The objectives of this study were 1) to analyze the capability contributing to the competitive advantage 2) to synthesize the key performance indicator from the internal factors 3) to examine the level of competitive capability and 4) to develop the strategy to enhance the capability of competitive advantage in the faculty of Mass Communication Technology Rajamangala University of Technology Phra Nakhon. The samples used in the study included 71 interviewed stakeholders in the university and 400 survey participants. The findings pointed out as follows: (1) the strategy t enhance the competitive advantage were defined in five aspects: curriculum educational management personnel learning environment and image and alumni association (2) the level of competitive advantage was rated high in the following order: personnel educational management curriculum and image and alumni association. The learning environment was also in high level.

This research aims to study the using cassava pit wastes mixed with cement to particle board walls. The Portland cement type1: fine sand: tap water ratio is equal to 1: 0.5: 0.416 by weight. The ratios of cassava pit wastes to cement are used following: 0.05 0.06 0.07 0.08 0.09 and 0.10 by weight. The cassava pit wastes are crushed by plastic plastics granulators (pass sieve no.4). The casting of particle board walls use the compression machine in room temperature (30 – 35 degree of Celsius) and control 0.75 g/cm3 of density. The TIS 878-2537 standard (cement bonded particle board: high density) is followed to test the properties of particle board wall. Resulting the cassava pit wastes mixed with cement can cast to particle board walls and have good properties especially the thermal insulation property.

The using of ground coffee wastes from industries to develop the cement board is an objective of this research that can solve the air pollution problems from smell and spreading of ground coffee wastes. The ratio of Portland cement type1: fine sand: tap water is equal to 1: 0.5: 0.416 by weight and the ratios of Portland cement type1: ground coffee wastes include 1: 0.05 1: 0.06 1: 0.07 1: 0.08 1:0.09 and 1: 0.10 by weight (6 ratios). The production of cement board uses the pressure casting in temperature 30 – 35 degree of Celsius and controls 0.75 g/cm3 of density. The testing of cement-bonded fiberboard properties follow the TIS 878-2537 standard (cement bonded particle board: high density). From the results 1: 0.05 is the most suitable quantity of cement: ground coffee wastes which mixed in cement board. This cement boards can reduce the ground coffee wastes by using as aggregate to produce the construction materials.

This research aims to develop the cement board from coconut shell ash. The Portland cement type1: fine sand: tap water ratio is equal to 1: 0.4: 0.33 by weight. The 5 ratios of Portland cement type1: coconut shell ash include 1: 0.12 1: 0.13 1: 0.14 1: 0.15 and 1: 0.16 by weight. The cement board production uses the pressure casting in normal temperature (30 – 35 degree of Celsius) and controls the 0.75 g/cm3 of density then test the properties of cement-bonded fiberboard follow TIS 878-2537 standard (cement bonded particle board: high density). From the results 1: 0.12 is the most suitable ratio of cement board from coconut shell ash. This developed cement boards can reduce the quantity of coconut shell ash waste and have the good thermal insulation.

This research aims to study the application of coconut meal and corncob fiber as high density cement-bonded fiberboard. The cement: fine sand: coconut meal and corncob fiber: water: cement setting accelerator (aluminium sulphate (Al2(SO4)3) calcium chloride (CaCl2) sodium silicate (Na2SiO3)) ratio is equal to 1: 0.2: 0.05: 0.3: 0.03 by weight. The fibers are taken from coconut meal: corncob that 5 ratios are used following: 0.0500: 0 (CN0) 0.0375: 0.0125 (CN25) 0.0250: 0.0250 (CN50) 0.0125: 0.0375 (CN75) and 0: 0.0500 (CN100) by weight. 12% of Sodium Hydroxide (NaOH) was used to modify the fibers by using 1: 10 of fiber: solution and boiling 100 degree of Celsius (1-3 hours). The fiberboard production use pressure casting in normal temperature (30 – 35 degree of Celsius) and 0.75 g/cm3 of density. Resulting the CN75 ratio is suitable ratio which pass TIS 878-2537 standard (cement bonded particle board: high density) and has good physical properties mechanical properties and thermal insulation. The most suitable cement setting accelerator is calcium chloride (CaCl2).