WC powder was obtained from recycling cemented carbide scraps. This metal power contained tungsten carbide (WC) at 89.17% titanium (Ti) at 4.90% tantalum (Ta) at 3.56% niobium (Nb) at 1.31% and molybdenum (Mo) at 0.93%. Its particle size and distribution was in the range of 0.03-85.31 µm. After quality improvement of the metal powder by ball milling screening and separating the compounds the result showed that the particle size of the metal powder was decreased to 0.01-0.10 µm (10-100 nm). The average size of the powdered particle was 28 nm. The tungsten powder was in more perfect condition by 95.85%

This research was on the production of hardmetal from recovery of tungsten carbide tool scraps recycling through ball milling for 40 hours. The metal powder obtained which was of the size between 0.11-0.22 µm was composed of 96.69% of tungsten carbide (WC) 1.68% of tantalum (Ta) 1.21% of titanium (Ti) and 0.42% of niobium (Nb). When mixed with 5-15% cobalt binder metal cold isostatic press (CIP) sintered at 1450 ° C it became hardmetal work piece dimension 12.39 x 13.82 x 5.60 mm with 1410 HV hardness and 14.34 g/cm3 density. The result of S45C steel turning was tools life good. The research concluded that the hardmetal work piece produced by the developed material had suitable basic specification and would lead to the development in working in the future.