This research is presented by the designing and constructing test package that are divided into three types; the liquid insulator solid insulator and gas insulator. These materials are provided by in country in order to construct the test package for the results of expected to have at least error. This leads to reliability and validity in this study. The design of the liquid insulator of test package was conducted by the standard IEC 156 in which the material tested used oil transformer. Additionally its solid insulation was the range of catching objects and adjusting using the sheet of bakelite. Furthermore its gas insulation used acrylic was consisted of gas inside oxygen of pressure at 2 Bar. Three types of test could be supplied AC high voltage to test package causing of breakdown via insulators. After that taking note the value of breakdown was the liquid insulator of test material at 29.86kV its solid insulator at 36.32kV and its gas insulator (oxygen) at 48.40 kV

This research was aimed to study the compressive strength and the abrasion resistance of Terrazzo floor which used glass cullet as aggregate. The mix proportion of Terrazzo was 1 : 2.5 (white cement : chipped stone) by weight. The weight percentages of replacement of chipped stone by glass cullet were 0 10 25 50 75 and 100% by weight of aggregate. The compressive strength and abrasion resistance of Terrazzo specimens were measured at 7 14 and 28 days. The results indicated that the compressive strength of mixtures with glass cullet of 0 10 25 50 75 and 100% were 581.11 540.81 534.83 480.94 435.42 and 343.71 kg/cm2 respectively. It showed that the compressive strength decreased with the increase of glass cullet content. The abrasion test of Terrazzo specimens showed that at low glass cullet content (10-50%) the abrasion resistance increased with the increase of glass cullet content. The mixtures with glass cullet of 75 and 100% have abrasion resistance nearly the same as the mixture without glass cullet