This quantitative research aimed 1) to study operation performance of Thai Gem Businesses. 2) To study factors affecting firm performance of Thai Gem Businesses. The research was collected data by using questionnaire with 452 participants from production group of Thai Gem Businesses. The samples were collected conveniently and analyzed by frequency percentage mean standard deviation Pearson’s correlation coefficient and analysis confirmatory with Structural Equation Modeling: SEM. It was one of all statistic techniques to test for causal relationship of variables. The results found that database information management systems have positively affect strategic management and firm performance of Thai Gem Businesses with significant level 0.05. Database information management systems also have positive affect on strategic management of Thai Gem Businesses with significant level α < 0.05. Besides this research results found that database information management systems has positively direct and indirect affecting firm performance by pass strategic management with direct affect on firm performance equal to 0.346 and indirect affect by pass strategic management equal to 0.575. And total affect was equal to 0.921 with significant level. It showed that overall affect of database information management system on firm performance was more than strategic management affect to Firm Performance (0.603) with significant level 0.05. The analysis of correlation coefficient model showed that measurement between latent variables have positive correlation with significant level α < 0.05. The analysis of Structural Equation Model revealed that it wassuitable harmonize with empirical data ( χ2 / df = 1.489 CFI = 0.997 AGFI = 0.957 RMSEA = 0.08 RMR = 0.004) and consistent with the define hypothesis. The research results described the environmental of firm performance approach to strategic management by TOWS Matrix and recommendation on strategic management to solve problems on firm performance of Thai Gem Businesses in order to develop continuous firm performance for competitive advantage.

This Research is a Development of 8k White Gold low Alloy Metal Components for Jewelry Pieces. By Study and Analyze the Influence of Silver Alloy Gold Alloy Bronze Alloy Zinc Alloy and Tin Alloy. Which Affect Microstructure and Mechanical Properties. (The Different of Color Scales) And Resistance Behavior of Lowered 8k White Gold Alloy in Varies Ratio. The Results Showed that Tests and Analysis to Find the Quantities of Elements has found out that Chemical Components of 8k White Gold Low Alloy Metal had a Little Different Quantities when Compared Between Before and After Centrifugal Casting Process. The Tests and Analysis Results of Mechanical Properties of Test Pieces Showed that the Hardness and Tensile Strength of 8k White Gold Low Alloy Metal with Mixture of 33.33%Au+50.67%Ag+10%Cu+5%Zn+1%Sn had Minimum Ultimate Tensile Strength Equal 0.54 kN/mm2 Minimum Elongation Percentage of 55% and Maximum Hardness of 137.0 HV. The Test Results also Show that the Mechanical Properties of the Material are Brittle Material. When Perform a Forming Process the Pieces will be Easily Broken which was Meant that the Forming Process would be Difficult. But The Color Level of the Test Pieces at this Composite Ratio had the Best Metal Color Level. The Brightness L * = 74.87 was a * = -0.89 b * = 13.74 and the Value of ΔE with the Lowest Color Difference Level of 1.35. Compared to other Varies Ratio. It Showed that 8k White Gold Low Alloy Metal Test Pieces were Very Green and Came out Slightly Yellow Compared to the Blue Line that Approached the Standard Line. These Properties were the Physical Properties Required in 8k White Gold Low Alloy Metal Jewelry Pieces Production. Also there were the Results of 8k White Gold Low Alloy Metal in Two Formulas 8k 33.33%Au+50.67%Ag +8%Cu+7%Zn+1%Sn 33.33%Au+50.67%Ag+8%Cu+8%Zn+0%Sn. These Formulas had Tensile Strength in the Range of 1.10 0.60 kN /mm2 Elongation Percentage in the Range of 70 61% and Hardness of 115.6 123.3HV Respectively. The Results of the Mechanical Properties Test of the Test Pieces Showed that 8k White Gold Low Alloy Metal 33.33% Au+50.67%Ag+8%Cu+7%Zn+1%Sn has Similar Tensile Strength but Maximum Elongation Percentage of 70% and Minimum Hardness of 115.6HV. Which was Suitable for Forming Because of good Ductility and Stretchness Properties (Ductile Material). Forming would be Easy. These were Good Mechanical Properties for Forming Precious Metals.

โครงการทำเครื่องประดับเงินลวดลายโบราณ ชื่อวิชา ออกแบบเครื่องประดับ / การทำต้นแบบเครื่องประดับ ผู้สืบทอด อาจารย์จักรกฤษณ์ ยิ้มแฉ่ง กำหนดการ วันอังคารที่ 21 กรกฎาคม พ.ศ. 2558 เวลา 9.00 – 16.00 น. สถานที่ สาขาเทคโนโลยีแม่พิมพ์เครื่องประดับ คณะวิศวกรรมศาสตร์ มทร.พระนคร จำนวนนักศึกษา 12 ราย วัตถุประสงค์ของโครงการ มีดังนี้ 1. เพื่อให้นักศึกษามีความเข้าใจเรื่องเทคนิคการทำเครื่องประดับเงินลวดลายโบราณ 2.เพื่อให้นักศึกษาสามารถนความรู้ด้านเทคนิคงานช่าง ไปประยุกต์ใช้ในการออกแบบเครื่องประดับ 3. เพื่อให้นักศึกษามีแนวคิดเพิ่มเติมในการบูรณาการความรู้ 4.เพื่อให้นักศึกษาสืบทอดภูมิปัญญาศิลปวัฒนธรรมทางช่างการทำเครื่องประดับลวดลายโบราณ 5. เพื่อเป็นโครงการในการบูรณาการการเรียนการสอน รายละเอียดการถ่ายทอด สอนตามกรรมวิธีโบราณ เช่น การหลอม การรีด การแผ่ การตีลวดลาย การดัดม้วน และการเชื่อมประสาน การวาดลงลาย การตอกลาย ผลที่คาดว่าจะได้รับ 1. นักศึกษามีความรู้ความเข้าใจในเทคนิคงานผลิตแหวนลวดลายโบราณ 2. นักศึกษาสามารถสร้างแนวคิดในการออกแบบ และหาแรงบันดาลใจในการศึกษาจากการอบรม 3. นักศึกษาสามารถประยุกต์งานช่างสิบหมู่ มาสร้างงานออกแบบเครื่องประดับได้ 4. ผู้เข้ารับการอบรมมีความตระหนักในความรับผิดชอบต่อการอนุรักษ์ศิลปช่างสิบหมู่