This research aims to test the properties of concrete block mixed with basalt fragment as aggregates in products. The mix ratios of Portland cement type1 : basalt fragment : water are 1 : 10 : 0.7 1 : 10.5 : 0.7 1 : 11 : 0.7 1 : 11.5 : 0.7 and 1 : 12 : 0.7 by weight. The concrete block samples were mixed and casted in 7 x 19 x 39 centimeter by the concrete block molding machine. The concrete block sample testing follows the TIS 58-2533 standard on non-load bearing concrete blocks. From the results the density compressive strength and thermal conductivity of concrete block mixed with basalt fragment are lower than the common concrete block. In addition the water absorption and volumetric change are higher than the common concrete block. The optimal ratio in this work is 1: 11: 0.7

This research aims to study the using rock fragments of basalt mining to develop paving block product. The mixture ratios of Portland cement type1: basalt rock fragments: tap water are 1 : 4 : 0.45 1 : 4.5 : 0.45 1 : 5 : 0.45 1 : 5.5 : 0.45 and 1 : 6 : 0.45 by weight. The paving block samples are cast in 30 x 30 x 5 centimeter in dimension. The paving block sample testing follows the TIS 378-2531 on concrete flooring tiles. From the experiment bending strength of paving blocks with high quantity of basalt rock fragments is lower than paving blocks with low quantity of basalt rock fragments but the water absorption of paving blocks with high quantity of basalt rock fragments are higher. However all of basalt rock fragments paving block samples with lower than 1 : 5.5 : 0.45 of ratio can pass the standard.

This research aims to study the using basalt rock fragments to develop as interlocking block product. The mixture ratios of Portland cement type1: basalt rock fragments are 11 : 6 1 : 6.5 1 : 7 1 : 7.5 and 1 : 8 by weight and water per cement ratio was 0.6 by weight. The interlocking block samples are cast in 10 x 20 x 10 cubic centimeter of dimension with manual compression molding machine. The interlocking block samples were tested in accordance with TCPS 602-2547 standard which subjected for the interlocking block. The results show that the weight compressive strength and thermal conductivity of interlocking blocks with high quantity of basalt rock fragments are lower than interlocking blocks with low quantity of basalt rock fragments while that the water absorption of interlocking blocks with high quantity of basalt rock fragments are higher. From this research the medium and small enterprises could choose the proper ration for the interlocking block production mixing basalt rock fragments as per requirement.

This research aims to study the properties of natural rubber STR 20 at 100 phr with various contents of coir (e.g. 0 5 10 20 40 and 80 phr) and then mixed with chemical substance at constant ratio. After that the samples are ground by two-roll mill and formed by compression molding at 150 degree Celsius. This leads into the coir reinforcement natural rubber plate of dimension 30x30x0.5 cm. The properties of the natural rubber plates are tested under ASTM standard. From the results it is found that increasing in coir then the properties of resilience and density are improved at every mix ratio. However the tensile strength tear strength and wearing are increased at some certain value of coir. The samples give no water absorption at every mix ratio. The results from this research indicate that it can develop into the rubber floor tiles and rubber wall tiles for furnishing the buildings in natural style.

การวิจัยนี้เป็นการศึกษาพฤติกรรมการอบชุบด้วยกระบวนการทางความร้อนของโลหะเงิน เจือต่ำ58.45wt%Ag +41.55wt%Cu โดยทำการเปรียบเทียบกับสมบัติของโลหะเงินสเตอร์ลิง 925 และโลหะเงินเจือต่ำ 58.33% เพื่อศึกษาสภาวะที่เหมาะในหาการปรับปรุงคุณสมบัติเชิงกลและโครงสร้าง จุลภาคของโลหะเงินเจือต่ำที่เป็นไปตามมาตรฐานผลิตเครื่องประดับ ผลจากการศึกษาโลหะเงิน 58.33 % ที่อัตราส่วนผสม 58.33Ag+36.66Cu+5.01Sn ซึ่งมี ค่าคุณสมบัติเชิงกลจากการทดสอบเบื้องต้นมีค่าเหมาะสมที่สุด จากนั้นท่าการศึกษาค่าความแข็งแรงดึง สูงสุดแบบเส้นลวดพบว่ามีค่าความต้านทานแรงดึงสูงสุดเท่ากับ 0.36 MPa ค่าเปอร์เซ็นต์การยืดตัว 0.11% เมื่อท่าการอบที่อุณหภูมิ 650 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่ อุณหภูมิห้องปกติ และค่าความแข็งจากการทดสอบมีค่าสูงสุดเท่ากับ 105.12 HV อบที่อุณหภูมิ 600 °C เวลาในการอบ 10 นาที ซึ่งปล่อยให้ชิ้นงานเย็นตัวในอากาศที่อุณหภูมิห้องปกติ ศึกษาโครงสร้างจุลภาค ของโลหะเงินเจือต่ำ 58.33Ag+41.57Cu+0.10Sn เมื่อท่าการอบปรับปรุงคุณสมบัติทางความร้อนและการ ชุบแข็งแบต่างๆ พบว่าโครงสร้างจุลภาคของชิ้นงานทดสอบหลังปล่อยให้เย็นตัวในอากาศ เกิดการ เปลี่ยนแปลงจาก β phase ที่มีขนาดเล็กลงเป็นโครงสร้าง Eutectic phase ที่มี α -phase และ β - phase ขนาดเล็กและละเอียด ซึ่งมีลักษณะสอดคล้องกับโครงสร้างจุลภาคของเฟสไดอะแกรมสมดุลโลหะ เงิน-ทองแดง ผลจากการทดลองและวิเคราะห์หาค่าคุณสมบัติเชิงกลของชิ้นงานทดสอบและโครงสร้างจุลภาค ที่ได้จากการทดลองในสภาวะต่างๆ มีค่าที่เป็นไปตามมาตรฐานของเครื่องประดับเงินตามมาตรฐาน อุตสาหกรรมการผลิตเครื่องประดับ ทั้งของในประเทศและต่างประเทศ