This research is aimed at studying the development of strong and high strength fiberboard from coconut fiber and corn plant. This is the second consecutive year by using natural latex. To enhance thermal insulation performance. By using the cement ratio: fine sand: coconut pulp: corn fiber: water: surfactant: surfactant is 1: 0.2: 0.0125: 0.0375: 0.3: 0.03: 0.04 by weight Then add natural rubber latex at cement ratio: 5: 1 ratio of natural rubber latex: 1: 0.05 1: 0.10 1: 0.15 1: 0.20 and 1: 0.25 by weight tested in accordance with TIS 878- 2537 on cement slabs. : High density the test results show that the ratio of 1: 0.05 is the fiber cement ratio. The most appropriate the amount of natural latex said. Can make fiber Cement sheets. Best compression and bending strength. And has passed the standard TIS 878-2537 cement fiberboard developed this can help reduce the amount of natural latex is very high. And have a good thermal insulation properties

This research aims to compare the mechanical properties of materials made from hyacinth pineapple and sugarcane fibers and also to study the feasibility of producing automotive interior parts from natural fibers. The 9 specimens that made from natural fiber such as water hyacinth pineapple leaf fiber sugar can and husk and there are also three different binders: glue polymer and polymer plus hardener were produced. All of specimens were controlled mass and density. The specimens were classified into 2 types: 1) thin type with a size of 3.5x14x1 cm in order to test the flexibility 2) thick type with a size of 6.5x6.5x20 cm for testing the ability to absorb energy. The test results showed that the specimen produced from sugar cane and husk using adhesive bonding able to receive bending stress and modulus of elasticity more than other specimens up to 80.63% and 69.19% respectively. While the ability to absorb energy from work piece made from pineapple leaf fiber and husks using polymer bender was able to absorb energy more than other work pieces 51.58%.

This research aims to study the using oil palm fiber to develop ceiling board product. The mixture ratios of Gypsum plaster: oil palm fiber: tap water: catalyst are 1 : 0.15 : 1: 0.03 1 : 0.20 : 1: 0.03 1 : 0.25 : 1: 0.03 1 : 0.30: 1: 0.03 and 1 : 0.35 : 1: 0.03 by weight. The ceiling board samples are cast in 30 x 30 x 1 centimeter in dimension. The ceiling board sample testing follows the TIS 219-2552. The results show that the longitudinal and lateral breaking load Nail pull resistance density and thermal conductivity of ceiling board with high quantity of oil palm fiber are lower than ceiling board with low quantity of oil palm fiber while that the deflection and water absorption of ceiling board with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.2 of ratio can pass the standard.

This research aims to study the using oil palm fiber to develop pseudo-plywood from polyethylene product. The mixture ratios of oil palm fiber : polyethylene are 50 : 50 55 : 45 60 : 40 65 : 35 and 70 : 30 by weight. The pseudo-plywood samples are cast in 30 x 30 x 1.5 centimeter in dimension. The pseudo-plywood sample testing follows the TIS 966-2547. The results show that the density bending strength modulus of elasticity thermal conductivity and tension perpendicular to surface of pseudo-plywood with high quantity of oil palm fiber are lower than pseudo-plywood with low quantity of oil palm fiber while that the water absorption and swelling by density of pseudo-plywood with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 65 of ratio can pass the standard.

This research aims to study the using oil palm fiber to develop cement-bonded fiberboard product. The mixture ratios of Portland cement type1: fine sand: oil palm fiber:tap water: catalyst are 1 : 1.95 : 0.05 : 0.40 : 0.03 1 : 1.94 : 0.06 : 0.40 : 0.03 1 : 1.93 : 0.07 : 0.40 : 0.03 1 : 1.92 : 0.08 : 0.40 : 0.03 and 1 : 1.91 : 0.09 : 0.40 : 0.03 by weight. The cement-bonded fiberboard samples are cast in 30 x 30 x 1.5 centimeter in dimension. The cement-bonded fiberboard sample testing follows the TIS 878-2537. The results show that the density thermal conductivity bending strength modulus of elasticity and tension perpendicular to surface of cement-bonded fiberboard with high quantity of oil palm fiber are lower than cement-bonded fiberboard with low quantity of oil palm fiber while that the water absorption and swelling in water of cement-bonded fiberboard with high quantity of oil palm fiber are higher. However all of oil palm fiber samples with lower than 0.06 of ratio can pass the standard.