This research aims to study the using oil palm fiber to develop ceiling board product. The mixture ratios of Gypsum plaster: oil palm fiber: tap water: catalyst are 1 : 0.15 : 1: 0.03 1 : 0.20 : 1: 0.03 1 : 0.25 : 1: 0.03 1 : 0.30: 1: 0.03 and 1 : 0.35 : 1: 0.03 by weight. The ceiling board samples are cast in 30 x 30 x 1 centimeter in dimension. The ceiling board sample testing follows the TIS 219-2552. The results show that the longitudinal and lateral breaking load Nail pull resistance density and thermal conductivity of ceiling board with high quantity of oil palm fiber are lower than ceiling board with low quantity of oil palm fiber while that the deflection and water absorption of ceiling board with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.2 of ratio can pass the standard.

This research aims to study the using oil palm fiber to develop pseudo-plywood from polyethylene product. The mixture ratios of oil palm fiber : polyethylene are 50 : 50 55 : 45 60 : 40 65 : 35 and 70 : 30 by weight. The pseudo-plywood samples are cast in 30 x 30 x 1.5 centimeter in dimension. The pseudo-plywood sample testing follows the TIS 966-2547. The results show that the density bending strength modulus of elasticity thermal conductivity and tension perpendicular to surface of pseudo-plywood with high quantity of oil palm fiber are lower than pseudo-plywood with low quantity of oil palm fiber while that the water absorption and swelling by density of pseudo-plywood with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 65 of ratio can pass the standard.

This research aims to study the using oil palm fiber to develop cement-bonded fiberboard product. The mixture ratios of Portland cement type1: fine sand: oil palm fiber:tap water: catalyst are 1 : 1.95 : 0.05 : 0.40 : 0.03 1 : 1.94 : 0.06 : 0.40 : 0.03 1 : 1.93 : 0.07 : 0.40 : 0.03 1 : 1.92 : 0.08 : 0.40 : 0.03 and 1 : 1.91 : 0.09 : 0.40 : 0.03 by weight. The cement-bonded fiberboard samples are cast in 30 x 30 x 1.5 centimeter in dimension. The cement-bonded fiberboard sample testing follows the TIS 878-2537. The results show that the density thermal conductivity bending strength modulus of elasticity and tension perpendicular to surface of cement-bonded fiberboard with high quantity of oil palm fiber are lower than cement-bonded fiberboard with low quantity of oil palm fiber while that the water absorption and swelling in water of cement-bonded fiberboard with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.06 of ratio can pass the standard.

Currently transport has played an important role in everyday life resulting in huge traffic jams caused by big city streets and pollution problems from global warming to global temperatures are rising. Since humans are creatures that prefer comfort in all areas which contrasts with the higher temperatures of the Earth. Currently the use of air conditioning a lot. To modify the temperature is reduced in the range 2 3 to 25 degrees Celsius makes people feel comfortable. However the use of air conditioning in the car cabin cooling efficiency can be increased to a higher level than it is by cooling the refrigerant. The aim of this research is to test and compare the performance of car air conditioning systems usually equipped with a heat exchanger. Using water from the condensation of evaporator as a medium for heat transfer. By installing the equipment at the outlet of the condenser. This causes the temperature of the refrigerant is low. The pipe lengths in the equipment from the calculation of 1 .2 meters and copper lines that increases the length of the tubes was calculated to compare with a length of 1.6 meters to test the speed of the compressor 1000 1500 2000 and. 2500 rpm and a wind speed of 20 35 and 50 kilometers per hour. The results of experiment found that the temperature refrigerant equipment decreased from an average of 1.6 degrees Celsius the pipe length of 1.2 meters and 1.6 meters of pipe temperature drops 1.8 degrees average temperature attended Eva sufficiently reduced operator. It increases energy efficiency ratio averaged 6.68% of the pipe length 1.2 m and 22.24% at a length of 1.6 meters as well as to increase the coefficient of performance of the air conditioning system. 6 .6 9 % of the pipe length of 1.2 meters and a length of 1.6 meters at 22.4% with the key factor in optimizing the cars air conditioning system. Making the refrigerant from the condenser the temperature drops to pull heat out of the cabin through evaporator higher.

จากการทดลองวิจัยพบว่าดินลูกรัง ที่ใช้ในการททำวิจัยเป็นดินชั้นคุณภาพ A4 ประเภทของดินทรายแป้ง (Silty Soils) โดยมีอัตราส่วนผ่านตะแกรงเบอร์ 4 เทากับ 99.20% อัตราส่วนผ่านตะแกรงเบอร์ 10 เทากับ 96.20% อัตราส่วนผ่านตะแกรงเบอร์ 40 เทากับ 92.34% และอัตราส่วนผ่านตะแกรงเบอร์ 200 เทากับ 72.08% ดินลูกรังมีค่าพิกัด Atterberg พิกัดเหลว (Liquid Limit) เทากับ 17.49% พิกัดพลาสติก (Plastic Limit) เทากับ 15.08 % และดัชนีมวลดิน (Plasticity Index) เทากับ 2.41% องค์ประกอบทางเคมีของดินลูกรังพบว่าดินลูกรังมีซิลิกอน ออกไซด์ (SiO2) อลูมิน่า ออกไซด์ (Al2O3) ไอรอน ออกไซด์ (Fe2O3) เป็น 58.60 % 25.50% 13.00% ตามลำดับและพบสารประกอบ Silicon Oxide (SiO2) : Quartz ดินลูกรังมีผลการทดสอบหาความหนาแน่นปรากฏมีค่า 2.69 g/cm3 ความถ่วงจำเพาะ 2.32 ค่า Loss on Ignition 3.43 % การกระจายตัวของขนาดอนุภาค 28.42 μmขนาดรูพรุน 42.62 μm และพรุน ตัว 47.74% การขึ้นรูปตามอัตราส่วนของ ดินลูกรัง – พลาสติก ที่ดินลูกรัง 100% 90% และ80% ไม่สามารถอัดขึ้นรูปได้เนื่องจากดินมีมวลที่ละเอียดเมื่อขึ้นรูปจะไม่เกิดการยึดเกาะระหว่างมวลกับพลาสติกดังรูปในตารางและอัตราส่วนดินลูกรังตังแต่ 70%-0%สามารถขึ้นรูปได้สมบูรณ์ ตัวอย่างทดสอบดินลูกรัง-พลาสติกที่มีกำลังอัดสูงขึ้นตามเวลาที่ทำการกำ เนื่องจากวัสดุ HDPE มีความเหนียวและยืดหยุ่นทำให้วัสดุทดสอบไม่มีการแตกหักแต่จะเปลี่ยนรูปตามแรงที่กระทำ ซึ้งพบว่าดินลูกรังผสมพลาสติกเมื่อเพิ่มปริมาณพลาสติกมากขึ้นกำลังรับแรงเพิ่มตามสำดับผู้ใช้ควรเลือกใช้ตามความเหมาะสมกับงาน ปริมาณดินลูกรัง 50% ขึ้นไปตัวอย่างจบน้ำและปริมาณดินลูกรังตำกว่า 50% ก้อนตัวอย่างทดสอบลอยน้ำ ตัวอย่างสามารถดูซึมน้ำได้น้อยกว่า 30% ทุก ตัวอย่างที่สามารถขึ้นรูปได้ ซึ้งสามารถนำไปใช้ในงานก่อสร้างได้ ดินลูกรังผสมปลาสติกไม่เกิดการเปลี่ยนแปลงปริมาตรหรือเกิดน้อยมาก ซึ้งเป็นคุณสมบัติที่ดีของวัสดุก่อสร้าง ผลการทดสอบด้วยกล้องขยายกำลัง 50x พบว่าดินลูกรังสามารถขึ้นรูปได้ด้วยการประสานของพลาสติกโดยยิงมีอัตราสวนของพลาสติกมากยิงทำให้มีความสามารยึดเกาะขึ้นรูปและกำลังได้ดีตามไปด้วย