The objective of this research is to produce the T-Bar. The mixed Gule Phenol-cyanate to made ceiling Plate-Bar plate from the agriculture process’s waste. The researcher brought physic nut plant to produce T- BAR plate for interior building. It was tested based on Thailand industrial standard (TIS 876-2547) for determination of moisture content density absorption and expansion when soak in water as well a cohesion and perpendicular surface tension flexural resistance and modulus of elasticity . at The results show that suitable size material should not thicker than 2 centimeters. The experiment of ratio between physic nut plant and phenol cyanide resin at 90:10 and 92:8. It was found that suitable proportion of physic nut pant and phenol cyanide resin was 92:8. The temperature used for compression was 120o C. The appropriate density prior to the compression plate was 0.80 g/cm.3 The average moisture content of materials before compression was 8.88%. The suitable compression was 151 lb/in?. The moisture content of the product was 7.64% The density was 0.818 g/cm.3 The expansion value after soaking in water for 2 hours was 8.02% and water absorption was 14.22%. Inner bond was 0.55 MPa. Flexibility was 22.44 MPa. and mordulus was 2112MPa.The result of testing complied with the Thailand Industrial Standard (TIS 876-2547).It was concluded that physic nut plant can be used as raw material to make T- Bar plate for interior building

Nutritive values moringa leaves meal were evaluated and compared with luecaena leaves meal which has similar chemical compositions in order to use moringa leaves meal as broiler chicken feed ingredient. Thirty 3-week old chickens were divided into 3 groups of 10 birds (5 males 5 females) each. Each chicken was randomly fed with experimental diet that was composed with cassava powder (for endogenous nitrogen analysis) powdered moringa Leaves meal and powdered luecaena Leaves meal. The chickens were raised individually in metabolic cage where feed and water were provided ad libitum and both feed intake and feces weight were recorded. Experimental diets and excreta were sampled and subjected to proximate analysis for chemical compositions and gross energy. T-test comparison was used for statistical analysis. Results indicated that nutrients utilization of moringa Leaves meal (utilization percentage of dry matter organic matter protein crude fiber nitrogen free extract energy and metabolizable energy) were higher than those of luecaena Leaves meal (P<0.01). However there was no statistical difference (P>0.05) between moringa Leaves meal and luecaena Leaves meal in utilization percentage of ether extract. Moreover usable energy of moringa leaves meal was also higher than that of luecaena leaves meal (p<0.01). Therefore moringa Leaves meal could be one of potential feedstuffs for use in broiler diet production.

Banana flour (BF) was to use a stabilizer in coconut milk ice-cream (CMIC) in order to add value for Thai fruit; Banana. BF was varied at 4 levels as follows; 0.1 0.3 0.5 and 0.7%. Data from various treatments were analyzed using non-parametric test with the software. Mean and standard deviation were compared using The LSD based on sig at p value < 0.05. The panelists were accepted CMIC which use BF 0.5%. The physical specifications include stickiness 705.43?6.16 cps %Overrun 47.600.11 %solubility 25.50.12 at ambient temperature for 30 min pH 5.980.02 and total soluble solid 20.50.43. The chemical specifications include %protein 1.78 %fat 6.06 %carbohydrate 18.94 %moisture 72.76 %ash 0.46 and could be stored at -20 C for 3 days. CMIC was not found microorganisms that cause food to be rotten.

The study. Utilization coconut fiber added in Kha Nom Tong Muan. Aims to study the amount of coconut fiber in the production of Kha Nom Tong Muan .The total amount of coconut fiber production level of 3% as the best recipe Kha Nom Tong Muan. Recognized in terms of appearance color sweet taste crispness overall liking by a mean of 8.20 8.03 8.06 8.20 and 8.16 order. The differences were statistically significant (p ? 0.05). Shelf life of coconut fiber added Thong Muan at 5 weeks Kha Nom Tong Muan packed in a Freud bag and then put the paper kept at room temperature. The random quality checks every week. This suggests that coconut fiber in Kha Nom Tong Muan products is safe for the consumer. And to study the consumer acceptance of food products with coconut fiber added in Kha Nom Tong Muan. Questionnaires were used of 100 consumers who were accidental. The satisfaction of the Kha Nom Tong Muanproducts Appearance. Sweet taste coconut fiber smell crispness and feel left behind. The analysis of coconut fiber added in Kha Nom Tong Muan filled has satisfaction level in this medium to get 71 percent.

This research aims to study the application of coconut meal corncob and durian peel as wood-substituted biocomposites in medium density fiberboard. The fiber: urea formaldehyde glue: isocyanate glue with polymeric diphenymethane diisocyanate type (pMDI) ratio is equal to 1: 0.13: 0.003. The fibers are taken from coconut meal corncob and durian peel that 7 ratios are used to all of fiber mixing. The fiberboard production use 130?C of temperature with 20 – 50 kg/sq.cm of compressive pressure with 8 minutes per piece of rate. Their fiberboards have 603 – 856 kg/m of density that was tested follow the TIS 876-2547 standard. Resulting the MM33 ratio (coconut meal fibers: corncob fibers: durian peel fibers is equal to 0.33: 0.33: 0.33) and the CC50 ratio (coconut meal fibers: corncob fibers: durian peel fibers is equal to 0.50: 0.25: 0.25) can pass the standard in physical properties and mechanical properties. Moreover their fiberboards have good thermal insulation