 87.55/94.66/85.13 that higher than 80/80/80 about the expectation. The test percentage mean score after training each topic was 92.11 that higher than 90 about the expectation. The percentage mean score difference test between before and after training was significant at statistical level .01 and the after training score was higher than before training score.

The objectives of this research are to study the production step proper ratio physical properties mechanical properties and thermal insulation of concrete blocks mixed with waste ceramic powder. The ratios of concrete block mixed with waste ceramic powder include Portland cement type1: quarry dust: waste ceramic powder equal to1: 6.8: 0.2 1: 6.7: 0.3 1: 6.6: 0.4 1: 6.5: 0.5 and1: 6.4: 0.6 by weight. Water per cement ratio are 0.6 by weight. The concrete block samples were castedby the general production as same as the ordinary concrete blocks and were tested follow TIS.58. From the results the best amount of waste ceramic powder which put into concrete block is 1: 6.7: 0.3 of ratio. The proper ratios of waste ceramic powder can decrease the density or weight and increase the thermal insulation efficiency of concrete blocks. However the high amounts of waste ceramic powder effect to decrease the mechanical properties concrete blocks that are lower than TIS.58 standard.

The objective of this research is to develop the concrete flooring tile product from old asphalt road waste. The 6 ratios of Portland cement type1: coarse sand: old asphalt road waste: water reducer type A: tap water were designed including: 1: 5: 0: 0.02: 0.4 1: 4.5: 0.5: 0.02: 0.4 1: 4: 1: 0.02: 0.4 1: 3.5: 1.5: 0.02: 0.4 1: 3: 2: 0.02: 0.4 and 1: 2.5: 2.5: 0.02: 0.4 by weight. The concrete flooring tile casted with the compressive machine. The property tests followed the TIS.378 - 1988 (concrete flooring tiles). According to the result it was found that the 1: 2.5: 2.5: 0.02: 0.4 was the proper ratio of the concrete flooring tile. The increasing of old asphalt road waste in concrete flooring tile effected to decrease the water absorption and thermal conductivity properties. In term of the density and bending strength properties there were not many differences. The developed concrete flooring tile product from old asphalt road waste can use as same as the common concrete flooring tile product in market.

This research aims to develop the natural rubber and ethylene vinyl acetate (EVA) plastic floor tile with flame resistance property. The 6 ratios of natural-rubber STR 20: zinc oxide: stearic acid: sulfur: mercaptobenzothiazole: diphenyl guanidine: EVA plastic: antimony trioxide were equal to 100: 5: 2: 3: 0.5: 0.2: 20: 0 100: 5: 2: 3: 0.5: 0.2: 20: 20 100: 5: 2: 3: 0.5: 0.2: 20: 40 100: 5: 2: 3: 0.5: 0.2: 20: 60 100: 5: 2: 3: 0.5: 0.2: 20: 80 and 100: 5: 2: 3: 0.5: 0.2: 20: 100 by weight or phr. The samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius with 30x30x0.2 cm of dimension for 4: 29 to 5: 19 minutes. The properties of the natural-rubber floor tiles were tested under ASTM standard. From the results it was found that the natural rubber and ethylene vinyl acetate plastic floor tile with flame resistance property was the suitable ratio for using as the rubber floor tiles in building and extinguished a fire by themselves. The antimony trioxide effected to increase the density hardness and thermal conductivity and decrease the tensile strength tear strength and wear resistance properties of the natural rubber and EVA plastic floor tiles

This research is a study of the optimum heat temperature for baking sintered castings for burnout removal of EC 500 type ash wax from cast mortar. Improving jewelry casting process to reduce waste from silver jewelry production process. By studying the temperature of the mortar. To burn remove wax from the mortar and clean the gaps. Then try to bring silver water instead of metal casting. The results of a baked casing study using the EC500 housing prototype from the study showed that the EC500 wax material is melted from all solids to ash wax by heating at 850 ° C to burn. Remove ash wax which makes the cavity clean. When the casting was casted with 925 sterling silver the most complete workpiece after the improvement of the waste jewelry casting process was found to be 1 piece 1 percent 99 pieces or 99 percent.